Electronic device and polymer compound

ABSTRACT

An electronic device that serves as a high-brightness electroluminescent device includes a layer containing a polymer compound having one or more structural units selected from a structural unit represented by formula (1) and a structural unit represented by formula (14) as a charge injection layer and/or a charge transport layer: 
     
       
         
         
             
             
         
       
     
     wherein Ar 1  and Ar 2  represent certain fused polycyclic aromatic groups; R 1 , R 2 , R 6  and R 7  represent certain organic groups; m1, m2 and m6 represent an integer of 1 or more; m7 represents an integer of 0 or more; and when R 1 , R 2 , R 6  and R 7  are each plurally present, they each may be the same or different.

TECHNICAL FIELD

The present invention relates to an electronic device and a polymer compound for use in the electronic device.

BACKGROUND ART

In order to improve characteristics, disposing various types of layers between a light-emitting layer and an electrode is under study. For example, it is known that an electroluminescent device has a layer formed of a non-conjugated polymer compound containing a substituent having a cation and two hetero atoms between a light-emitting layer and an electrode (Patent Literature 1).

PRIOR ART DOCUMENT Patent Literature

-   Patent Literature 1: Patent application laid-open publication No.     2003-530676

SUMMARY OF INVENTION Problem to be Solved by the Invention

However, the brightness of the above electroluminescent device is still insufficient.

An object of the present invention is to provide an electronic device that serves as a high-brightness electroluminescent device.

Means for Solving Problem

The present inventors have found that the above object can be achieved by the electronic device or the like below to achieve the present invention.

Accordingly, the present invention provides an electronic device including a layer comprising a polymer compound comprising one or more structural units selected from the group consisting of a structural unit represented by formula (1) and a structural unit represented by formula (14) as a charge injection layer and/or a charge transport layer; and the like. The structural unit represented by formula (1) and the structural unit represented by formula (14) are each a divalent structural unit.

The structural unit represented by formula (1) is:

wherein

Ar¹ represents a (2+m1+m2)-valent fused polycyclic aromatic group that optionally has a substituent;

R¹ represents a group represented by formula (2) or formula (3);

R² represents a group represented by formula (4);

m1 represents an integer of 1 or more;

m2 represents an integer of 1 or more;

when R¹ and R² are each plurally present, they each may be the same or different; and

a hydrogen atom in formula (1) may be replaced with a substituent other than R¹ or R²;

wherein the group represented by formula (2) is:

—R³-{(Q¹)_(n1)-Y¹(M¹)_(a1)(Z¹)_(b1)}_(m3)  (2)

wherein

-   -   R³ represents a single bond, or a (1+m3)-valent organic group         that optionally has a substituent;     -   Q¹ represents a divalent organic group;     -   Y¹ represents —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, —PO₃ ²⁻ or —B(R^(α))₃ ⁻;     -   M¹ represents a metallic cation, or represents an ammonium         cation that optionally has a substituent;     -   Z¹ represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(a))₄ ⁻, R^(a)SO₃ ⁻,         R^(a)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄         ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻;     -   n1 represents an integer of 0 or more;     -   a1 represents an integer of 1 or more, and b1 represents an         integer of 0 or more, wherein a1 and b1 are selected such that a         charge of the group represented by formula (2) is zero;     -   R^(α) represents an alkyl group having 1 to 30 carbon atoms that         optionally has a substituent, or an aryl group having 6 to 50         carbon atoms that optionally has a substituent;     -   R^(a) represents an alkyl group having 1 to 30 carbon atoms that         optionally has a substituent, or an aryl group having 6 to 50         carbon atoms that optionally has a substituent;     -   m3 represents an integer of 1 or more, and when R³ is a single         bond, m3 represents 1; and     -   when Q¹, Y¹, M¹, Z¹, n1, a1 and b1 are each plurally present,         they each may be the same or different;

wherein the group represented by formula (3) is:

—R⁴-{(Q²)_(n2)-Y²(M²)_(a2)(Z²)_(b2)}_(m4)  (3)

wherein

-   -   R⁴ represents a single bond, or a (1+m4)-valent organic group         that optionally has a substituent;     -   Q² represents a divalent organic group;     -   Y² represents a carbocation, an ammonium cation, a phosphonium         cation, a sulfonium cation, or an iodonium cation;     -   M² represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(b))₄, R^(b)SO₃ ⁻,         R^(b)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄         ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻;     -   Z² represents a metallic cation, or represents an ammonium         cation that optionally has a substituent;     -   n2 represents an integer of 0 or more;     -   a2 represents an integer of 1 or more, and b2 represents an         integer of 0 or more, wherein a2 and b2 are selected such that a         charge of the group represented by formula (3) is zero;     -   R^(b) represents an alkyl group having 1 to 30 carbon atoms that         optionally has a substituent, or an aryl group having 6 to 50         carbon atoms that optionally has a substituent;     -   m4 represents an integer of 1 or more, and when R⁴ is a single         bond, m4 represents 1; and     -   when Q², Y², M², Z², n2, a2 and b2 are each plurally present,         they each may be the same or different;

wherein the group represented by formula (4) is:

—R⁵-{(Q³)_(n3)-Y³}_(m5)  (4)

wherein

-   -   R⁵ represents a single bond, or a (1+m5)-valent organic group         that optionally has a substituent;     -   Q³ represents a divalent organic group;     -   Y³ represents a cyano group, or a group represented by any one         of formulae (5) to (13);     -   n3 represents an integer of 0 or more;     -   m5 represents an integer of 1 or more, and when R⁵ is a single         bond, m5 is 1; and     -   when Q³, Y³ and n3 are each plurally present, they each may be         the same or different;     -   wherein the group represented by any one of formulae (5) to (13)         is:

—O—(R′O)_(a3)—R″  (5)

—S—(R′S)_(a4)—R″  (7)

—C(═O)—(R′—C(═O))_(a4)—R″  (8)

—C(═S)—(R′—C(═S))_(a4)—R″  (9)

—N{(R′)_(a4)R″}₂  (10)

—C(═O)O—(R′—C(═O)O)_(a4)—R″  (11)

—C(═O)O—(R′O)_(a4)—R″  (12)

—NHC(═O)—(R′NHC(═O))_(a4)—R″  (13)

-   -   wherein         -   R′ represents a divalent hydrocarbon group that optionally             has a substituent;         -   R″ represents a hydrogen atom, a monovalent hydrocarbon             group that optionally has a substituent, a carboxyl group, a             sulfo group, a hydroxy group, a mercapto group, —NR^(C) ₂, a             cyano group or —C(═O)NR^(c) ₂;         -   R′″ represents a trivalent hydrocarbon group that optionally             has a substituent;         -   a3 represents an integer of 1 or more;         -   a4 represents an integer of 0 or more;         -   R^(c) represents an alkyl group having 1 to 30 carbon atoms             that optionally has a substituent, or an aryl group having 6             to 50 carbon atoms that optionally has a substituent; and         -   when R′, R″ and R′″ are each plurally present, they each may             be the same or different;             and

wherein the structural unit represented by formula (14) is:

wherein

Ar² represents a (2+m6+m7)-valent fused polycyclic aromatic group that optionally has a substituent;

R⁶ represents a group represented by formula (15) or formula (16);

R⁷ represents the group represented by formula (4);

m6 represents an integer of 1 or more;

m7 represents an integer of 0 or more;

when R⁶ and R⁷ are each plurally present, they each may be the same or different; and

a hydrogen atom in formula (14) may be replaced with a substituent other than R⁶ or R⁷;

wherein the group represented by formula (15) is:

wherein

-   -   R⁸ represents a (1+m8+m9)-valent organic group that optionally         has a substituent;     -   Q¹, Q³, Y¹, Y³, M¹, Z¹, n1, n3, a1 and b1 are the same as the         corresponding definitions above;     -   m8 and m9 each independently represent an integer of 1 or more;         and     -   when Q¹, Q³, Y¹, Y³, M¹, Z¹, n1, n3, a1 and b1 are each plurally         present, they each may be the same or different;

wherein the group represented by formula (16) is:

wherein

-   -   R⁹ represents a (1+m10+m11)-valent organic group that optionally         has a substituent;     -   Q², Q³, Y², Y³, M², Z², n2, n3, a2 and b2 are the same as the         corresponding definitions above;     -   m10 and m11 each independently represent an integer of 1 or         more; and     -   when Q², Q³, Y², Y³, M², Z², n2, n3, a2 and b2 are each plurally         present, they each may be the same or different.

Effect of the Invention

The electronic device of the present invention serves as a high-brightness electroluminescent device.

MODE(S) FOR CARRYING OUT THE INVENTION

The present invention will be described in detail below.

<Polymer Compound>

The polymer compound of the present invention is a polymer compound having one or more structural units selected from the group consisting of a structural unit represented by Formula (1) and a structural unit represented by Formula (14).

The polymer compound has preferably 15 to 100% by mole of the structural unit represented by Formula (1) and/or the structural unit represented by Formula (14) based on all structural units.

Structural Unit Represented by Formula (1)

In Formula (1), Ar¹ represents a (1+m1+m2)-valent fused polycyclic aromatic group that optionally has a substituent. R¹ represents a group represented by Formula (2) or Formula (3). In view of stability of the polymer compound of the present invention on electron current, R¹ is preferably the group represented by Formula (2). R² represents a group represented by Formula (4). m1 represents an integer of 1 or more and m2 represents an integer of 1 or more. When R¹ and R² are each plurally present, they each may be the same or different.

The above Ar¹ may have a substituent other than R¹ or R². Examples of the substituent may include an alkyl group, an alkoxy group, an alkylthio group, an aryl group, an aryloxy group, an arylthio group, an arylalkyl group, an arylalkoxy group, an arylalkylthio group, an arylalkenyl group, an arylalkynyl group, an amino group, a substituted amino group, a silyl group, a substituted silyl group, a halogen atom, an acyl group, an acyloxy group, an imine residue, an amido group, an acid imide group, a monovalent heterocyclic group, a hydroxy group, a substituted carboxy group, a cyano group, a nitro group, and a cross-linkable group. When the substituent is plurally present, they may be the same or different.

The substituent will be described below. The term “C_(m) to C_(n)” (m and n are positive integers satisfying m<n) represents that the number of carbon atoms of the organic group described with this term is m to n. For example, a C_(m) to C_(n) alkyl group represents that the number of carbon atoms of the alkyl group is m to n; a C_(m) to C_(n) alkylaryl group represents that the number of carbon atoms of the alkyl group is m to n; and an aryl-C_(m) to C_(n) alkyl group represents that the number of carbon atoms of the alkyl group is m to n. The following term may be used for groups other than the above substituents. A certain group that optionally has a substituent means a certain group having a substituent or a certain group having no substituent.

The alkyl group may be linear or branched, or may also be a cycloalkyl group. The number of carbon atoms of the alkyl group is usually 1 to 20 (usually 3 to 20 for a cycloalkyl group) and preferably 1 to 10 (3 to 10 for a cycloalkyl group). The alkyl group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the alkyl group may include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, and a lauryl group. A hydrogen atom in the alkyl group may be substituted with a fluorine atom. Examples of such a fluorine atom-substituted alkyl group may include a trifluoromethyl group, a pentafluoroethyl group, a perfluorobutyl group, a perfluorohexyl group, and a perfluorooctyl group. Examples of the C₁ to C₁₂ alkyl group may include a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, an isoamyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, and a lauryl group.

The alkoxy group (also referred to as an alkyloxy group) may be linear or branched, or may also be a cycloalkyloxy group. The number of carbon atoms of the alkoxy group is usually 1 to 20 (usually 3 to 20 for a cycloalkyloxy group) and preferably 1 to 10 (3 to 10 for a cycloalkyloxy group). The alkoxy group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the alkoxy group may include a methoxy group, an ethoxy group, a propyloxy group, an isopropyloxy group, a butoxy group, an isobutoxy group, a sec-butoxy group, a tert-butoxy group, a pentyloxy group, a hexyloxy group, a cyclohexyloxy group, a heptyloxy group, an octyloxy group, a nonyloxy group, a decyloxy group, and a lauryloxy group. A hydrogen atom in the alkoxy group may be substituted with a fluorine atom. Examples of such a fluorine atom-substituted alkoxy group may include a trifluoromethoxy group, a pentafluoroethoxy group, a perfluorobutoxy group, a perfluorohexyloxy group and a perfluorooctyloxy group. Examples of the alkoxy group may also include a methoxymethyloxy group and a 2-methoxyethyloxy group. Examples of the C₁ to C₁₂ alkoxy group may include a methoxy group, an ethoxy group, a propyloxy group, an isopropyloxy group, a butoxy group, an isobutoxy group, a sec-butoxy group, a tert-butoxy group, a pentyloxy group, a hexyloxy group, a cyclohexyloxy group, a heptyloxy group, an octyloxy group, a 2-ethylhexyloxy group, a nonyloxy group, a decyloxy group, a 3,7-dimethyloctyloxy group, and a lauryloxy group.

The alkylthio group may be linear or branched, or may also be a cycloalkylthio group. The number of carbon atoms of the alkylthio group is usually 1 to 20 (usually 3 to 20 for a cycloalkylthio group) and preferably 1 to 10 (3 to 10 for a cycloalkylthio group). The alkylthio group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the alkylthio group may include a methylthio group, an ethylthio group, a propylthio group, an isopropylthio group, a butylthio group, an isobutylthio group, a sec-butylthio group, a tert-butylthio group, a pentylthio group, a hexylthio group, a cyclohexylthio group, a heptylthio group, an octylthio group, a nonylthio group, a decylthio group, and a laurylthio group. A hydrogen atom in the alkylthio group may be substituted with a fluorine atom. Examples of such a fluorine atom-substituted alkylthio group may include a trifluoromethylthio group.

The aryl group is an atomic group remaining after removing one hydrogen atom that is bonded to a carbon atom constituting a ring (preferably, an aromatic ring) from an aromatic hydrocarbon, and also includes a group having a benzene ring, a group having a fused ring, and a group in which two or more independent benzene rings or fused rings are bonded through a single bond or a divalent organic group, for example, an alkenylene group such as a vinylene group. The aryl group has usually 6 to 60 carbon atoms and preferably 6 to 48 carbon atoms. The aryl group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the aryl group may include a phenyl group, a C₁ to C₁₂ alkoxyphenyl group, a C₁ to C₁₂ alkylphenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, and a 9-anthracenyl group. A hydrogen atom in the aryl group may be substituted with a fluorine atom. Examples of such a fluorine atom-substituted aryl group may include a pentafluorophenyl group. Among the aryl groups, a phenyl group, a C₁ to C₁₂ alkoxyphenyl group, and a C₁ to C₁₂ alkylphenyl group are preferred.

Among the aryl groups, examples of the C₁ to C₁₂ alkoxyphenyl group may include a methoxyphenyl group, an ethoxyphenyl group, a propyloxyphenyl group, an isopropyloxyphenyl group, a butoxyphenyl group, an isobutoxyphenyl group, a sec-butoxyphenyl group, a tert-butoxyphenyl group, a pentyloxyphenyl group, a hexyloxyphenyl group, a cyclohexyloxyphenyl group, a heptyloxyphenyl group, an octyloxyphenyl group, a 2-ethylhexyloxyphenyl group, a nonyloxyphenyl group, a decyloxyphenyl group, a 3,7-dimethyloctyloxyphenyl group, and a lauryloxyphenyl group.

Among the aryl groups, examples of the C₁ to C₁₂ alkylphenyl group may include a methylphenyl group, an ethylphenyl group, a dimethylphenyl group, a propylphenyl group, a mesityl group, a methylethylphenyl group, an isopropylphenyl group, a butylphenyl group, an isobutylphenyl group, a tert-butylphenyl group, a pentylphenyl group, an isoamylphenyl group, a hexylphenyl group, a heptylphenyl group, an octylphenyl group, a nonylphenyl group, a decylphenyl group, and a dodecylphenyl group.

The aryloxy group has usually 6 to 60 carbon atoms and preferably 6 to 48 carbon atoms. The aryloxy group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the aryloxy group may include a phenoxy group, a C₁ to C₁₂ alkoxyphenoxy group, a C₁ to C₁₂ alkylphenoxy group, a 1-naphthyloxy group, a 2-naphthyloxy group, and a pentafluorophenyloxy group. Among the aryloxy group, a phenoxy group, a C₁ to C₁₂ alkoxyphenoxy group and a C₁ to C₁₂ alkylphenoxy group are preferred.

Among the aryloxy groups, examples of the C₁ to C₁₂ alkoxyphenoxy group may include a methoxyphenoxy group, an ethoxyphenoxy group, a propyloxyphenoxy group, an isopropyloxyphenoxy group, a butoxyphenoxy group, an isobutoxyphenoxy group, a sec-butoxyphenoxy group, a tert-butoxyphenoxy group, a pentyloxyphenoxy group, a hexyloxyphenoxy group, a cyclohexyloxyphenoxy group, a heptyloxyphenoxy group, an octyloxyphenoxy group, a 2-ethylhexyloxyphenoxy group, a nonyloxyphenoxy group, a decyloxyphenoxy group, a 3,7-dimethyloctyloxyphenoxy group, and a lauryloxyphenoxy group.

The arylthio group is a group in which the above aryl group is bonded to a sulfur atom. The arylthio group has usually 6 to 60 carbon atoms and preferably 6 to 30 carbon atoms. The arylthio group may have a substituent on an aromatic ring of the aryl group, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the arylthio group may include a phenylthio group, a C₁ to C₁₂ alkoxyphenylthio group, a C₁ to C₁₂ alkylphenylthio group, a 1-naphthylthio group, a 2-naphthylthio group, and a pentafluorophenylthio group.

The arylalkyl group is a group in which the above aryl group is bonded to the above alkyl group. The arylalkyl group has usually 7 to 60 carbon atoms and preferably 7 to 30 carbon atoms. The arylalkyl group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the arylalkyl group may include a phenyl-C₁ to C₁₂ alkyl group, a C₁ to C₁₂ alkoxyphenyl-C₁ to C₁₂ alkyl group, a C₁ to C₁₂ alkylphenyl-C₁ to C₁₂ alkyl group, a 1-naphthyl-C₁ to C₁₂ alkyl group, and a 2-naphthyl-C₁ to C₁₂ alkyl group.

The arylalkoxy group (also referred to as an arylalkyloxy group) is a group in which the above aryl group is bonded to the above alkoxy group. The arylalkoxy group has usually 7 to 60 carbon atoms and preferably 7 to 30 carbon atoms. The arylalkoxy group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the arylalkoxy group may include a phenyl-C₁ to C₁₂ alkoxy group, a C₁ to C₁₂ alkoxyphenyl-C₁ to C₁₂ alkoxy group, a C₁ to C₁₂ alkylphenyl-C₁ to C₁₂ alkoxy group, a 1-naphthyl-C₁ to C₁₂ alkoxy group, and a 2-naphthyl-C₁ to C₁₂ alkoxy group.

The arylalkylthio group is a group in which the above aryl group is bonded to the above alkylthio group. The arylalkylthio group has usually 7 to 60 carbon atoms and preferably 7 to 30 carbon atoms. The arylalkylthio group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the arylalkylthio group may include a phenyl-C₁ to C₁₂ alkylthio group, a C₁ to C₁₂ alkoxyphenyl-C₁ to C₁₂ alkylthio group, a C₁ to C₁₂ alkylphenyl-C₁ to C₁₂ alkylthio group, a 1-naphthyl-C₁ to C₁₂ alkylthio group, and a 2-naphthyl-C₁ to C₁₂ alkylthio group.

The arylalkenyl group is a group in which the above aryl group is bonded to an alkenyl group. The arylalkenyl group has usually 8 to 60 carbon atoms and preferably 8 to 30 carbon atoms. The arylalkenyl group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the arylalkenyl group may include a phenyl-C₂ to C₁₂ alkenyl group, a C₁ to C₁₂ alkoxyphenyl-C₂ to C₁₂ alkenyl group, a C₁ to C₁₂ alkylphenyl-C₂ to C₁₂ alkenyl group, a 1-naphthyl-C₂ to C₁₂ alkenyl group, and a 2-naphthyl-C₂ to C₁₂ alkenyl group, and a C₁ to C₁₂ alkoxyphenyl-C₂ to C₁₂ alkenyl group and a C₂ to C₁₂ alkylphenyl-C₂ to C₁₂ alkenyl group are preferred. Examples of the C₂ to C₁₂ alkenyl group may include a vinyl group, a 1-propenyl group, a 2-propenyl group, a 1-butenyl group, a 2-butenyl group, a 1-pentenyl group, a 2-pentenyl group, a 1-hexenyl group, a 2-hexenyl group, and a 1-octenyl group.

The arylalkynyl group is a group in which the above aryl group is bonded to an alkynyl group. The arylalkynyl group has usually 8 to 60 carbon atoms and preferably 8 to 30 carbon atoms. The arylalkynyl group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the arylalkynyl group may include a phenyl-C₂ to C₁₂ alkynyl group, a C₁ to C₁₂ alkoxyphenyl-C₂ to C₁₂ alkynyl group, a C₁ to C₁₂ alkylphenyl-C₂ to C₁₂ alkynyl group, a 1-naphthyl-C₂ to C₁₂ alkynyl group, and a 2-naphthyl-C₂ to C₁₂ alkynyl group, and a C₁ to C₁₂ alkoxyphenyl-C₂ to C₁₂ alkynyl group and a C₁ to C₁₂ alkylphenyl-C₂ to C₁₂ alkynyl group are preferred. Examples of the C₂ to C₁₂ alkynyl group may include an ethynyl group, a 1-propynyl group, a 2-propynyl group, a 1-butynyl group, a 2-butynyl group, a 1-pentynyl group, a 2-pentynyl group, a 1-hexynyl group, a 2-hexynyl group, and a 1-octynyl group.

The substituted amino group means an amino group in which at least one hydrogen atom in an amino group is substituted with one or two groups selected from the group consisting of an alkyl group, an aryl group, an arylalkyl group, and a monovalent heterocyclic group. The alkyl group, the aryl group, the arylalkyl group, or the monovalent heterocyclic group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons of the substituted amino group. The carbon number of the substituted amino group is usually 1 to 60 and preferably 2 to 48, without including the number of carbon atoms of the substituent that the alkyl group, the aryl group, the arylalkyl group, or the monovalent heterocyclic group may have.

Examples of the substituted amino group may include a methylamino group, a dimethylamino group, an ethylamino group, a diethylamino group, a propylamino group, a dipropylamino group, an isopropylamino group, a diisopropylamino group, a butylamino group, an isobutylamino group, a sec-butylamino group, a tert-butylamino group, a pentylamino group, a hexylamino group, a cyclohexylamino group, a heptylamino group, an octylamino group, a 2-ethylhexylamino group, a nonylamino group, a decylamino group, a 3,7-dimethyloctylamino group, a laurylamino group, a cyclopentylamino group, a dicyclopentylamino group, a cyclohexylamino group, a dicyclohexylamino group, a ditrifluoromethylamino group, a phenylamino group, a diphenylamino group, a (C₁ to C₁₂ alkoxyphenyl)amino group, a di(C₁ to C₁₂ alkoxyphenyl)amino group, a di(C₁ to C₁₂ alkylphenyl)amino group, a 1-naphthylamino group, a 2-naphthylamino group, a pentafluorophenylamino group, a pyridylamino group, a pyridazinylamino group, a pyrimidinylamino group, a pyrazinylamino group, a triazinylamino group, a (phenyl-C₁ to C₁₂ alkyl)amino group, a (C₁ to C₁₂ alkoxyphenyl-C₁ to C₁₂ alkyl)amino group, a (C₁ to C₁₂ alkylphenyl-C₁ to C₁₂ alkyl)amino group, a di (C₁ to C₁₂ alkoxyphenyl-C₁ to C₁₂ alkyl]amino group, a di (C₁ to C₁₂ alkylphenyl-C₁ to C₁₂ alkyl)amino group, a 1-naphthyl-C₁ to C₁₂ alkylamino group, and a 2-naphthyl-C₁ to C₁₂ alkylamino group.

The substituted silyl group means a silyl group in which at least one hydrogen atom in a silyl group is substituted with one to three groups selected from the group consisting of an alkyl group, an aryl group, an arylalkyl group, and a monovalent heterocyclic group. The alkyl group, the aryl group, the arylalkyl group, or the monovalent heterocyclic group may have a substituent, and the number of carbons of the substituent is not included in the number of carbons of the substituted silyl group. The number of carbon atoms of the substituted silyl group is usually 1 to 60 and preferably 3 to 48, without including the number of carbon atoms of the substituent that the alkyl group, the aryl group, the arylalkyl group, or the monovalent heterocyclic group may have.

Examples of the substituted silyl group may include a trimethylsilyl group, a triethylsilyl group, a tripropylsilyl group, a triisopropylsilyl group, an isopropyldimethylsilyl group, an isopropyldiethylsilyl group, a tert-butyldimethylsilyl group, a pentyldimethylsilyl group, a hexyldimethylsilyl group, a heptyldimethylsilyl group, an octyldimethylsilyl group, a 2-ethylhexyldimethylsilyl group, a nonyldimethylsilyl group, a decyldimethylsilyl group, a 3,7-dimethyloctyldimethylsilyl group, a laurydimethylsilyl group, a (phenyl-C₁ to C₁₂ alkyl)silyl group, a (C₁ to C₁₂ alkoxyphenyl-C₁ to C₁₂ alkyl)silyl group, a (C₁ to C₁₂ alkylphenyl-C₁ to C₁₂ alkyl)silyl group, a (1-naphthyl-C₁ to C₁₂ alkyl)silyl group, a (2-naphthyl-C₁ to C₁₂ alkyl)silyl group, a (phenyl-C₁ to C₁₂ alkyl)dimethylsilyl group, a triphenylsilyl group, a tri(p-xylyl)silyl group, a tribenzylsilyl group, a diphenylmethylsilyl group, a tert-butyldiphenylsilyl group, and a dimethylphenylsilyl group.

Examples of the halogen atom may include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.

The acyl group (also referred to as an alkyl carbonyl group) has usually 2 to 20 carbon atoms and preferably 2 to 18 carbon atoms. The acyl group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the acyl group may include an acetyl group, a propionyl group, a butyryl group, an isobutyryl group, a pivaloyl group, a benzoyl group, a trifluoroacetyl group, and a pentafluorobenzoyl group.

The acyloxy group (also referred to as an alkyl carbonyloxy group) has usually 2 to 20 carbon atoms and preferably 2 to 18 carbon atoms. The acyloxy group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the acyloxy group may include an acetoxy group, a propionyloxy group, a butyryloxy group, an isobutyryloxy group, a pivaloyloxy group, a benzoyloxy group, a trifluoroacetyloxy group, and a pentafluorobenzoyloxy group.

The imine residue means a group remaining after removing one hydrogen atom from an imine compound having a structure represented by at least any one of formula: H—N═C< and formula: —N═CH—. Examples of such an imine compound may include aldimine; ketimine; and a compound in which a hydrogen atom that is bonded to a nitrogen atom in aldimine is substituted with a group such as an alkyl group, an aryl group, an arylalkyl group, an arylalkenyl group, and an arylalkynyl group. The number of carbon atoms of the imine residue is usually 2 to 20 and preferably 2 to 18. The imine residue may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the imine residue may include a group represented by formula: —CR^(β)═N—R^(γ) or general formula: —N═C(R^(γ))₂, (where R^(β) represents a hydrogen atom, an alkyl group, an aryl group, an arylalkyl group, an arylalkenyl group, or an arylalkynyl group; and R^(γ) independently represents an alkyl group, an aryl group, an arylalkyl group, an arylalkenyl group, or an arylalkynyl group, and when two R^(γ) are present, the two R^(γ) may be combined with each other to form a ring as a divalent group (e.g., an alkylene group having 2 to 18 carbon atoms such as an ethylene group, a trimethylene group, a tetramethylene group, a pentamethylene group, and a hexamethylene group). Examples of the imine residue may include the following groups.

The amido group has usually 1 to 20 carbon atoms and preferably 2 to 18 carbon atoms. The amido group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the amido group may include a formamido group, an acetamido group, a propioamido group, a butyramido group, a benzamido group, a trifluoroacetamido group, a pentafluorobenzamido group, a diformamido group, a diacetamido group, a dipropioamido group, a dibutyramido group, a dibenzamido group, a ditrifluoroacetamido group, and a dipentafluorobenzamido group.

The acid imido group means a group obtained by removing a hydrogen atom that is bonded to a nitrogen atom from an acid imide. The acid imido group has usually 4 to 20 carbon atoms and preferably 4 to 18 carbon atoms. The acid imido group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the acid imido group may include the following groups.

The monovalent heterocyclic group means an atomic group remaining after removing one hydrogen atom that is bonded to a carbon atom constituting a ring from a heterocyclic compound. The heterocyclic compound refers to an organic compound containing not only a carbon atom, but also a hetero atom such as an oxygen atom, a sulfur atom, a nitrogen atom, a phosphorus atom, a boron atom, a silicon atom, a selenium atom, a tellurium atom, and an arsenic atom as an element constituting the ring, among organic compounds having a cyclic structure. The monovalent heterocyclic group has usually 3 to 60 carbon atoms and preferably 3 to 20 carbon atoms. The monovalent heterocyclic group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of such a monovalent heterocyclic group may include a thienyl group, a C₁ to C₁₂ alkylthienyl group, a pyrrolyl group, a furyl group, a pyridyl group, a C₁ to C₁₂ alkylpyridyl group, a pyridazinyl group, a pyrimidyl group, a pyrazinyl group, a triazinyl group, a pyrrolidyl group, a piperidyl group, a quinolyl group, and an isoquinolyl group, and among them, a thienyl group, a C₁ to C₁₂ alkylthienyl group, a pyridyl group, a C₁ to C₁₂ alkylpyridyl group, and a triazinyl group are preferred. The monovalent heterocyclic group is preferably a monovalent aromatic heterocyclic group.

The substituted carboxy group means a carboxy group in which a hydrogen atom in a carboxy group is substituted with an alkyl group, an aryl group, an arylalkyl group, or a monovalent heterocyclic group, that is, a group represented by formula: —C(═O)OR* (where R* represents an alkyl group, an aryl group, an arylalkyl group, or a monovalent heterocyclic group). The substituted carboxy group has usually 2 to 60 carbon atoms and preferably 2 to 48 carbon atoms. The alkyl group, the aryl group, the arylalkyl group, or the monovalent heterocyclic group may have a substituent, and the number of carbons of the substituent is not included in the above number of carbons.

Examples of the substituted carboxy group may include a methoxycarbonyl group, an ethoxycarbonyl group, a propyloxycarbonyl group, an isopropyloxycarbonyl group, a butoxycarbonyl group, an isobutoxycarbonyl group, a sec-butoxycarbonyl group, a tert-butoxycarbonyl group, a pentyloxycarbonyl group, a hexyloxycarbonyl group, a cyclohexyloxycarbonyl group, a heptyloxycarbonyl group, an octyloxycarbonyl group, a 2-ethylhexyloxycarbonyl group, a nonyloxycarbonyl group, a decyloxycarbonyl group, a 3,7-dimethyloctyloxycarbonyl group, a dodecyloxycarbonyl group, a trifluoromethoxycarbonyl group, a pentafluoroethoxycarbonyl group, a perfluorobutoxycarbonyl group, a perfluorohexyloxycarbonyl group, a perfluorooctyloxycarbonyl group, a phenoxycarbonyl group, a naphthoxycarbonyl group, and a pyridyloxycarbonyl group.

The cross-linkable group means a group that can form bonds among two or more molecules by causing a polymerization reaction through the action of heat, light, a thermal polymerization initiator, or a photopolymerization initiator.

Examples of the cross-linkable group may include an ethenyl group, an ethynyl group, a butenyl group, an acryloyl group, an acrylate group, an acrylamidyl group, a methacryl group, a methacrylate group, a methacrylamidyl group, an ethenyloxy group, an ethenylamino group, a hydroxysilyl group, a functional group containing a structure of a small ring (e.g., cyclopropane, cyclobutane, benzocyclobutene, epoxide, oxetane, diketene, thiirane, lactone, and lactam), and a functional group having a structure of a siloxane derivative. In addition to the above groups, a combination of groups that can form an ester bond or an amide bond may be used. Examples of the combination of groups that can form an ester bond or an amide bond may include a combination of an ester group and an amino group and a combination of an ester group and a hydroxyl group.

The substituent other than R¹ that the above Ar¹ has is preferably the alkyl group, the alkoxy group, the aryl group, the aryloxy group, the carboxyl group or the substituted carboxyl group, or the halogen atom, because the synthesis of the raw material monomer is simplified.

In Formula (1), m1 represents an integer of 1 or more, preferably an integer of from 1 to 4, and more preferably an integer of from 1 to 3.

In Formula (1), m2 represents an integer of 1 or more, preferably an integer of from 1 to 4, and more preferably an integer of from 1 to 3.

The (2+m1+m2)-valent fused polycyclic aromatic group represented by Ar¹ in Formula (1) may include a group remaining after removing (2+m1+m2) hydrogen atoms from a fused polycyclic aromatic group in which two or more benzene rings are fused.

Examples of the fused polycyclic aromatic group may includes the following:

In view of the solubility of the polymer compound, the (2+m1+m2)-valent fused polycyclic aromatic group is preferably a group remaining after removing (2+m1+m2) hydrogen atoms from the group represented by any one of Formulae 1 to 4, 7, and 8, more preferably a group remaining after removing (2+m1+m2) hydrogen atoms from the group represented by any one of Formulae 1 to 3, 7, and 8, and further more preferably a group remaining after removing (2+m1+m2) hydrogen atoms from the group represented by any one of Formulae 1 to 3, and 7.

In Formula (1), Ar¹ is preferably a group remaining after removing (m1+m2) hydrogen atoms from a divalent group represented by any one of Formulae 10 to 17.

—Group Represented by Formula (2)—

In Formula (2), R³ represents a single bond or a (1+m3)-valent organic group that optionally has a substituent. The group represented by Formula (2) is a monovalent group.

In Formula (2), examples of the (1+m3)-valent organic group that optionally has a substituent represented by R³ may include: a group remaining after removing m3 hydrogen atoms from an alkyl group having 1 to 20 carbon atoms that optionally has a substituent, such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m3 hydrogen atoms from an aryl group having 6 to 30 carbon atoms that optionally has a substituent, such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, a 9-anthracenyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m3 hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms that optionally has a substituent, such as a methoxy group, an ethoxy group, a propyloxy group, a butoxy group, a pentyloxy group, a hexyloxy group, a nonyloxy group, a dodecyloxy group, a cyclopropyloxy group, a cyclobutyloxy group, a cyclopentyloxy group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m3 hydrogen atoms from an amino group having a substituent containing a carbon atom; and a group remaining after removing m3 hydrogen atoms from a silyl group having a substituent containing a carbon atom. The number of carbons of the substituent is not included in the above number of carbons. Because the synthesis of the raw material monomer is simplified, preferred examples are a group remaining after removing m3 hydrogen atoms from an alkyl group, a group remaining after removing m3 hydrogen atoms from an aryl group, and a group remaining after removing m3 hydrogen atoms from an alkoxy group. More preferably, it is a group remaining after removing m3 hydrogen atoms from an aryl group.

Examples of the above substituent may include the same as the substituent exemplified in the description with respect to the above Ar¹. When the substituent is plurally present, they may be the same or different.

In Formula (2), m3 represents an integer of 1 or more (e.g., 1, 2, or 3), and when R³ is a single bond, m3 represents 1.

In Formula (2), examples of the divalent organic group represented by Q¹ may include: a divalent chain saturated hydrocarbon group having 1 to 50 carbon atoms that optionally has a substituent, such as a methylene group, an ethylene group, a 1,2-propylene group, a 1,3-propylene group, a 1,2-butylene group, a 1,3-butylene group, a 1,4-butylene group, a 1,5-pentylene group, a 1,6-hexylene group, a 1,9-nonylene group, a 1,12-dodecylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a divalent chain unsaturated hydrocarbon group having 2 to 50 carbon atoms that optionally has a substituent including an alkenylene group having 2 to 50 carbon atoms that optionally has a substituent, such as an ethenylene group, a propenylene group, a 3-butenylene group, a 2-butenylene group, a 2-pentenylene group, a 2-hexenylene group, a 2-nonenylene group, a 2-dodecenylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent and an ethynylene group; a divalent saturated cyclic hydrocarbon group having 3 to 50 carbon atoms that optionally has a substituent, such as a cyclopropylene group, a cyclobutylene group, a cyclopentylene group, a cyclohexylene group, a cyclononylene group, a cyclododecylene group, a norbornylene group, an adamantylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; an arylene group having 6 to 50 carbon atoms that optionally has a substituent, such as a 1,3-phenylene group, a 1,4-phenylene group, a 1,4-naphthylene group, a 1,5-naphthylene group, a 2,6-naphthylene group, a biphenyl-4,4′-diyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; an alkyleneoxy group having 1 to 50 carbon atoms that optionally has a substituent, such as a methyleneoxy group, an ethyleneoxy group, a propyleneoxy group, a butyleneoxy group, a pentyleneoxy group, a hexyleneoxy group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent (that is, a divalent organic group represented by formula: —R^(d)—O— (where R^(d) is an alkylene group having 1 to 50 carbon atoms that optionally has a substituent, such as a methylene group, an ethylene group, a propylene group, a butylene group, a pentylene group, a hexylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent)); an imino group having a substituent containing a carbon atom; and a silylene group having a substituent containing a carbon atom. The number of carbons of the substituent is not included in the above number of carbons. Because the synthesis of a monomer that is a raw material of the macromolecule compound (referred to as the “raw material monomer” in this specification) is simplified, preferred examples are a divalent chain saturated hydrocarbon group, an arylene group, and an alkyleneoxy group.

The group exemplified for the divalent organic group represented by Q¹ may have a substituent. Examples of the substituent may include the same as the substituent exemplified in the description with respect to the above Q¹. When the substituent is plurally present, they may be the same or different.

In Formula (2), Y¹ represents —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, —PO₃ ²⁻, or —B(R^(α))₃ ⁻. In view of the acidity of the polymer compound, Y¹ is preferably, —CO₂ ⁻, —SO₂ ⁻, or —PO₃ ²⁻ and more preferably —CO₂ ⁻. In view of the stability of the polymer compound, Y¹ is preferably —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, or —PO₃ ²⁻. R^(α) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent or an aryl group having 6 to 50 carbon atoms that optionally has a substituent. The number of carbons of the substituent is not included in the above number of carbons. Examples of the substituent may include the same as the substituent exemplified in the description with respect to Formula (1). When the substituent is plurally present, they may be the same or different. Examples of R^(α) may include: an alkyl group having 1 to 20 carbon atoms such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, and a lauryl group; and an aryl group having 6 to 30 carbon atoms such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, and a 9-anthracenyl group.

In Formula (2), M¹ represents a metal cation, or represents an ammonium cation that optionally has a substituent. The metal cation is preferably a monovalent, divalent, or trivalent ion. Examples of the metal cation may include an ion of Li, Na, K, Cs, Be, Mg, Ca, Ba, Ag, Al, Bi, Cu, Fe, Ga, Mn, Pb, Sn, Ti, V, W, Y, Yb, Zn, Zr, and Li⁺, Na⁺, K⁺, Rb⁺, Cs⁺, Ag⁺, Mg²⁺, and Ca²⁺ are preferred. Examples of the substituent that the ammonium cation may have may include: an alkyl group having 1 to 10 carbon atoms such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a n-butyl group, an i-butyl group, and a tert-butyl group; and an aryl group having 6 to 60 carbon atoms such as a phenyl group, a 1-naphthyl group, and a 2-naphthyl group.

In Formula (2), Z¹ represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(a))₄ ⁻, R^(a)SO₃ ⁻, R^(a)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻, or PF₆ ⁻. R^(a) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent or an aryl group having 6 to 50 carbon atoms that optionally has a substituent. The number of carbons of the substituent is not included in the above number of carbons. Examples of the substituent may include the same as the substituent exemplified in the description with respect to Formula (1). When the substituent is plurally present, they may be the same or different. Examples of R^(a) may include: an alkyl group having 1 to 20 carbon atoms such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, and a lauryl group; and an aryl group having 6 to 30 carbon atoms such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, and a 9-anthracenyl group.

In Formula (2), n1 represents an integer of 0 or more, and in view of the synthesis of the raw material monomer, n1 is preferably an integer of from 0 to 8, and more preferably an integer of from 0 to 2.

In Formula (2), a1 represents an integer of 1 or more (e.g., an integer of from 1 to 10), and b1 represents an integer of 0 or more (e.g., an integer of from 1 to 10).

a1 and b1 are selected so that the electric charge of the group represented by Formula (2) is zero. For example, when Y¹ is —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, —PO₃ ²⁻, or —B(R^(α))₃ ⁻; M¹ is a monovalent metal cation or an ammonium cation that optionally has a substituent; and Z¹ is F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(a))₄ ⁻, R^(a)SO₃ ⁻, R^(a)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, HSO₄ ⁻, H₂PO₄ ⁻, BF₄ ⁻, or PF₆ ⁻, a1 and b1 are selected so as to satisfy a1=b1+1. When Y¹ is —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, —PO₃ ²⁻, or —B(R^(α))₃ ⁻; M¹ is a divalent metal cation; and Z¹ is F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(a))₄ ⁻, R^(a)SO₃ ⁻, R^(a)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃, HSO₄ ⁻, H₂PO₄ ⁻, BF₄ ⁻, or PF₆ ⁻, a1 and b1 are selected so as to satisfy b1=2×a1−1. When Y¹ is —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, or —PO₃ ²⁻; M¹ is a trivalent metal cation; and Z¹ is F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(a))₄ ⁻, R^(a)SO₃ ⁻, R^(a)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, HSO₄ ⁻, H₂PO₄ ⁻, BF₄ ⁻, or PF₆ ⁻, a1 and b1 are selected so as to satisfy b1=3×a1−1. When Y¹ is —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, —PO₃ ²⁻, or —B(R^(α))₃ ⁻; M¹ is a monovalent metal cation or an ammonium cation that optionally has a substituent; and Z¹ is SO₄ ²⁻ or HPO₄ ²⁻, a1 and b1 are selected so as to satisfy a1=2×b1+1. In any one of the above numerical formulae expressing the relationship between a1 and b1, a1 is preferably an integer of from 1 to 5, and more preferably 1 or 2.

Examples of the group represented by Formula (2) may include groups represented by the following formulae. In the following formulae, M represents Li, Na, K, Rb, Cs, or N(CH₃)₄.

—Group Represented by Formula (3)—

In Formula (3), R⁴ represents a single bond or a (1+m4)-valent organic group that optionally has a substituent. The group represented by Formula (3) is a monovalent group.

In Formula (3), examples of the (1+m4)-valent organic group that optionally has a substituent represented by R⁴ may include a group remaining after removing m4 hydrogen atoms from an alkyl group having 1 to 20 carbon atoms that optionally has a substituent, such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m4 hydrogen atoms from an aryl group having 6 to 30 carbon atoms that optionally has a substituent, such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, a 9-anthracenyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m4 hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms that optionally has a substituent, such as a methoxy group, an ethoxy group, a propyloxy group, a butoxy group, a pentyloxy group, a hexyloxy group, a nonyloxy group, a dodecyloxy group, a cyclopropyloxy group, a cyclobutyloxy group, a cyclopentyloxy group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m4 hydrogen atoms from an amino group having a substituent containing a carbon atom; and a group remaining after removing m4 hydrogen atoms from a silyl group having a substituent containing a carbon atom. The number of carbons of the substituent is not included in the above number of carbons. Because the synthesis of the raw material monomer is simplified, preferred examples are a group remaining after removing m4 hydrogen atoms from an alkyl group, a group remaining after removing m4 hydrogen atoms from an aryl group, and a group remaining after removing m4 hydrogen atoms from an alkoxy group. More preferably, it is a group remaining after removing m4 hydrogen atoms from an aryl group.

Examples of the above substituent may include the same as the substituent exemplified in the description with respect to the above Ar¹. When the substituent is plurally present, they may be the same or different.

In Formula (3), m4 represents an integer of 1 or more (e.g., 1, 2, or 3), and when R⁴ is a single bond, m4 represents 1.

In Formula (3), examples of the divalent organic group represented by Q² may include the same as the group exemplified with respect to the divalent organic group represented by Q¹. Because the synthesis of the raw material monomer is simplified, preferred examples are a divalent chain saturated hydrocarbon group, an arylene group, and an alkyleneoxy group.

The group exemplified for the divalent organic group represented by Q² may have a substituent. Examples of the substituent may include the same as the substituent exemplified in the description with respect to Formula (1). When the substituent is plurally present, they may be the same or different.

In Formula (3), Y² represents a carbocation, an ammonium cation, a phosphonium cation, a sulfonium cation, or an iodonium cation.

Examples of the carbonation may include a group represented by:

—C⁺R₂

(where R represents the above alkyl group or aryl group; R that is plurally present may be the same or different).

Examples of the ammonium cation may include a group represented by:

—N⁺R₃

(where R represents the same meaning as described above; R that is plurally present may be the same or different).

Examples of the phosphonium cation may include a group represented by:

—P⁺R₃

(where R represents the same meaning as described above; R that is plurally present may be the same or different).

Examples of the sulfonium cation may include a group represented by:

—S⁺R₂

(where R represents the same meaning as described above; R that is plurally present may be the same or different).

Examples of the iodonium cation may include a group represented by:

—I⁺R₂

(where R represents the same meaning as described above; R that is plurally present may be the same or different).

In Formula (2), because of the simplicity of the synthesis of the raw material monomer and the stability of the raw material monomer and the polymer compound against air, moisture, or heat, Y² is preferably a carbocation, an ammonium cation, a phosphonium cation, or a sulfonium cation, and more preferably an ammonium cation.

In Formula (3), M² represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(b))₄ ⁻, R^(b)SO₃ ⁻, R^(b)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻, or PF₆ ⁻. R^(b) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent or an aryl group having 6 to 50 carbon atoms that optionally has a substituent. The number of carbons of the substituent is not included in the above number of carbons. Examples of the substituent may include the same as the substituent exemplified in the description with respect to Formula (1). When the substituent is plurally present, they may be the same or different. Examples of R^(b) may include: an alkyl group having 1 to 20 carbon atoms such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, and a lauryl group; and an aryl group having 6 to 30 carbon atoms such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, and a 9-anthracenyl group.

In Formula (3), Z² represents a metal cation, or represents an ammonium cation that optionally has a substituent. Examples of the metal cation or ammonium cation that optionally has a substituent represented by Z² may include the same as exemplified with respect to the metal cation or ammonium cation that optionally has a substituent represented by the above Z¹.

In Formula (3), n2 represents an integer of 0 or more, preferably an integer of from 0 to 6, and more preferably an integer of from 0 to 2.

In Formula (3), a2 represents an integer of 1 or more (e.g., an integer of from 1 to 10), and b2 represents an integer of 0 or more (e.g., an integer of from 0 to 10).

a2 and b2 are selected so that the electric charge of the group represented by Formula (3) is zero, as is the case with a1 and b1 with respect to Formula (2). a2 is preferably an integer of from 1 to 5 and more preferably 1 or 2.

Examples of the group represented by Formula (3) may include groups represented by the following formulae. In the following formulae, X represents F, Cl, Br, I, B(C₆H₅)₄, CH₃COO, or CF₃SO₃.

—Group Represented by Formula (4)—

In Formula (4), R⁵ represents a single bond or a (1+m5)-valent organic group that optionally has a substituent. The group represented by Formula (4) is a monovalent group.

In Formula (4), examples of the (1+m5)-valent organic group that optionally has a substituent represented by R⁵ may include a group remaining after removing m5 hydrogen atoms from an alkyl group having 1 to 20 carbon atoms that optionally has a substituent, such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m5 hydrogen atoms from an aryl group having 6 to 30 carbon atoms that optionally has a substituent, such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, a 9-anthracenyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m5 hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms that optionally has a substituent, such as a methoxy group, an ethoxy group, a propyloxy group, a butoxy group, a pentyloxy group, a hexyloxy group, a nonyloxy group, a dodecyloxy group, a cyclopropyloxy group, a cyclobutyloxy group, a cyclopentyloxy group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m5 hydrogen atoms from an amino group having a substituent containing a carbon atom; and a group remaining after removing m5 hydrogen atoms from a silyl group having a substituent containing a carbon atom. The number of carbons of the substituent is not included in the above number of carbons. Because the synthesis of the raw material monomer is simplified, preferred examples are a group remaining after removing m5 hydrogen atoms from an alkyl group, a group remaining after removing m5 hydrogen atoms from an aryl group, and a group remaining after removing m5 hydrogen atoms from an alkoxy group.

Examples of the substituent may include the same as the substituent exemplified in the description with respect to the above Ar¹. When the substituent is plurally present, they may be the same or different.

In Formula (4), m5 represents an integer of 1 or more (e.g., 1, 2, or 3), and when R⁵ is a single bond, m5 represents 1.

In Formula (4), examples of the divalent organic group represented by Q³ may include the same as the group exemplified with respect to the divalent organic group represented by Q¹. Because the synthesis of the raw material monomer is simplified, preferred examples are a divalent chain saturated hydrocarbon group, an arylene group, and an alkyleneoxy group.

The group exemplified for the divalent organic group represented by Q³ may have a substituent. Examples of the substituent may include the same as the substituent exemplified in the description with respect to the above Ar¹. When the substituent is plurally present, they may be the same or different.

In Formula (3), n3 represents an integer of 0 or more, preferably an integer of from 0 to 20, and more preferably an integer of from 0 to 8.

In Formula (3), Y³ represents a cyano group or a group represented by any of Formulae (5) to (13). The group represented by any of Formulae (5) to (13) is a monovalent group.

In Formulae (5) to (13), examples of the divalent hydrocarbon group that optionally has a substituent represented by R′ may include: a divalent chain saturated hydrocarbon group having 1 to 50 carbon atoms that optionally has a substituent, such as a methylene group, an ethylene group, a 1,2-propylene group, a 1,3-propylene group, a 1,2-butylene group, a 1,3-butylene group, a 1,4-butylene group, a 1,5-pentylene group, a 1,6-hexylene group, a 1,9-nonylene group, a 1,12-dodecylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a divalent chain unsaturated hydrocarbon group having 2 to 50 carbon atoms that optionally has a substituent including an alkenylene group having 2 to 50 carbon atoms that optionally has a substituent, such as an ethenylene group, a propenylene group, a 3-butenylene group, a 2-butenylene group, a 2-pentenylene group, a 2-hexenylene group, a 2-nonenylene group, a 2-dodecenylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent, and an ethynylene group; a divalent saturated cyclic hydrocarbon group having 3 to 50 carbon atoms that optionally has a substituent, such as a cyclopropylene group, a cyclobutylene group, a cyclopentylene group, a cyclohexylene group, a cyclononylene group, a cyclododecylene group, a norbornylene group, an adamantylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; and an arylene group having 6 to 50 carbon atoms that optionally has a substituent, such as a 1,3-phenylene group, a 1,4-phenylene group, a 1,4-naphthylene group, a 1,5-naphthylene group, a 2,6-naphthylene group, a biphenyl-4,4′-diyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent. The number of carbons of the substituent is not included in the above number of carbons.

Examples of the substituent may include the same as the substituent exemplified in the description with respect to the above Ar¹. When the substituent is plurally present, they may be the same or different.

In Formulae (5) to (13), examples of the monovalent hydrocarbon group that optionally has a substituent represented by R″ may include: an alkyl group having 1 to 20 carbon atoms that optionally has a substituent, such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; and an aryl group having 6 to 30 carbon atoms that optionally has a substituent, such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, a 9-anthracenyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent. The number of carbons of the substituent is not included in the above number of carbons. In view of the solubility of the polymer compound, preferred examples are a methyl group, an ethyl group, a phenyl group, a 1-naphthyl group, and 2-naphthyl group. Examples of the substituent may include the same as the substituent exemplified in the description with respect to the above Ar¹. When the substituent is plurally present, they may be the same or different.

In Formula (6), examples of the trivalent hydrocarbon group that optionally has a substituent represented by R′″ may include: an alkanetriyl group having 1 to 20 carbon atoms that optionally has a substituent, such as a methanetriyl group, an ethanetriyl group, a 1,2,3-propanetriyl group, a 1,2,4-butanetriyl group, a 1,2,5-pentanetriyl group, a 1,3,5-pentanetriyl group, a 1,2,6-hexanetriyl group, a 1,3,6-hexanetriyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; and an arenetriyl group having 6 to 30 carbon atoms that optionally has a substituent, such as a 1,2,3-benzenetriyl group, a 1,2,4-benzenetriyl group, a 1,3,5-benzenetriyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent. The number of carbons of the substituent is not included in the above number of carbons. In view of the solubility of the polymer compound, preferred examples are a methanetriyl group, an ethanetriyl group, a 1,2,4-benzenetriyl group, and a 1,3,5-benzenetriyl group. Examples of the substituent may include the same as the substituent exemplified in the description with respect to Formula (1). When the substituent is plurally present, they may be the same or different.

With respect to —NR^(C) ₂ and —C(═O)NR^(c) ₂ that are examples of R″, R^(c) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent or an aryl group having 6 to 50 carbon atoms that optionally has a substituent. The number of carbons of the substituent is not included in the above number of carbons. Examples of the substituent may include the same as the substituent exemplified in the description with respect to Formula (1). In Formulae (5) to (13), in view of the solubility of the polymer compound, preferred examples of R^(c) are a methyl group, an ethyl group, a phenyl group, a 1-naphthyl group, and 2-naphthyl group.

In Formulae (5) and (6), a3 represents an integer of 1 or more, preferably an integer of from 3 to 10. In Formulae (7) to (13), a4 represents an integer of 0 or more. In Formula (7), a4 is preferably an integer of from 0 to 30, more preferably an integer of from 3 to 20. In Formulae (8) to (11), a4 is preferably an integer of from 0 to 10, more preferably an integer of from 0 to 5. In Formula (12), a4 is preferably an integer of from 0 to 20, more preferably an integer of from 3 to 20. In Formula (13), a4 is preferably an integer of from 0 to 20, more preferably an integer of from 0 to 10.

Because the synthesis of the raw material monomer is simplified, Y³ is preferably a cyano group, a group represented by Formula (5), a group represented by Formula (6), a group represented by Formula (7), a group represented by Formula (11), and a group represented by Formula (12), more preferably a group represented by Formula (5), a group represented by Formula (6), a group represented by Formula (7), and a group represented by Formula (12), particularly preferably the following groups.

[Specific Examples of Group Represented by Formula (4)]

Examples of the group represented by Formula (4) may include groups represented by the following formulae.

[Examples of Structural Unit Represented by Formula (1)]

Examples of the structural unit represented by Formula (1) may include structural units optionally having a substituent represented by the following formulae.

In view of the stability against an electronic current of the polymer compound according to the present invention, the structural unit represented by Formula (1) is preferably a structural unit that optionally has a substituent represented by the following formulae. In the following formulae, M means the same as described above, and examples of the substituent may include the same as the substituent exemplified in the above description with respect to Ar¹. When the substituent is plurally present, they may be the same or different.

Structural Unit Represented by Formula (14)

In Formula (14), Ar² represents a (2+m6+m7)-valent fused polycyclic aromatic group that optionally has a substituent. R⁶ represents the group represented by Formula (15) or Formula (16), and in view of the stability against an electronic current of the polymer compound according to the present invention, R⁶ is preferably the group represented by Formula (15). R⁷ represents the group represented by Formula (4); m6 is an integer of 1 or more; and m7 represents an integer of 0 or more.

Ar² may have a substituent other than R⁶ or R⁷. Examples of the substituent may include the same as the substituent exemplified in the above description with respect to Ar¹.

In Formula (14), m6 represents an integer of 1 or more, preferably an integer of from 1 to 4, and more preferably an integer of from 1 to 3.

In Formula (14), m7 represents an integer of 0 or more, preferably an integer of from 0 to 4, and more preferably an integer of from 0 to 3.

Examples of the (2+m6+m7)-valent fused polycyclic aromatic group represented by Ar² in Formula (2) may include a (2+m6+m7)-valent group remaining after removing (2+m6+m7) hydrogen atoms from a fused polycyclic aromatic ring in which two or more benzene rings are fused.

Examples of the fused polycyclic aromatic ring may include the same as the ring exemplified in the above description with respect to Ar¹ described above.

In view of the solubility of the polymer compound, the (2+m6+m7)-valent fused polycyclic aromatic group is preferably a group remaining after removing (2+m6+m7) hydrogen atoms from the group represented by any one of Formulae 1 to 4, 7, and 8, more preferably a group remaining after removing (2+m6+m7) hydrogen atoms from the group represented by any one of Formulae 1 to 3, 7, and 8, and further more preferably a group remaining after removing (2+m6+m7) hydrogen atoms from the group represented by any one of Formulae 1 to 3, and 7.

In Formula (2), Ar² is preferably a group remaining after removing (m6+m7) hydrogen atoms from the divalent group represented by any one of Formulae 10 to 17.

—Group Represented by Formula (15)—

In Formula (15), R⁸ represents a (1+m8+m9) valent organic group that optionally has a substituent. The group represented by Formula (15) is a monovalent group.

In Formula (15), examples of the (1+m8+m9) valent organic group that optionally has a substituent represented by R⁸ may include a group remaining after removing (m8+m9) hydrogen atoms from an alkyl group having 1 to 20 carbon atoms that optionally has a substituent, such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing (m8+m9) hydrogen atoms from an aryl group having 6 to 30 carbon atoms that optionally has a substituent, such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, a 9-anthracenyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing (m8+m9) hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms that optionally has a substituent, such as a methoxy group, an ethoxy group, a propyloxy group, a butoxy group, a pentyloxy group, a hexyloxy group, a nonyloxy group, a dodecyloxy group, a cyclopropyloxy group, a cyclobutyloxy group, a cyclopentyloxy group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing (m8+m9) hydrogen atoms from an amino group having a substituent containing a carbon atom; and a group remaining after removing (m8+m9) hydrogen atoms from a silyl group having a substituent containing a carbon atom. The number of carbons of the substituent is not included in the above number of carbons. Because the synthesis of the raw material monomer is simplified, preferred examples are a group remaining after removing (m8+m9) hydrogen atoms from an alkyl group, a group remaining after removing (m8+m9) hydrogen atoms from an aryl group, and a group remaining after removing (m8+m9) hydrogen atoms from an alkoxy group, and a more preferred example is a group remaining after removing (m8+m9) hydrogen atoms from an aryl group.

Examples of the substituent may include the same as the substituent exemplified in the above description with respect to Ar¹. When the substituent is plurally present, they may be the same or different.

In Formula (15), m8 and m9 each independently represent an integer of 1 or more (e.g., 1, 2, or 3).

In Formula (15) Q¹, Q³, Y¹, Y³, M¹, Z¹, n1, n3, a1, and b1 are the same as the corresponding definitions above.

[Specific Examples of Group Represented by Formula (15)]

Examples of the group represented by Formula (15) may include groups represented by the following formulae. In the following formulae, M represents the same meaning as described above.

—Group Represented by Formula (16)—

In Formula (16), R⁹ represents a (1+m10+m11) valent organic group that optionally has a substituent. The group represented by Formula (16) is a monovalent group.

In Formula (16), examples of the (1+m10+m11) valent organic group represented by R⁹ may include a group remaining after removing (m10+m11) hydrogen atoms from an alkyl group having 1 to 20 carbon atoms that optionally has a substituent, such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing (m10+m11) hydrogen atoms from an aryl group having 6 to 30 carbon atoms that optionally has a substituent, such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, a 9-anthracenyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing (m10+m11) hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms that optionally has a substituent, such as a methoxy group, an ethoxy group, a propyloxy group, a butoxy group, a pentyloxy group, a hexyloxy group, a nonyloxy group, a dodecyloxy group, a cyclopropyloxy group, a cyclobutyloxy group, a cyclopentyloxy group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing (m10+m11) hydrogen atoms from an amino group having a substituent containing a carbon atom; and a group remaining after removing (m10+m11) hydrogen atoms from a silyl group having a substituent containing a carbon atom. The number of carbons of the substituent is not included in the above number of carbons. Because the synthesis of the raw material monomer is simplified, preferred examples are a group remaining after removing (m10+m11) hydrogen atoms from an alkyl group, a group remaining after removing (m10+m11) hydrogen atoms from an aryl group, and a group remaining after removing (m10+m11) hydrogen atoms from an alkoxy group, and a more preferred example is a group remaining after removing (m10+m11) hydrogen atoms from an aryl group.

Examples of the substituent may include the same as the substituent exemplified in above the description with respect to Ar¹. When the substituent is plurally present, they may be the same or different.

In Formula (16), m10 and m11 each independently represent an integer of 1 or more (e.g., 1, 2, or 3 for each).

In Formula (16) Q², Q³, Y², Y³, M², Z², n2, n3, a2, and b2 are the same as the corresponding definitions above.

[Specific Examples of Group Represented by Formula (16)]

Examples of the group represented by Formula (16) may include groups represented by the following formulae. In the following formulae, M represents the same meaning as described above.

Examples of Structural Unit Represented by Formula (14)

Examples of the structural unit represented by Formula (14) may include structural units optionally having a substituent represented by the following formulae.

In view of the stability against an electronic current of the polymer compound according to the present invention, the structural unit represented by Formula (14) is preferably structural units optionally having a substituent represented by the following formulae. In the following formulae, M means the same as described above, and examples of the substituent may include the same as the substituent exemplified in the above description with respect to Ar¹. When the substituent is plurally present, they may be the same or different.

Other Structural Units

The polymer compound according to the present invention may further have one or more structural units selected from the group consisting of a structural unit represented by Formula (23) and a structural unit represented by Formula (24).

(In Formula (23), Ar⁵ represents a (2+m22)-valent aromatic group that optionally has a substituent or a (2+m22)-valent aromatic amine residue that optionally has a substituent; R¹⁷ represents the group represented by Formula (4); and m22 represents an integer of 1 or more. When R¹⁷ is plurally present, they may be the same or different. A hydrogen atom in Formula (23) may be replaced with a substituent other than R¹⁷.)

(In Formula (24), Ar⁶ represents a divalent aromatic group that optionally has a substituent or a divalent aromatic amine residue that optionally has a substituent; X′ represents an imino group that optionally has a substituent, a silylene group that optionally has a substituent, an ethenylene group that optionally has a substituent, or an ethynylene group; m23 and m24 each independently represent 0 or 1; and at least one of m23 and m24 is 1.)

—Structural Unit Represented by Formula (23)—

Examples of the (2+m22)-valent aromatic group represented by Ar⁵ in Formula (23) may include a (2+m22)-valent aromatic hydrocarbon group and a (2+m22)-valent aromatic heterocyclic group. Examples of the (2+m12)-valent aromatic group include: a (2+m22)-valent group remaining after removing (2+m22) hydrogen atoms that are bonded to any of the carbon atoms constituting a ring from a monocyclic aromatic ring such as a benzene ring, a pyridine ring, a 1,2-diazine ring, a 1,3-diazine ring, a 1,4-diazine ring, a 1,3,5-triazine ring, a furan ring, a pyrrole ring, a thiophene ring, a pyrazole ring, an imidazole ring, an oxazole ring, an oxadiazole ring, and an azadiazole ring; a (2+m22)-valent group remaining after removing (2+m22) hydrogen atoms that are bonded to any of the carbon atoms constituting a ring from a fused polycyclic aromatic ring in which two or more rings selected from the group consisting of the above monocyclic aromatic rings are fused; a divalent group remaining after removing two hydrogen atoms that are bonded to any of the carbon atoms constituting a ring from an aromatic ring assembly in which two or more aromatic rings selected from the group consisting of the above monocyclic aromatic rings and the above fused polycyclic aromatic rings are linked through a single bond, an ethenylene group, or an ethynylene group; and a (2+m22)-valent group remaining after removing (2+m22) hydrogen atoms that are bonded to any of the carbon atoms constituting a ring from a bridged polycyclic aromatic ring having a bridge in which two aromatic rings adjacent to each other of the above fused polycyclic aromatic ring or the above aromatic ring assembly are bridged through a divalent group such as a methylene group, an ethylene group, a carbonyl group, and an imino group.

In the fused polycyclic aromatic ring, the number of monocyclic aromatic rings to be fused is preferably 2 to 4, more preferably 2 to 3, and further preferably 2, in view of the solubility of the polymer compound. In the aromatic ring assembly, the number of aromatic rings to be linked is preferably 2 to 4, more preferably 2 to 3, and further preferably 2, in view of the solubility. In the bridged polycyclic aromatic ring, the number of aromatic rings to be bridged is preferably 2 to 4, more preferably 2 to 3, and further preferably 2, in view of the solubility of the polymer compound.

Examples of the monocyclic aromatic ring may include the following rings.

Examples of the fused polycyclic aromatic ring may include the following rings.

Examples of the aromatic ring assembly may include the following rings.

Examples of the bridged polycyclic aromatic ring may include the following rings.

In view of any one of or both of the electron acceptability and the hole acceptability of the polymer compound, the (2+m22)-valent aromatic group represented by Ar⁵ is preferably a (2+m22)-valent group remaining after removing (2+m22) hydrogen atoms from the ring represented by any one of Formulae 52 to 67, 68 to 83, 89 to 93, 104 to 106, 108, and 109, and more preferably a (2+m22)-valent group remaining after removing (2+m22) hydrogen atoms from the ring represented by any one of Formulae 52 to 57, 66, 67, 89, 91, 93, 104, 105, 108, and 109.

The (2+m22)-valent aromatic group may have a substituent. Examples of the substituent may include the same as the substituent exemplified in the above description with respect to Ar¹.

Examples of the (2+m22)-valent aromatic amine residue represented by Ar⁵ in Formula (23) may include a (2+m22)-valent group remaining after removing m22 hydrogen atoms from a group represented by Formula (25).

(In Formula (25), Ar⁷, Ar⁸, Ar⁹, and Ar¹⁰ each independently represent an arylene group that optionally has a substituent or a divalent heterocyclic group that optionally has a substituent; Ar¹¹, Ar¹², and Ar¹³ each independently represent an aryl group that optionally has a substituent or a monovalent heterocyclic group that optionally has a substituent; and m25 and m26 each independently represent 0 or 1.)

Examples of the substituent that the arylene group, the aryl group, the divalent heterocyclic group, and the monovalent heterocyclic group may have may include a halogen atom, an alkyl group, an alkyloxy group, an alkylthio group, an aryl group, an aryloxy group, an arylthio group, an arylalkyl group, an arylalkyloxy group, an arylalkylthio group, an alkenyl group, an alkynyl group, an arylalkenyl group, an arylalkynyl group, an acyl group, an acyloxy group, an amido group, an acid imido group, an imine residue, a substituted amino group, a substituted silyl group, a substituted silyloxy group, a substituted silylthio group, a substituted silylamino group, a cyano group, a nitro group, a monovalent heterocyclic group, a heteroaryloxy group, a heteroarylthio group, an alkyloxycarbonyl group, an aryloxycarbonyl group, an arylalkyloxycarbonyl group, a heteroaryloxycarbonyl group, and a carboxy group. The substituent may also be a cross-linkable group such as a vinyl group, an acetylene group, a butenyl group, an acryl group, an acrylate group, an acrylamido group, a methacryl group, a methacrylate group, a methacrylamido group, a vinyl ether group, a vinyl amino group, a silanol group, a group having a small ring (such as a cyclopropyl group, a cyclobutyl group, an epoxy group, an oxetane group, a diketene group, and an episulfide group), a lactone group, a lactam group, and a group containing a structure of a siloxane derivative.

When m25 is 0, a carbon atom in Ar⁷ and a carbon atom in Ar⁹ may be bonded to each other directly or may be bonded to each other through a divalent group such as —O— and —S—.

The aryl group and the monovalent heterocyclic group represented by Ar¹¹, Ar¹², and Ar¹³ are the same as the aryl group and the monovalent heterocyclic group described and exemplified above as a substituent.

Examples of the arylene group represented by Ar⁷, Ar⁸, Ar⁹, and Ar¹⁰ may include an atomic group remaining after removing two hydrogen atoms that are bonded to any of the carbon atoms constituting a ring (preferably, an aromatic ring) from an aromatic hydrocarbon, and examples of the arylene group may include a group having a benzene ring, a group having a fused ring, and a group in which two or more of independent benzene rings or fused rings are bonded with each other through a single bond or a divalent organic group, for example, an alkenylene group such as a vinylene group. The arylene group has usually 6 to 60 carbon atoms, preferably 7 to 48 carbon atoms. Specific examples of the arylene group may include a phenylene group, a biphenylene group, a C₁ to C₁₇ alkoxyphenylene group, a C₁ to C₁₇ alkylphenylene group, a 1-naphthylene group, a 2-naphthylene group, a 1-anthracenylene group, a 2-anthracenylene group, and a 9-anthracenylene group. A hydrogen atom in the arylene group may be substituted with a fluorine atom. Examples of such a fluorine atom-substituted arylene group may include a tetrafluorophenylene group. Among the arylene groups, a phenylene group, a biphenylene group, a C₁ to C₁₂ alkoxyphenylene group, and a C₁ to C₁₂ alkylphenylene group are preferred.

Examples of the divalent heterocyclic group represented by Ar⁷, Ar⁸, Ar⁹, and Ar¹⁰ may include an atomic group remaining after removing two hydrogen atoms that are bonded to any of the carbon atoms constituting a ring from a heterocyclic compound. The heterocyclic compound refers to an organic compound containing not only a carbon atom, but also a hetero atom such as an oxygen atom, a sulfur atom, a nitrogen atom, a phosphorus atom, a boron atom, a silicon atom, a selenium atom, a tellurium atom, and an arsenic atom as an element constituting the ring, among organic compounds having a cyclic structure. The divalent heterocyclic group may have a substituent. The divalent heterocyclic group has usually 4 to 60 carbon atoms, and preferably 4 to 20 carbon atoms. The number of carbon atoms of the divalent heterocyclic group does not include the number of carbon atoms of the substituent. Examples of such a divalent heterocyclic group may include a thiophenediyl group, a C₁ to C₁₂ alkylthiophenediyl group, a pyrroldiyl group, a furandiyl group, a pyridinediyl group, a C₁ to C₁₂ alkylpyridinediyl group, a pyridazinediyl group, a pyrimidinediyl group, a pyrazinediyl group, a triazinediyl group, a pyrrolidinediyl group, a piperidinediyl group, a quinolinediyl group, and an isoquinolinediyl group, and among them, a thiophenediyl group, a C₁ to C₁₂ alkylthiophenediyl group, a pyridinediyl group, and a C₁ to C₁₂ alkylpyridinediyl group are more preferred.

The polymer compound containing a (2+m22)-valent aromatic amine residue as a structural unit may further have other structural units. Examples of the other structural unit may include an arylene group such as a phenylene group and a fluorenediyl group.

Examples of the (2+m22)-valent aromatic amine residue represented by Formula (25) may include a group remaining after removing two hydrogen atoms from an aromatic amine represented by any one of the following Formulae 115 to 124. In view of the stability of the polymer compound against a hole current, a group remaining after removing (2+m22) hydrogen atoms from an aromatic amine represented by any one of Formulae 115, 116, 117, and 120 is preferred.

The aromatic amine represented by any one of Formulae 115 to 124 may have a substituent so long as the aromatic amine can generate a (2+m22)-valent aromatic amine residue. Examples of the substituent may include the same as the substituent exemplified in the above description with respect to Ar¹. When the substituent is plurally present, they may be the same or different.

m22 represents an integer of 1 or more. m12 is preferably 1 to 3, and more preferably 1 or 2.

—Structural Unit Represented by Formula (24)—

Examples of the divalent aromatic group represented by Ar⁶ in Formula (24) may include a divalent aromatic hydrocarbon group and a divalent aromatic heterocyclic group. The divalent aromatic group may include: a divalent group remaining after removing two hydrogen atoms that are bonded to any of the carbon atoms constituting a ring from a monocyclic aromatic ring such as a benzene ring, a pyridine ring, a 1,2-diazine ring, a 1,3-diazine ring, a 1,4-diazine ring, a 1,3,5-triazine ring, a furan ring, a pyrrole ring, a thiophene ring, a pyrazole ring, an imidazole ring, an oxazole ring, an oxadiazole ring, and an azadiazole ring; a divalent group remaining after removing two hydrogen atoms that are bonded to any of the carbon atoms constituting a ring from a fused polycyclic aromatic ring in which two or more rings selected from the group consisting of the above monocyclic aromatic rings are fused; a divalent group remaining after removing two hydrogen atoms that are bonded to any of the carbon atoms constituting a ring from an aromatic ring assembly in which two or more aromatic rings selected from the group consisting of the above monocyclic aromatic rings and the above fused polycyclic aromatic rings are linked through a single bond, an ethenylene group, or an ethynylene group; and a divalent group remaining after removing two hydrogen atoms that are bonded to any of the carbon atoms constituting a ring from a bridged polycyclic aromatic ring having a bridge in which two aromatic rings adjacent to each other of the above fused polycyclic aromatic ring or the above aromatic ring assembly are bridged through a divalent group such as a methylene group, an ethylene group, a carbonyl group, and an imino group.

In the fused polycyclic aromatic ring, the number of monocyclic aromatic rings to be fused is preferably 2 to 4, more preferably 2 to 3, and further preferably 2, in view of the solubility of the polymer compound. In the aromatic ring assembly, the number of aromatic rings to be linked is preferably 2 to 4, more preferably 2 to 3, and further preferably 2, in view of solubility. In the bridged polycyclic aromatic ring, the number of aromatic rings to be bridged is preferably 2 to 4, more preferably 2 to 3, and further preferably 2, in view of the solubility of the polymer compound.

Examples of the monocyclic aromatic ring may include the same as the ring exemplified in the above description for Ar⁵.

Examples of the fused polycyclic aromatic ring may include the same as the ring exemplified in the above description for Ar⁵.

Examples of the aromatic ring assembly may include the same as the ring exemplified in the above description for Ar⁵.

Examples of the bridged polycyclic aromatic ring may include the same as the ring exemplified in the above description for Ar⁵.

In view of any one of or both of the electron acceptability and the hole acceptability of the polymer compound, the divalent aromatic group represented by Ar⁶ is preferably a divalent group remaining after removing two hydrogen atoms from the ring represented by any one of Formulae 52 to 67, 68 to 83, 89 to 93, 104 to 106, 108, and 109, and more preferably a divalent group remaining after removing two hydrogen atoms from the ring represented by any one of Formulae 52 to 57, 66, 67, 89, 91, 93, 104, 105, 108, and 109.

The divalent aromatic group may have a substituent. Examples of the substituent may include the same as the substituent exemplified in the above description with respect to Formula (1).

Examples of the divalent aromatic amine residue represented by Ar⁶ in Formula (24) may include, except for their valence, the same as the (2+m22)-valent aromatic amine residue exemplified in the above description for Ar⁵.

The polymer compound containing a divalent aromatic amine residue as a structural unit may further have other structural units. The examples of the other structural unit may include an arylene group such as a phenylene group and fluorenediyl group.

Examples of the divalent aromatic amine residue represented by Ar⁶ in Formula (24) may include a group remaining after two hydrogen atoms from the aromatic amine represented by any one of Formulae 115 to 124. In view of the stability against a hole current of the polymer compound, a group remaining after removing two hydrogen atoms from the aromatic amine represented by any one of Formulae 115, 116, 117, and 120 is preferred.

The divalent aromatic amine residue represented by Ar⁶ in Formula (24) may have a substituent. Examples of the substituent may include the same as the substituent exemplified in the above description with respect to Ar¹. When the substituent is plurally present, they may be the same or different.

In Formula (24), X′ represents an imino group that optionally has a substituent, a silylene group that optionally has a substituent, an ethenylene group that optionally has a substituent, or an ethynylene group. Examples of the substituent that the imino group, the silyl group, or the ethenylene group may have may include an alkyl group having 1 to 20 carbon atoms such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, 2-ethylhexyl group, a nonyl group, a decyl group, 3,7-dimethyloctyl group, and a lauryl group; and an aryl group having 6 to 30 carbon atoms such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, and a 9-anthracenyl group. When the substituent is plurally present, they may be the same or different.

In view of the stability of the polymer compound against air, moisture, and heat, X′ is preferably an imino group, an ethenylene group, or an ethynylene group.

In view of the electron transport property of the polymer compound, m15 is preferably 1, and m16 is preferably 0.

In view of solubility, the polymer compound according to the present invention preferably has the structural unit represented by Formula (23).

In view of stability, the polymer compound according to the present invention preferably has the structural unit represented by Formula (24).

Ratio of Structural Units

In view of the light-emitting efficiency of the electroluminescent device, the ratio of the sum of the structural unit represented by Formula (1), and the structural unit represented by Formula (14) contained in the polymer compound according to the present invention is more preferably 30 to 100% by mole, based on all structural units contained in the polymer compound with the terminal structural unit excluded.

Terminal Structural Unit

Examples of the terminal structural unit (terminal group) of the polymer compound according to the present invention may include a hydrogen atom, a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, an isoamyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, a methoxy group, an ethoxy group, a propyloxy group, an isopropyloxy group, a butoxy group, an isobutoxy group, a sec-butoxy group, a tert-butoxy group, a pentyloxy group, a hexyloxy group, a cyclohexyloxy group, a heptyloxy group, an octyloxy group, a 2-ethylhexyloxy group, a nonyloxy group, a decyloxy group, a 3,7-dimethyloctyloxy group, a lauryloxy group, a methylthio group, an ethylthio group, a propylthio group, an isopropylthio group, a butylthio group, an isobutylthio group, a sec-butylthio group, a tert-butylthio group, a pentylthio group, a hexylthio group, a cyclohexylthio group, a heptylthio group, an octylthio group, a nonylthio group, a decylthio group, a laurylthio group, a methoxyphenyl group, an ethoxyphenyl group, a propyloxyphenyl group, an isopropyloxyphenyl group, a butoxyphenyl group, an isobutoxyphenyl group, a sec-butoxyphenyl group, a tert-butoxyphenyl group, a pentyloxyphenyl group, a hexyloxyphenyl group, a cyclohexyloxyphenyl group, a heptyloxyphenyl group, an octyloxyphenyl group, a 2-ethylhexyloxyphenyl group, a nonyloxyphenyl group, a decyloxyphenyl group, a 3,7-dimethyloctyloxyphenyl group, a lauryloxyphenyl group, a methylphenyl group, an ethylphenyl group, a dimethylphenyl group, a propylphenyl group, a mesityl group, a methylethylphenyl group, an isopropylphenyl group, a butylphenyl group, an isobutylphenyl group, a tert-butylphenyl group, a pentylphenyl group, an isoamylphenyl group, a hexylphenyl group, a heptylphenyl group, an octylphenyl group, a nonylphenyl group, a decylphenyl group, a dodecylphenyl group, a methylamino group, a dimethylamino group, an ethylamino group, a diethylamino group, a propylamino group, a dipropylamino group, an isopropylamino group, a diisopropylamino group, a butylamino group, an isobutylamino group, a sec-butylamino group, a tert-butylamino group, a pentylamino group, a hexylamino group, a cyclohexylamino group, a heptylamino group, an octylamino group, a 2-ethylhexylamino group, a nonylamino group, a decylamino group, a 3,7-dimethyloctylamino group, a laurylamino group, a cyclopentylamino group, a dicyclopentylamino group, a cyclohexylamino group, a dicyclohexylamino group, a ditrifluoromethylamino group, a phenylamino group, a diphenylamino group, a (C₁ to C₁₂ alkoxyphenyl)amino group, a di(C₁ to C₁₂ alkoxyphenyl)amino group, a di (C₁ to C₁₂ alkylphenyl)amino group, a 1-naphthylamino group, a 2-naphthylamino group, a pentafluorophenylamino group, a pyridylamino group, a pyridazinylamino group, a pyrimidylamino group, a pyrazinylamino group, a triazinylamino group, a (phenyl-C₁ to C₁₂ alkyl)amino group, a (C₁ to C₁₂ alkoxyphenyl-C₁ to C₁₂ alkyl)amino group, a (C₁ to C₁₂ alkylphenyl-C₁ to C₁₂ alkyl)amino group, a di(C₁ to C₁₂ alkoxyphenyl-C₁ to C₁₂ alkyl)amino group, a di(C₁ to C₁₂ alkylphenyl-C₁ to C₁₂ alkyl)amino group, a 1-naphthyl-C₁ to C₁₂ alkylamino group, a 2-naphthyl-C₁ to C₁₂ alkylamino group, a trimethylsilyl group, a triethylsilyl group, a tripropylsilyl group, a triisopropylsilyl group, an isopropyldimethylsilyl group, an isopropyldiethylsilyl group, a tert-butyldimethylsilyl group, a pentyldimethylsilyl group, a hexyldimethylsilyl group, a heptyldimethylsilyl group, an octyldimethylsilyl group, a 2-ethylhexyldimethylsilyl group, a nonyldimethylsilyl group, a decyldimethylsilyl group, a 3,7-dimethyloctyldimethylsilyl group, a lauryldimethylsilyl group, a (phenyl-C₁ to C₁₂ alkyl)silyl group, a (C₁ to C₁₂ alkoxyphenyl-C₁ to C₁₂ alkyl)silyl group, a (C₁ to C₁₂ alkylphenyl-C₁ to C₁₂ alkyl)silyl group, a (1-naphthyl-C₁ to C₁₂ alkyl)silyl group, a (2-naphthyl-C₁ to C₁₂ alkyl)silyl group, a (phenyl-C₁ to C₁₂ alkyl)dimethylsilyl group, a triphenylsilyl group, a tri(p-xylyl)silyl group, a tribenzylsilyl group, a diphenylmethylsilyl group, a tert-butyldiphenylsilyl group, a dimethylphenylsilyl group, a thienyl group, a C₁ to C₁₂ alkylthienyl group, a pyrrolyl group, a furyl group, a pyridyl group, a C₁ to C₁₂ alkylpyridyl group, a pyridazinyl group, a pyrimidyl group, a pyrazinyl group, a triazinyl group, a pyrrolidyl group, a piperidyl group, a quinolyl group, an isoquinolyl group, a hydroxy group, a mercapto group, a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom. When the terminal structural unit is plurally present, they may be the same or different.

—Characteristics of Polymer Compound—

The polymer compound refers to a compound whose polystyrene-equivalent weight-average molecular weight is 1×10³ or more.

In view of the film forming property by the application of the polymer compound according to the present invention, polystyrene-equivalent weight-average molecular weight of the polymer compound is preferably 1×10³ or more, more preferably 2×10³ or more, further preferably 3×10³ or more, and particularly preferably 5×10³ or more; the upper limit of the weight-average molecular weight is preferably 1×10⁸ or less and more preferably 1×10⁷ or less; and the range of the weight-average molecular weight is preferably 1×10³ to 1×10⁸, more preferably 2×10³ to 1×10⁷, further preferably 3×10³ to 1×10⁷, and particularly preferably 5×10³ to 1×10⁷. In view of the purity of the polymer compound, polystyrene-equivalent number-average molecular weight is preferably 1×10³ or more; the upper limit of the number-average molecular weight is preferably 5×10⁷ or less, more preferably 1×10⁷ or less, and further preferably 5×10⁶ or less; and the range of the number-average molecular weight is preferably 1×10³ to 5×10⁷, more preferably 1×10³ to 1×10⁷, and further preferably 1×10³ to 5×10⁶. In view of the solubility of the polymer compound, polystyrene-equivalent weight-average molecular weight is preferably 1×10³ or more; the upper limit of the weight-average molecular weight is preferably 5×10⁵ or less, more preferably 5×10⁴ or less, and further preferably 3×10³ or less; and the range of the weight-average molecular weight is preferably 1×10³ to 5×10⁵, more preferably 1×10³ to 5×10⁴, and further preferably 1×10³ to 3×10³. Polystyrene-equivalent number-average molecular weight and polystyrene-equivalent weight-average molecular weight of the polymer compound according to the present invention can be determined using, for example, gel permeation chromatography (GPC).

The polymer compound according to the present invention is preferably a conjugated polymer compound. That the polymer compound according to the present invention is a conjugated polymer compound means that the polymer compound contains, in the main chain thereof, a region in which multiple bonds or unshared electron pairs possessed by a nitrogen atom, an oxygen atom, or the like are linked through a single bond. When the polymer compound is a conjugated polymer compound, in view of the electron transport property of the conjugated polymer compound, the polymer compound has a ratio calculated by a formula of {(the number of atoms on the main chain contained in the region in which multiple bonds or unshared electron pairs possessed by a nitrogen atom, an oxygen atom, or the like are linked through a single bond)/(the number of all atoms on the main chain)}×100% of preferably 50% or more, more preferably 60% or more, further preferably 70% or more, particularly preferably 80% or more, and most of all preferably 90% or more.

In view of the electron acceptability and the hole acceptability of the polymer compound according to the present invention, the orbital energy of the lowest unoccupied molecular orbital (LUMO) of the polymer compound is preferably −5.0 eV or more and more preferably −4.5 eV or less; the upper limit of the orbital energy of LUMO is preferably −2.0 eV or less; and the range of the orbital energy of LUMO is preferably −5.0 eV or more and −2.0 eV or less, and more preferably −4.5 eV or more and −2.0 eV or less. In view of the same, the orbital energy of the highest occupied molecular orbital (HOMO) of the polymer compound is preferably −6.0 eV or more and more preferably −5.5 eV or more; the upper limit of the orbital energy of HOMO is preferably −3.0 eV or less; and the range of the orbital energy of HOMO is preferably −6.0 eV or more and −3.0 eV or less, and more preferably −5.5 eV or more and −3.0 eV or less, provided that the orbital energy of HOMO is lower than the orbital energy of LUMO. The orbital energy of HOMO of the polymer compound is determined by measuring the ionization potential of the polymer compound, and regarding the obtained ionization potential as the orbital energy. On the other hand, the orbital energy of LUMO of the polymer compound is determined by measuring the energy difference between HOMO and LUMO, and regarding the sum of the value and the above measured ionization potential as the orbital energy. For measuring the ionization potential, a photoelectron spectrophotometer is used. The energy difference between HOMO and LUMO is determined by measuring an absorption spectrum of the polymer compound using an ultraviolet-visible-near infrared spectrophotometer through its absorption edge.

Examples of the polymer compound may include the polymer compounds having structural units represented by the following formulae. Among these polymer compounds, in polymer compounds having structural units represented by a formula in which a plurality of structures are delimited by a slash “/”, the ratio of the left-hand structural unit is p % by mole and the ratio of the right-hand structural unit is (100-p) % by mole, and these structural units are arranged at random. Structural units other than the structural units represented by the following formulae may be further contained, and also in this case, they can be represented in the same manner as below. In the following formulae, M represents the same meaning as described above; n represents the degree of polymerization; and any hydrogen atom in the formulae may be replaced with a substituent to the extent of capable of being synthesized. Examples of the substituent may include the same as the group that may be substituted in the above Ar¹.

—Method for Manufacturing Polymer Compound—

Next, a method for manufacturing the polymer compound according to the present invention will be described. Preferred examples of the method for manufacturing the polymer compound according to the present invention may include: a method in which a compound represented by the following Formula (17) and/or a compound represented by Formula (20) are selected and used as raw materials, and polymerized (a polymer compound manufacturing method 1); and a method in which a polymer compound containing no ionic group is synthesized in the first process, and in the second process, from the polymer compound, a polymer compound containing an ionic group is synthesized (a polymer compound manufacturing method 2).

(In Formula (17), Ar³ represents a (2+m12+m13)-valent fused polycyclic aromatic group that optionally has a substituent; R¹⁰ represents the group represented by Formula (2) or Formula (3), or a group represented by Formula (18) or Formula (19); R¹¹ represents the group represented by Formula (4); m12 and m13 each independently represent an integer of 1 or more; and X¹ and X² each independently represent a group involved in condensation polymerization. When R¹⁰ and R¹¹ are each plurally present, they each may be the same or different. A hydrogen atom in Formula (17) may be replaced with a substituent other than R¹⁰ or R¹¹.)

[Chemical Formula 68]

—R¹²-{(Q⁴)_(n4)-Y⁴}_(m14)  (18)

(In Formula (18), R¹² represents a single bond or a (1+m14)-valent organic group that optionally has a substituent; Q⁴ represents a divalent organic group; Y⁴ represents —CO₂R^(χ), —SO₃R^(χ), —SO₂R^(χ), —PO₃(R^(χ))₂, or —B (R^(χ))₂; n4 represents an integer of 0 or more; R^(χ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms optionally having a substituent, or an aryl group having 6 to 50 carbon atoms optionally having a substituent; and m14 represents an integer of 1 or more, and when R¹² is a single bond, m14 represents 1. When Q⁴, Y⁴, n4, R^(χ) are each plurally present, they each may be the same or different.)

[Chemical Formula 69]

—R¹³-{(Q⁵)_(n5)-Y⁵}_(m15)  (19)

(In Formula (19), R¹³ represents a single bond or a (1+m15)-valent organic group that optionally has a substituent; Q⁵ represents a divalent organic group; Y⁵ represents a halogenated alkyl group, a halogen atom, —N(R^(δ))₂, —P(R^(δ))₂, or —SR^(δ); n5 represents an integer of 0 or more; R^(δ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms optionally having a substituent, or an aryl group having 6 to 50 carbon atoms optionally having a substituent; and m15 represents an integer of 1 or more, and when R¹³ is a single bond, m15 represents 1. When Q⁵, Y⁵, n5, and R^(δ) are each plurally present, they may be the same or different.)

(In Formula (20), Ar⁴ represents a (2+m16+m17)-valent fused polycyclic aromatic group that optionally has a substituent; R¹⁴ represents the group represented by Formula (15) or Formula (16), or a group represented by Formula (21) or Formula (22); R¹⁵ represents the group represented by Formula (4); m16 represents an integer of 1 or more; m17 represents an integer of 0 or more; and X³ and X⁴ each independently represent a group involved in condensation polymerization. When R¹⁴ and R¹⁵ are each plurally present, they each may be the same or different. A hydrogen atom in Formula (20) may be replaced with a substituent other than R¹⁴ or R¹⁵.)

(In Formula (21), R^(15′) represents a (1+m18+m19)-valent organic group that optionally has a substituent; Q³, Q⁴, Y³, Y⁴, n3, and n4 are the same as the corresponding definitions above; m18 and m19 each independently represent an integer of 1 or more; and when Q³, Q⁴, Y³, Y⁴, n3, and n4 are each plurally present, they each may be the same or different.)

(In Formula (22), R¹⁶ represents a (1+m20+m21)-valent organic group that optionally has a substituent; Q³, Q⁵, Y³, Y⁵, n3, and n5 are the same as the corresponding definitions above; m20 and m21 each independently represent an integer of 1 or more; and when Q³, Q⁵, Y³, Y⁵, n3, and n5 are each plurally present, they each may be the same or different.)

—Compound Represented by Formula (17)—

In Formula (17), Ar³ represents a (2+m12+m13)-valent fused polycyclic aromatic group that optionally has a substituent; R¹⁰ represents the group represented by Formula (2) or Formula (3), or the group represented by Formula (18) or Formula (19); R⁷ represents the group represented by Formula (4); m12 and m13 each independently represent an integer of 1 or more; and X¹ and X² each independently represent a group involved in condensation polymerization.

Ar³ may have a substituent other than R¹⁰ or R¹¹. Examples of the substituent may include the same as the substituent exemplified in the above description with respect to Ar¹.

In Formula (17), m12 represents an integer of 1 or more, preferably an integer of from 1 to 4, and more preferably an integer of from 1 to 3.

In Formula (17), m13 represents an integer of 1 or more, preferably an integer of from 1 to 4, and more preferably an integer of from 1 to 3.

Examples of the (2+m12+m13)-valent fused polycyclic aromatic group represented by Ar³ in Formula (17) may include a (2+m12+m13)-valent group remaining after removing (2+m12+m13) hydrogen atoms from a fused polycyclic aromatic ring in which two or more benzene rings are fused.

Examples of the fused polycyclic aromatic ring may include the same as the ring exemplified in the above description with respect to Ar¹.

In view of the solubility of the polymer compound, the (2+m12+m13)-valent fused polycyclic aromatic group is preferably a group remaining after removing (2+m12+m13) hydrogen atoms from the ring represented by any one of Formulae 1 to 4, 7, and 8, more preferably a group remaining after removing (2+m12+m13) hydrogen atoms from the ring represented by any one of Formulae 1 to 3, 7, and 8, and further preferably a group remaining after removing (2+m12+m13) hydrogen atoms from the ring represented by any one of Formulae 1 to 3, and 7.

In Formula (17), Ar³ is preferably a group remaining after removing (m12+m13) hydrogen atoms from the divalent group represented by any one of Formulae 10 to 17.

—Group Represented by Formula (18)—

In Formula (18), R¹² represents a single bond or a (1+m14)-valent organic group that optionally has a substituent. The group represented by Formula (18) is a monovalent group.

In Formula (18), examples of the (1+m14)-valent organic group that optionally has a substituent represented by R¹² may include: a group remaining after removing m14 hydrogen atoms from an alkyl group having 1 to 20 carbon atoms optionally having a substituent, such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m14 hydrogen atoms from an aryl group having 6 to 30 carbon atoms optionally having a substituent, such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, a 9-anthracenyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m14 hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms optionally having a substituent, such as a methoxy group, an ethoxy group, a propyloxy group, a butoxy group, a pentyloxy group, a hexyloxy group, a nonyloxy group, a dodecyloxy group, a cyclopropyloxy group, a cyclobutyloxy group, a cyclopentyloxy group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m14 hydrogen atoms from an amino group having a substituent containing a carbon atom; and a group remaining after removing m14 hydrogen atoms from a silyl group having a substituent containing a carbon atom. The number of carbons of the substituent is not included in the above number of carbons. Because the synthesis of the raw material monomer is simplified, preferred examples are a group remaining after removing m14 hydrogen atoms from an alkyl group, a group remaining after removing m14 hydrogen atoms from an aryl group, and a group remaining after removing m14 hydrogen atoms from an alkoxy group.

Examples of the substituent may include the same as the substituent exemplified in the above description with respect to Formula (1). When the substituent is plurally present, they may be the same or different.

In Formula (18), m14 represents an integer of 1 or more, and when R¹² is a single bond, m14 represents 1. m14 is preferably 1 to 3, and more preferably 1 or 2.

In Formula (18), examples of the divalent organic group represented by Q⁴ may include: a divalent chain saturated hydrocarbon group having 1 to 50 carbon atoms optionally having a substituent, such as a methylene group, an ethylene group, a 1,2-propylene group, a 1,3-propylene group, a 1,2-butylene group, a 1,3-butylene group, a 1,4-butylene group, a 1,5-pentylene group, a 1,6-hexylene group, a 1,9-nonylene group, a 1,12-dodecylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a divalent unsaturated hydrocarbon group having 2 to 50 carbon atoms optionally having a substituent including an alkenylene group having 2 to 50 carbon atoms optionally having a substituent, such as an ethenylene group, a propenylene group, a 3-butenylene group, a 2-butenylene group, a 2-pentenylene group, a 2-hexenylene group, a 2-nonenylene group, a 2-dodecenylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent, and an ethynylene group; a divalent cyclic saturated hydrocarbon group having 3 to 50 carbon atoms optionally having a substituent, such as a cyclopropylene group, a cyclobutylene group, a cyclopentylene group, a cyclohexylene group, a cyclononylene group, a cyclododecylene group, a norbornylene group, an adamantylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; an arylene group having 6 to 50 carbon atoms optionally having a substituent, such as a 1,3-phenylene group, a 1,4-phenylene group, a 1,4-naphthylene group, a 1,5-naphthylene group, a 2,6-naphthylene group, a biphenyl-4,4′-diyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; an alkyleneoxy group having 1 to 50 carbon atoms optionally having a substituent, such as a methyleneoxy group, an ethyleneoxy group, a propyleneoxy group, a butyleneoxy group, a pentyleneoxy group, a hexyleneoxy group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent (that is, a divalent organic group represented by formula: —R^(d)—O— (wherein R^(d) is an alkylene group having 1 to 50 carbon atoms optionally having a substituent, such as a methylene group, an ethylene group, a propylene group, a butylene group, a pentylene group, a hexylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent)); an imino group having a substituent containing a carbon atom; and a silylene group having a substituent containing a carbon atom. The number of carbons of the substituent is not included in the above number of carbons. Because the synthesis is simplified, preferred examples are a divalent chain saturated hydrocarbon group, an arylene group, and an alkyleneoxy group.

The group exemplified as the divalent organic group represented by Q⁴ may have a substituent, and examples of the substituent may include the same as the substituent exemplified in the above description with respect to Formula (1). When the substituent is plurally present, they may be the same or different.

In Formula (18), Y⁴ represents —CO₂R^(χ), —SO₃R^(χ), —SO₂R^(χ), —PO₃(R^(χ))₂, or —B(R^(χ))₂. R^(χ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms optionally having a substituent, or an aryl group having 6 to 50 carbon atoms optionally having a substituent. The number of carbons of the substituent is not included in the above number of carbons. Examples of the substituent may include the same as the substituent exemplified in the above description with respect to Formula (1). When the substituent is plurally present, they may be the same or different. Examples of R^(χ) may include: an alkyl group having 1 to 20 carbon atoms such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, and a lauryl group; an aryl group having 6 to 30 carbon atoms such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, and a 9-anthracenyl group.

In Formula (18), n4 represents an integer of 0 or more, and in view of the synthesis of the raw material monomer, n4 is preferably an integer of from 0 to 8, and more preferably an integer of from 0 to 2.

—Group Represented by Formula (19)—

In Formula (19), R¹³ represents a single bond or a (1+m15)-valent organic group that optionally has a substituent. The group represented by Formula (19) is a monovalent group.

In Formula (19), examples of the (1+m15)-valent organic group that optionally has a substituent represented by R¹³ may include: a group remaining after removing m15 hydrogen atoms from an alkyl group having 1 to 20 carbon atoms optionally having a substituent, such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m15 hydrogen atoms from an aryl group having 6 to 30 carbon atoms optionally having a substituent, such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, a 9-anthracenyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m15 hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms optionally having a substituent, such as a methoxy group, an ethoxy group, a propyloxy group, a butoxy group, a pentyloxy group, a hexyloxy group, a nonyloxy group, a dodecyloxy group, a cyclopropyloxy group, a cyclobutyloxy group, a cyclopentyloxy group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing m15 hydrogen atoms from an amino group having a substituent containing a carbon atom; and a group remaining after removing m15 hydrogen atoms from a silyl group having a substituent containing a carbon atom. The number of carbons of the substituent is not included in the above number of carbons. Because the synthesis of the raw material monomer is simplified, preferred examples are a group remaining after removing m15 hydrogen atoms from an alkyl group, a group remaining after removing m15 hydrogen atoms from an aryl group, and a group remaining after removing m15 hydrogen atoms from an alkoxy group.

Examples of the substituent may include the same as the substituent exemplified in the above description with respect to Formula (1). When the substituent is plurally present, they may be the same or different.

In Formula (19), m15 represents an integer of 1 or more, and when R¹³ is a single bond, m15 represents 1. m15 is preferably 1 to 3, and more preferably 1 or 2.

In Formula (19), examples of the divalent organic group represented by Q⁵ may include: a divalent chain saturated hydrocarbon group having 1 to 50 carbon atoms optionally having a substituent, such as a methylene group, an ethylene group, a 1,2-propylene group, a 1,3-propylene group, a 1,2-butylene group, a 1,3-butylene group, a 1,4-butylene group, a 1,5-pentylene group, a 1,6-hexylene group, a 1,9-nonylene group, a 1,12-dodecylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a divalent unsaturated hydrocarbon group having 2 to 50 carbon atoms optionally having a substituent including an alkenylene group having 2 to 50 carbon atoms optionally having a substituent, such as an ethenylene group, a propenylene group, a 3-butenylene group, a 2-butenylene group, a 2-pentenylene group, a 2-hexenylene group, a 2-nonenylene group, a 2-dodecenylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent, and an ethynylene group; a divalent cyclic saturated hydrocarbon group having 3 to 50 carbon atoms optionally having a substituent, such as a cyclopropylene group, a cyclobutylene group, a cyclopentylene group, a cyclohexylene group, a cyclononylene group, a cyclododecylene group, a norbornylene group, an adamantylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; an arylene group having 6 to 50 carbon atoms optionally having a substituent, such as a 1,3-phenylene group, a 1,4-phenylene group, a 1,4-naphthylene group, a 1,5-naphthylene group, a 2,6-naphthylene group, a biphenyl-4,4′-diyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; an alkyleneoxy group having 1 to 50 carbon atoms optionally having a substituent, such as a methyleneoxy group, an ethyleneoxy group, a propyleneoxy group, a butyleneoxy group, a pentyleneoxy group, a hexyleneoxy group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent (that is, a divalent organic group represented by formula: —R^(d)—O— (wherein R^(d) is an alkylene group having 1 to 50 carbon atoms optionally having a substituent, such as a methylene group, an ethylene group, a propylene group, a butylene group, a pentylene group, a hexylene group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent)); an imino group having a substituent containing a carbon atom; and a silylene group having a substituent containing a carbon atom. The number of carbons of the substituent is not included in the above number of carbons. Because the synthesis is simplified, preferred examples are a divalent chain saturated hydrocarbon group, an arylene group, and an alkyleneoxy group.

The group exemplified as the divalent organic group represented by Q⁵ may have a substituent, and examples of the substituent may include the same as the substituent exemplified in the above description with respect to Formula (1). When the substituent is plurally present, they may be the same or different.

In Formula (19), Y⁵ represents a halogenated alkyl group, a halogen atom, —N(R^(δ))₂, —P(R^(δ))₂, or —SR^(δ). R^(δ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms optionally having a substituent, or an aryl group having 6 to 50 carbon atoms optionally having a substituent. The number of carbons of the substituent is not included in the above number of carbons. Examples of the substituent may include the same as the substituent exemplified in the above description with respect to Formula (1). When the substituent is plurally present, they may be the same or different. Examples of R^(δ) may include: an alkyl group having 1 to 20 carbon atoms such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, and a lauryl group; and an aryl group having 6 to 30 carbon atoms such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, and a 9-anthracenyl group. The alkyl group in the halogenated alkyl group may be the same as the alkyl group described above. The halogen atom with respect to the halogenation in the halogenated alkyl group may be the same as the halogen atom described above. Examples of the halogenated alkyl group may include a halogenated methyl group, a halogenated ethyl group, a halogenated propyl group, and a halogenated butyl group.

In Formula (19), n5 represents an integer of 0 or more, and in view of the synthesis of the raw material monomer, n5 is preferably an integer of from 0 to 8, and more preferably an integer of from 0 to 2.

—Compound Represented by Formula (20)—

In Formula (20), Ar⁴ represents a (2+m16+m17)-valent fused polycyclic aromatic group that optionally has a substituent; R¹⁴ represents the group represented by Formula (15) or Formula (16), or the group represented by Formula (18) or Formula (19); R⁷ represents the group represented by Formula (4); m16 represents an integer of 1 or more; and m17 represents an integer of 0 or more.

Ar⁴ may have a substituent other than R¹⁴ or R¹⁵. Examples of the substituent may include the same as the substituent exemplified in the above description with respect to Ar⁴.

In Formula (20), m16 represents an integer of 1 or more, preferably an integer of from 1 to 4, and more preferably an integer of from 1 to 3.

In Formula (20), m17 represents an integer of 0 or more, preferably an integer of from 0 to 4, and more preferably an integer of from 0 to 3.

Examples of the (2+m16+m17)-valent fused polycyclic aromatic group represented by Ar⁴ in Formula (20) may include a (2+m16+m17)-valent group remaining after removing (2+m16+m17) hydrogen atoms from a fused polycyclic aromatic ring in which two or more benzene rings are fused.

Examples of the fused polycyclic aromatic ring may include the same as the ring exemplified in the above description with respect to Ar¹.

In view of the solubility of the polymer compound, the (2+m16+m17)-valent fused polycyclic aromatic group is preferably a group remaining after removing (2+m16+m17) hydrogen atoms from the ring represented by any one of Formulae 1 to 4, 7, and 8, more preferably a group remaining after removing (2+m16+m17) hydrogen atoms from the ring represented by any one of Formulae 1 to 3, 7, and 8, and further preferably a group remaining after removing (2+m16+m17) hydrogen atoms from the ring represented by any one of Formulae 1 to 3, and 7.

In Formula (20), Ar⁴ is preferably a group remaining after removing (m16+m17) hydrogen atoms from the divalent group represented by any one of Formulae 10 to 17.

—Group Represented by Formula (21)—

In Formula (21), R^(15′) represents a (1+m18+m19) valent organic group that optionally has a substituent. The group represented by Formula (21) is a monovalent group.

In Formula (21), examples of the (1+m18+m19)-valent organic group that optionally has a substituent represented by R^(15′) may include: a group remaining after removing (m18+m19) hydrogen atoms from an alkyl group having 1 to 20 carbon atoms optionally having a substituent, such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing (m18+m19) hydrogen atoms from an aryl group having 6 to 30 carbon atoms optionally having a substituent, such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, a 9-anthracenyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing (m18+m19) hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms optionally having a substituent, such as a methoxy group, an ethoxy group, a propyloxy group, a butoxy group, a pentyloxy group, a hexyloxy group, a nonyloxy group, a dodecyloxy group, a cyclopropyloxy group, a cyclobutyloxy group, a cyclopentyloxy group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing (m18+m19) hydrogen atoms from an amino group having a substituent containing a carbon atom; and a group remaining after removing (m18+m19) hydrogen atoms from a silyl group having a substituent containing a carbon atom. The number of carbons of the substituent is not included in the above number of carbons. Because the synthesis of the raw material monomer is simplified, preferred examples are a group remaining after removing (m18+m19) hydrogen atoms from an alkyl group, a group remaining after removing (m18+m19) hydrogen atoms from an aryl group, and a group remaining after removing (m18+m19) hydrogen atoms from an alkoxy group.

Examples of the above substituent may include the same as the substituent exemplified in the description with respect to Formula (1). When the substituent is plurally present, they may be the same or different.

In Formula (21), m18 and m19 each independently represent an integer of 1 or more (e.g., 1, 2, or 3 for each).

In Formula (21), Q⁴, n4, Y⁴, Q³, n3, and Y³ are the same as the corresponding definitions above. When Q⁴, n4, Y⁴, Q³, n3, and Y³ are each plurally present, they may be the same or different.

—Group Represented by Formula (22)—

In Formula (22), R¹⁶ represents a (1+m20+m21) valent organic group that optionally has a substituent. The group represented by Formula (22) is a monovalent group.

In Formula (22), examples of the (1+m20+m21)-valent organic group that optionally has a substituent represented by R¹⁶ may include: a group remaining after removing (m20+m21) hydrogen atoms from an alkyl group having 1 to 20 carbon atoms optionally having a substituent, such as a methyl group, an ethyl group, a propyl group, an isopropyl group, a butyl group, an isobutyl group, a sec-butyl group, a tert-butyl group, a pentyl group, a hexyl group, a cyclohexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, a lauryl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing (m20+m21) hydrogen atoms from an aryl group having 6 to 30 carbon atoms optionally having a substituent, such as a phenyl group, a 1-naphthyl group, a 2-naphthyl group, a 1-anthracenyl group, a 2-anthracenyl group, a 9-anthracenyl group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing (m20+m21) hydrogen atoms from an alkoxy group having 1 to 50 carbon atoms optionally having a substituent, such as a methoxy group, an ethoxy group, a propyloxy group, a butoxy group, a pentyloxy group, a hexyloxy group, a nonyloxy group, a dodecyloxy group, a cyclopropyloxy group, a cyclobutyloxy group, a cyclopentyloxy group, a cyclohexyloxy group, a cyclononyloxy group, a cyclododecyloxy group, a norbornyloxy group, an adamantyloxy group, and a group in which at least one hydrogen atom in these groups is substituted with a substituent; a group remaining after removing (m20+m21) hydrogen atoms from an amino group having a substituent containing a carbon atom; and a group remaining after removing (m20+m21) hydrogen atoms from a silyl group having a substituent containing a carbon atom. The number of carbons of the substituent is not included in the above number of carbons. Because the synthesis of the raw material monomer is simplified, preferred examples are a group remaining after removing (m20+m21) hydrogen atoms from an alkyl group, a group remaining after removing (m20+m21) hydrogen atoms from an aryl group, and a group remaining after removing (m20+m21) hydrogen atoms from an alkoxy group.

Examples of the above substituent may include the same as the substituent exemplified in the description with respect to Formula (1). When the substituent is plurally present, they may be the same or different.

In Formula (22), m20 and m21 each independently represent an integer of 1 or more (e.g., 1, 2, or 3 for each).

In Formula (22), Q⁵, n5, Y⁵, Q³, n3, and Y³ are the same as the corresponding definitions above. When Q⁵, n5, Y⁵, Q³, n3, and Y³ are each plurally present, they may be the same or different.

When, together with the structural unit represented by Formula (1) and/or the structural unit represented by Formula (14), another structural unit is contained in the polymer compound according to the present invention, the polymer compound according to the present invention further having a structural unit represented by -A_(a)- can be manufactured by condensation polymerizing a compound represented by Formula (26) in addition to the compounds represented by Formulae (17) and (20).

X⁵-A_(a)-X⁶  (26)

(In Formula (26), A_(a) represents a group constituting the structural unit represented by Formula (23), and/or a divalent aromatic group represented by the above Ar⁶ or a divalent aromatic amine residue that optionally has a substituent, and X⁵ and X⁶ each independently represent a group involved in condensation polymerization.)

Examples of the group involved in condensation polymerization represented by X¹, X², X³, X⁴, X⁵, and X⁶ may include a hydrogen atom, a halogen atom, an alkyl sulfonate group, an aryl sulfonate group, an arylalkyl sulfonate group, a boric acid ester residue, a sulfonium methyl group, a phosphonium methyl group, a phosphonate methyl group, a monohalogenated methyl group, —B(OH)₂, a formyl group, a cyano group, and a vinyl group.

Examples of the halogen atom which can be selected as the group involved in condensation polymerization may include a fluorine atom, a chlorine atom, a bromine atom, and an iodine atom.

Examples of the alkyl sulfonate group which can be selected as the group involved in condensation polymerization may include a methane sulfonate group, an ethane sulfonate group, and a trifluoromethane sulfonate group.

Examples of the aryl sulfonate group which can be selected as the group involved in condensation polymerization may include a benzene sulfonate group and a p-toluene sulfonate group.

Examples of the arylalkyl sulfonate group which can be selected as the group involved in condensation polymerization may include a benzyl sulfonate group.

Examples of the boric acid ester residue which can be selected as the group involved in condensation polymerization may include groups represented by the following formulae.

Examples of the sulfoniummethyl group which can be selected as the group involved in condensation polymerization may include groups represented by the following formulae:

—CH₂S⁺Me₂E⁻ or —CH₂S⁺Ph₂E⁻

(where E represents a halogen atom, and Ph represents a phenyl group; the same is applicable hereinafter).

Examples of the phosphoniummethyl group which can be selected as the group involved in condensation polymerization may include a group represented by the following formula:

—CH₂P⁺Ph₃E⁻

(where E represents the same meaning as described above).

Examples of the phosphonate methyl group which can be selected as the group involved in condensation polymerization may include a group represented by the following formula:

—CH₂PO(OR^(j))₂

(where R^(j) represents an alkyl group, an aryl group, or an arylalkyl group).

Examples of the monohalogenated methyl group which can be selected as the group involved in condensation polymerization may include a fluorinated methyl group, a chlorinated methyl group, a brominated methyl group, and an iodinated methyl group.

The group preferred as the group involved in condensation polymerization varies depending on the types of polymerization reactions. For example, when a zero-valent nickel complex for the Yamamoto coupling reaction or the like is used, examples of the group may include a halogen atom, an alkyl sulfonate group, an aryl sulfonate group, and an arylalkyl sulfonate group. When a nickel catalyst or a palladium catalyst for the Suzuki coupling reaction or the like is used, examples of the group may include an alkyl sulfonate group, a halogen atom, a boric acid ester residue, and —B(OH)₂. When an oxidation polymerization is conducted using an oxidant or conducted electrochemically, examples of the group may include a hydrogen atom.

Examples of the polymer compound manufacturing method 1 described above may include polymer compound manufacturing methods 1-1 and 1-2.

The polymer compound manufacturing method 1-1 is a method for manufacturing a polymer compound having the structural unit represented by Formula (1) including polymerizing an organic compound represented by the following formula (17A):

(in Formula (17A), R^(10′) represents the group represented by Formula (2) or Formula (3); Ar³, R¹¹, m12, m13, and X¹ and X² are the same as the corresponding definitions above; a hydrogen atom in Formula (17A) may be replaced with a substituent other than R^(10′) or R¹¹) to obtain the polymer compound having the structural unit represented by Formula (1).

The details of the groups in the organic compound represented by Formula (17A) are the same as those of the organic compound represented by Formula (17). In the manufacturing method 1-1, not only the organic compound represented by Formula (17A), but also one or two or more types of other organic compounds selected from the group consisting of the organic compound represented by Formula (17), the organic compound represented by Formula (20), and the organic compound represented by Formula (26) may be further polymerized. In the manufacturing method 1-1, Ar³, R^(10′), R¹¹, m12, and m13 in the organic compound represented by Formula (17A) correspond to Ar¹, R¹, R², m1, and m2 in the polymer compound having the structural unit represented by Formula (1), respectively.

The polymer compound manufacturing method 1-2 is a method for manufacturing a polymer compound having the structural unit represented by Formula (14) including polymerizing an organic compound represented by the following formula (20A):

(in Formula (20A), R^(14′) represents the group represented by Formula (15) or Formula (16); Ar⁴, R¹⁵, m16, m17, and X³ and X⁴ are the same as the corresponding definitions above; a hydrogen atom in Formula (20A) may be replaced with a substituent other than R^(14′) or R¹⁵) to obtain the polymer compound having the structural unit represented by Formula (14).

The details of the groups in the organic compound represented by Formula (20A) are the same as those of the organic compound represented by Formula (20). In the manufacturing method 1-2, not only the organic compound represented by Formula (20A), but also one or two or more types of organic compounds selected from the group consisting of the organic compound represented by Formula (17), the organic compound represented by Formula (20), and the organic compound represented by Formula (26) may be further polymerized. In the manufacturing method 1-2, Ar⁴, R^(14′), R¹⁵, m16, and m17 in the organic compound represented by Formula (20A) correspond to Ar², R⁶, R⁷, m6, and m7 in the polymer compound having the structural unit represented by Formula (14), respectively.

Examples of the polymer compound manufacturing method 2 described above may include polymer compound manufacturing methods 2-1 and 2-2.

The polymer compound manufacturing method 2-1 is a method for manufacturing a polymer compound having the structural unit represented by Formula (1) including:

(i) polymerizing an organic compound represented by the following Formula (17B):

(in Formula (17B), R^(10″) represents the group represented by Formula (18) or Formula (19). Ar³, R¹¹, m12, m13, and X¹ and X² are the same as the corresponding definitions above. A hydrogen atom in Formula (17B) may be replaced with a substituent other than R^(10″) or R¹¹.) to obtain a polymer compound represented by the following Formula (17B′):

(in Formula (17B′), R^(10″) represents the group represented by Formula (18) or Formula (19). Ar³, R¹¹, m12, and m13 are the same as the corresponding definitions above. A hydrogen atom in Formula (17B′) may be replaced with a substituent other than R^(10″) or R¹¹.); and (ii) ionizing the polymer compound having the structural unit represented by Formula (17B′) to obtain the polymer compound having the structural unit represented by Formula (1). The present invention also provides a polymer compound having the structural unit represented by Formula (17B′). The structural unit represented by Formula (17B′) is a divalent structural unit.

The details of the groups in the organic compounds represented by Formula (17B) and (17B′) may be the same as those of the organic compound represented by Formula (17). In the process (i) of the manufacturing method 2-1, not only the organic compound represented by Formula (17B), but also one or two or more types of organic compounds selected from the group consisting of the organic compound represented by Formula (17), the organic compound represented by Formula (20), and the organic compound represented by Formula (26) may be further polymerized. In the manufacturing method 2-1, Ar³, R^(10″), R¹¹, m12, and m13 in the organic compounds represented by Formulae (17B) and (17B′) correspond to Ar¹, R¹, R², m1, and m2 in the polymer compound having the structural unit represented by Formula (1), respectively.

In the process (ii) of the manufacturing method 2-1, the polymer compound having the structural unit represented by Formula (17B′) is ionized, thereby, in R^(10″), converting the group represented by Formula (18) or the group represented by Formula (19) (a non-ionic group) into the group represented by Formula (2) or the group represented by Formula (3) (an ionic group).

The manufacturing method 2-2 is a method for manufacturing a polymer compound having the structural unit represented by Formula (14) including:

(i′) polymerizing an organic compound represented by the following Formula (20B):

(in Formula (20B), R^(14″) represents the group represented by Formula (21) or Formula (22). Ar⁴, R¹⁵, m16, m17, X³, and X⁴ are the same as the corresponding definitions above. A hydrogen atom in Formula (20B) may be replaced with a substituent other than R^(14″) or R¹⁵.) to obtain a polymer compound represented by the following Formula (20B′):

(in Formula (20B′), R^(14″) represents the group represented by Formula (21) or Formula (22). Ar⁴, R¹⁵, m16, and m17 are the same as the corresponding definitions above. A hydrogen atom in Formula (20B′) may be replaced with a substituent other than R^(14″) or R¹⁵.); and (ii′) ionizing the polymer compound having the structural unit represented by Formula (20B′) to obtain the polymer compound having the structural unit represented by Formula (14). The present invention also provides a polymer compound having the structural unit represented by Formula (20B′). The structural unit represented by Formula (20B′) is a divalent structural unit.

The details of the groups in the organic compounds represented by Formula (20B) and (20B′) are the same as those of the organic compound represented by Formula (20). In the process (i) of the manufacturing method 2-2, not only the organic compound represented by Formula (20B), but also one or two or more types of organic compounds selected from the group consisting of the organic compound represented by Formula (17), the organic compound represented by Formula (20), and the organic compound represented by Formula (26) may be further polymerized. In the manufacturing method 2-2, Ar⁴, R^(14″), R¹⁵, m16, and m17 in the organic compounds represented by Formulae (20B) and (20B′) correspond to Ar², R⁶, R⁷, m6, and m7 in the polymer compound having the structural unit represented by Formula (14), respectively.

In the process (ii′) of the manufacturing method 2-2, the polymer compound having the structural unit represented by Formula (20B′) is ionized, thereby, in R^(14″), converting the group represented by Formula (21) or the group represented by Formula (22) (a non-ionic group) into the group represented by Formula (15) or the group represented by Formula (16) (an ionic group).

Examples of the ionization in the process (ii) of the manufacturing method 2-1 and the process (ii′) of the manufacturing method 2-2 may include cationization and anionization. Examples of the ionization may include a method in which the polymer compound obtained in the process (i) is reacted with a reagent such as a metal hydroxide, a metal carbonate, and alkylammonium hydroxide or a reagent such as an alkyl halide and SbF₅, as needed dissolved in water or an organic solvent, at a temperature of the melting point of the organic solvent or higher and the boiling point of the organic solvent or lower.

When the polymer compound according to the present invention is manufactured, a polymerization method may be employed in which, for example, a compound (monomer) represented by Formula (17) or (20) having a plurality of groups involved in condensation polymerization is dissolved in an organic solvent as needed and is reacted using an alkali or an appropriate catalyst, at a temperature of the melting point of the organic solvent or higher and the boiling point of the organic solvent or lower. Examples of such a polymerization method may include publicly known methods described in, for example, “Organic Reactions, vol. 14, pp. 270-490 (1965), published by John Wiley & Sons, Inc.,” “Organic Syntheses, Collective Volume VI, pp. 407-411 (1988), published by John Wiley & Sons, Inc.,” “Chemical Review (Chem. Rev.), vol. 95, p. 2457 (1995),” “Journal of Organometallic Chemistry (J. Organomet. Chem.), vol. 576, p. 147 (1999),” and “Macromolecular Chemistry, Macromolecular Symposium (Macromol. Chem., Macromol. Symp.) vol. 12, p. 229 (1987).”

When the polymer compound according to the present invention is manufactured, a known condensation polymerization reaction may be employed according to the group involved in condensation polymerization. Examples of such a polymerization method may include: a method of polymerizing the relevant monomer by the Suzuki coupling reaction; a method of polymerizing the relevant monomer by the Grignard reaction; a method of polymerizing the relevant monomer by a Ni(0) complex; a method of polymerizing the relevant monomer by an oxidant such as FeCl₃; a method of oxidative polymerizing the relevant monomer electrochemically; and a method of decomposing an intermediate polymer having an appropriate leaving group. Among such polymerization reactions, the method of polymerizing by the Suzuki coupling reaction, the method of polymerizing by the Grignard reaction, and the method of polymerizing by a zero-valent nickel complex are preferred, because the structure of the obtained ionic polymer can be easily controlled.

A preferred embodiment of the method for manufacturing the polymer compound according to the present invention is a method for manufacturing the polymer compound including: using a raw material monomer including a group selected from the group consisting of a halogen atom, an alkyl sulfonate group, an aryl sulfonate group, and an arylalkyl sulfonate group as the group involved in condensation polymerization; and condensation polymerizing the raw material monomer in the presence of a zero-valent nickel complex. Examples of the raw material monomer used for such a method may include a dihalogenated compound, a bis(alkyl sulfonate) compound, a bis(aryl sulfonate) compound, a bis(arylalkyl sulfonate) compound, a halogen-alkyl sulfonate compound, a halogen-aryl sulfonate compound, a halogen-arylalkyl sulfonate compound, an alkyl sulfonate-aryl sulfonate compound, an alkyl sulfonate-arylalkyl sulfonate compound, and an aryl sulfonate-arylalkyl sulfonate compound.

Another preferred embodiment of the method for manufacturing the polymer compound is a method for manufacturing the polymer compound including: using a raw material monomer including a group selected from the group consisting of a halogen atom, an alkyl sulfonate group, an aryl sulfonate group, an arylalkyl sulfonate group, —B(OH)₂, and a boric acid ester residue as the group involved in condensation polymerization, the raw material monomer in which the ratio between the sum (J) of the number of moles of a halogen atom, an alkyl sulfonate group, an aryl sulfonate group, and an arylalkyl sulfonate group that all raw material monomers have and the sum (K) of the number of moles of —B(OH)₂ and a boric acid ester residue that all raw material monomers have is substantially 1 (usually, K/J is in a range of 0.7 to 1.2); and condensation polymerizing the raw material monomer in the presence of a nickel catalyst or a palladium catalyst.

The organic solvent varies depending on the used compounds and the reaction. For the organic solvent, in order to suppress a side reaction, an organic solvent subjected thoroughly to deoxygenation treatment is generally preferred to be used. When the polymer compound is manufactured, it is preferred that the reaction is progressed using such an organic solvent in an inert atmosphere. The organic solvent is preferably subjected to a dehydration treatment as well as the deoxygenation treatment, provided that this may not be the case for the reaction in a two-phase system with water such as the Suzuki coupling reaction.

Examples of the organic solvent may include: a saturated hydrocarbon such as pentane, hexane, heptane, octane, and cyclohexane; an unsaturated hydrocarbon such as benzene, toluene, ethylbenzene, and xylene; alcohols such as methanol, ethanol, propanol, isopropanol, butanol, and tert-butyl alcohol; carboxylic acids such as formic acid, acetic acid, and propionic acid; ethers such as dimethyl ether, diethyl ether, methyl tert-butyl ether, tetrahydrofuran, tetrahydropyran, and dioxane; amines such as trimethylamine, triethylamine, N,N,N′,N′-tetramethylethylenediamine, and pyridine; and amides such as N,N-dimethylformamide, N,N-dimethylacetamide, N,N-diethylacetamide, and N-methylmorpholine oxide. These organic solvents may be used alone or in combination of two or more types thereof. Among such organic solvents, in view of the reactivity, ethers are more preferred, and tetrahydrofuran and diethyl ether are further preferred. In view of the reaction rate, toluene and xylene are preferred.

When the polymer compound is manufactured, it is preferred that an alkali or an appropriate catalyst is added in order to cause the raw material monomer to react. The alkali or catalyst may be selected according to an employed polymerization method or the like. The alkali and catalyst are preferably those capable of being thoroughly dissolved in the solvent used for the reaction. Examples of the method for mixing the alkali or catalyst may include a method in which while stirring a reaction mixture in an inert atmosphere such as argon and nitrogen, a solution of the alkali or the catalyst is slowly added thereto and a method in which the reaction mixture is slowly added to a solution of the alkali or the catalyst.

Regarding the polymer compound according to the present invention, if a polymerization-active group remains at the position of a terminal group as it is, there is such a probability that the light-emitting characteristics and the life characteristics of the obtained light-emitting device might lower. Therefore, the terminal group may be protected with a stable group. When the terminal group is protected with a stable group and the polymer compound according to the present invention is a conjugated compound, the polymer compound has preferably a conjugated bond in conjunction with a conjugated structure of the main chain of the polymer compound. Examples of such a structure may include a structure being bonded with an aryl group or a heterocyclic group through a carbon-carbon bond. Examples of such a stable group for protecting the terminal group may include a monovalent aromatic group.

Examples of a preferred method for manufacturing the polymer compound containing an ionic group may include a method in which in the first process, a polymer compound having no cationic group is polymerized, and in the second process, a polymer compound containing a cationic group is manufactured from the former polymer compound. Examples of the method for polymerizing the polymer compound having no cationic group in the first process may include the condensation polymerization reaction described above. Examples of the reaction in the second process may include a method in which the polymer compound obtained in the first process and a reagent such as a metal hydroxide, a metal carbonate, and alkylammonium hydroxide are dissolved in water or an organic solvent as needed and reacted at a temperature of the melting point of the organic solvent or higher and the boiling point of the organic solvent or lower.

Examples of another preferred method for manufacturing the polymer compound containing an ionic group may include a method in which in the first process, a polymer compound having no anionic group is polymerized, and in the second process, a polymer compound containing an anionic group is manufactured from the former polymer compound. Examples of the method for polymerizing the polymer compound having no anionic group in the first process may include the condensation polymerization reaction described above. Examples of the reaction in the second process may include a method in which a reagent such as an alkyl halide and SbF₅ is dissolved in water or an organic solvent as needed and reacted at a temperature of the melting point of the organic solvent or higher and the boiling point of the organic solvent or lower.

Impurities may be removed from the polymer compound containing an ionic group as needed through a process such as washing with water or an organic solvent and reprecipitation.

It is preferable that a layer containing the polymer compound according to the present invention is substantially non-luminescent when it is used for an electroluminescent device. Here, that a layer containing a given polymer compound is substantially non-luminescent means as follows. First, in Example 12 below, an electroluminescent device A is prepared in the same manner as Example 12 except that a polymer compound of interest is used in place of a non-conjugated polymer compound 1. On the other hand, an electroluminescent device C1 is prepared according to the description of Comparative Example 1. The electroluminescent device A and the electroluminescent device C1 are different only in that the electroluminescent device A has a layer containing the given polymer compound, while the electroluminescent device C1 has no layer containing the given polymer compound. Next, a forward voltage of 10 V is applied to the electroluminescent device A and the electroluminescent device C1 to measure a luminescent spectrum. A wavelength λ giving a maximum peak in the luminescent spectrum obtained with respect to the electroluminescent device C1 is measured. While assuming the luminescence intensity at the wavelength λ as 1, the luminescent spectrum obtained with respect to the electroluminescent device C1 is normalized and is integrated relative to the wavelength to calculate a normalized luminescence amount S₀. While assuming the luminescence intensity at the wavelength λ as 1, the luminescent spectrum obtained with respect to the electroluminescent device A is also normalized and is integrated relative to the wavelength to calculate a normalized luminescence amount S. When the value calculated by formula of (S−S₀)/S₀×100% is 30% or less, that is, when an increment of the normalized luminescence amount of the electroluminescent device A having the layer containing the given polymer compound from the normalized luminescence amount of the electroluminescent device C1 not having the layer containing the given polymer compound is 30% or less, the used layer containing the given polymer compound is regarded as substantially non-luminescent. The value calculated by formula of (S−S₀)/S₀×100 is preferably 15% or less and more preferably 10% or less.

<Electronic Device>

Next, an electronic device according to the present invention will be described.

The electronic device according to the present invention includes a layer containing a polymer compound having one or more structural units selected from the group consisting of the structural unit represented by Formula (1) and the structural unit represented by Formula (14) as a charge injection layer and/or a charge transport layer.

Examples of the electronic device according to the present invention can be used as an electroluminescent device, a photovoltaic cell, and the like. When the electronic device is used for the electroluminescent device (that may be referred to as the “electroluminescent device according to the present invention” below), the electronic device includes a light-emitting layer. When the electronic device is used for the photovoltaic cell (that may be referred to as the “photovoltaic cell according to the present invention” below), the electronic device includes a charge separation layer.

<Electroluminescent Device>

The electroluminescent device according to the present invention includes, for example, a cathode, an anode, a light-emitting layer positioned between the cathode and the anode, and a layer that is positioned between the light-emitting layer and the cathode or the anode and contains the polymer compound according to the present invention. The electroluminescent device according to the present invention may include a substrate as an optional constituent and may have a constitution in which the cathode, the anode, the light-emitting layer, the layer containing the polymer compound according to the present invention, and any optional constituents are provided on the surface of the substrate.

In one embodiment of the electroluminescent device according to the present invention, the anode is provided on the substrate, the light-emitting layer is stacked thereon, the layer containing the polymer compound according to the present invention is stacked thereon, and the cathode is further stacked thereon. In another embodiment, the anode is stacked on the substrate, the layer containing the polymer compound according to the present invention is stacked thereon, the light-emitting layer is stacked thereon, and the cathode is further stacked thereon. In still another embodiment, the anode is stacked on the substrate, the layer containing the polymer compound according to the present invention is stacked thereon, the light-emitting layer is stacked thereon, the layer containing the polymer compound according to the present invention is stacked thereon, and the cathode is further stacked thereon. In still another embodiment, the cathode is stacked on the substrate, the layer containing the polymer compound according to the present invention is stacked thereon, the light-emitting layer is stacked thereon, and the anode is further stacked thereon. In still another embodiment, the cathode is stacked on the substrate, the light-emitting layer is stacked thereon, the layer containing the polymer compound according to the present invention is stacked thereon, and the anode is further stacked thereon. In further another embodiment, the cathode is stacked on the substrate, the layer containing the polymer compound according to the present invention is stacked thereon, the light-emitting layer is stacked thereon, the layer containing the polymer compound according to the present invention is stacked thereon, and the anode is further stacked thereon. In these embodiments, layers having other functions such as a protective layer, a buffer layer, and a reflective layer may be further provided. The constitution of the electroluminescent device will be described separately in detail below. The electroluminescent device is further covered with a sealing film or a sealing substrate to form a light-emitting device with the electroluminescent device cut off from outside air.

The layer containing the polymer compound according to the present invention may be mixed with a known macromolecular or low molecular charge transport material, electroconductive carbons such as graphene, fullerene, and carbon nanotubes, an electroconductive compound such as a metal, an alloy, a metal oxide, and a metal sulfide, and a mixture thereof. As the charge transport material, those used for a hole transport layer or an electron transport layer, which will be described later, may be used. As the metal, alloy, metal oxide, and metal sulfide, those used for an anode or cathode, which will be described later, may be used. In addition, organic materials having neither a light-emitting function nor a charge transport function may be mixed without impairing the light-emitting function as the electroluminescent device.

The electroluminescent device according to the present invention may be an electroluminescent device of any type of what is called the bottom emission type that emits light from the substrate side, what is called the top emission type that emits light from the side opposite the substrate, and the double-sided emission type.

Examples of a method for forming the layer containing the polymer compound according to the present invention may include a film forming method using a solution containing the polymer compound.

Examples of a solvent for use in film formation from a solution may include solvents having a solubility parameter of 9.3 or more such as water, alcohols, ethers, esters, nitrile compounds, nitro compounds, alkyl halides, aryl halides, thiols, sulfides, sulfoxides, thioketones, amides, and carboxylic acids. Examples of the solvents may include (the value in parentheses denotes the value of the solubility parameter of each solvent) water (21.0), methanol (12.9), ethanol (11.2), 2-propanol (11.5), 1-butanol (9.9), t-butyl alcohol (10.5), acetonitrile (11.8), 1,2-ethanediol (14.7), N,N-dimethylformamide (11.5), dimethyl sulfoxide (12.8), acetic acid (12.4), nitrobenzene (11.1), nitromethane (11.0), 1,2-dichloroethane (9.7), dichloromethane (9.6), chlorobenzene (9.6), bromobenzene (9.9), dioxane (9.8), propylene carbonate (13.3), pyridine (10.4), carbon disulfide (10.0), and mixed solvents of these solvents (for the values of the solubility parameter, see Solvent Handbook, 14th printing, published by Kodansha Ltd. Publishers). Here, a description will be made on the mixed solvents composed of two solvents (designated as a solvent 1 and a solvent 2). The solubility parameter (δ_(m)) of the mixed solvent is determined by the equation: δ_(m)=δ₁×φ₁+δ₂×φ₂ (where δ₁ is the solubility parameter of the solvent 1, φ₁ is the volume fraction of the solvent 1, δ₂ is the solubility parameter of the solvent 2, and φ₂ is the volume fraction of the solvent 2.).

Examples of the film forming method from a solution may include application methods such as a spin coating method, a casting method, a micro gravure printing method, a gravure printing method, a bar coating method, a roll coating method, a wire bar coating method, a dip coating method, a slit coating method, a cap coating method, a spray coating method, a screen printing method, a flexographic printing method, an offset printing method, an inkjet printing method, and a nozzle coating method.

Because the optimum thickness of the layer containing the polymer compound according to the present invention varies depending on the polymer compound used, the thickness may be selected so as to give adequate values of drive voltage and light-emitting efficiency. The thickness is preferably from 1 nm to 1 μm, more preferably from 2 nm to 500 nm, and further more preferably from 2 nm to 200 nm. In view of protecting the light-emitting layer, the thickness is preferably from 5 nm to 1 μm.

The electroluminescent device includes a cathode and an anode and includes a light-emitting layer between the cathode and the anode. It may have another constituent.

For example, the electroluminescent device may include, between the anode and the light-emitting layer, one or more of a hole injection layer and a hole transport layer. When the hole injection layer is present, the device may include one or more hole transport layers between the light-emitting layer and the hole injection layer.

On the other hand, the device may include one or more of an electron injection layer and an electron transport layer between the cathode and the light-emitting layer. When the electron injection layer is present, the device may include one or more electron transport layers between the light-emitting layer and the electron injection layer.

The layer containing a polymer compound used in the present invention can be used for the hole injection layer, the hole transport layer, the electron injection layer, the electron transport layer, or the like. When the layer containing the polymer compound is used for the hole injection layer or the hole transport layer, the first electrode serves as the anode, and the second electrode serves as the cathode. When the layer containing the polymer compound is used for the electron injection layer or the electron transport layer, the first electrode serves as the cathode and the second electrode serves as the anode.

The anode is an electrode for supplying holes to the hole injection layer, the hole transport layer, the light-emitting layer, or the like, while the cathode is an electrode for supplying electrons to the electron injection layer, the electron transport layer, the light-emitting layer, or the like.

The light-emitting layer refers to a layer having a function of accepting holes from the anode or a layer adjacent on the anode side and accepting electrons from the cathode or a layer adjacent on the cathode side when an electric field is applied, a function of moving the accepted charges by the force of the electric field, and a function of providing a recombination site for electrons and holes to cause light emission.

The electron injection layer is a layer adjacent to the cathode and a layer having a function of receiving holes from the anode and refers to a layer having further as needed any of a function of transporting electrons, a function of blocking holes injected from the anode, and a function of supplying electrons to the light-emitting layer. The electron transport layer is a layer mainly having a function of transporting electrons and refers to a layer having further as needed any of a function of receiving electrons from the cathode, a function of blocking holes injected from the anode, and a function of supplying electrons to the light-emitting layer.

The hole injection layer is a layer adjacent to the anode and a layer having a function of receiving holes from the anode and refers to a layer having further as needed any of a function of transporting holes, a function of supplying holes to the light-emitting layer, and a function of blocking electrons injected from the cathode. The hole transport layer is a layer mainly having a function of transporting holes and refers to a layer having further as needed any of a function of receiving holes from the anode, a function of supplying holes to the light-emitting layer, and a function of blocking electrons injected from the cathode.

The electron transport layer and the hole transport layer may be collectively referred to as a charge transport layer. The electron injection layer and the hole injection layer may be collectively referred to as a charge injection layer.

In other words, the electroluminescent device according to the present invention may have the following layer structure (a) or may have a layer structure obtained by omitting one or more of the hole injection layer, the hole transport layer, the electron transport layer, and the electron injection layer from the layer structure (a). In the layer structure (a), the layer containing the polymer compound according to the present invention can be used as one or more layers selected from the group consisting of the hole injection layer, the hole transport layer, the electron injection layer, and the electron transport layer.

(a) Anode-Hole injection layer-(Hole transport layer)-Light-emitting layer-(Electron transport layer)-Electron injection layer-Cathode

The symbol “-” means that the layers are stacked adjacent to one another. The “(hole transport layer)” means a layer structure including one or more hole transport layers. The “(electron transport layer)” means a layer structure including one or more electron transport layers. The same is applicable to the description of the following layer structures.

Furthermore, the electroluminescent device according to the present invention can include two light-emitting layers within one layered structure. In this case, the electroluminescent device can include a layer structure (b) described below or a layer structure obtained by omitting one or more of the hole injection layer, the hole transport layer, the electron transport layer, the electron injection layer, and an electrode from the layer structure (b). In the layer structure (b), the layer containing the polymer compound according to the present invention can be used for a layer located between the anode and a light-emitting layer that is closest to the anode or used for a layer located between the cathode and a light-emitting layer that is closest to the cathode.

(b) Anode-Hole injection layer-(Hole transport layer)-Light-emitting layer-(Electron transport layer)-Electron injection layer-Electrode-Hole injection layer-(Hole transport layer)-Light-emitting layer-(Electron transport layer)-Electron injection layer-Cathode

Furthermore, the electroluminescent device according to the present invention can include three or more light-emitting layers within one layer structure. In this case, the electroluminescent device can include a layer structure (c) described below or a layer structure obtained by omitting one or more of the hole injection layer, the hole transport layer, the electron transport layer, the electron injection layer, and an electrode from the layer structure (c). In the layer structure (c), the layer containing the polymer compound according to the present invention can be used for a layer located between the anode and a light-emitting layer that is closest to the anode or used for a layer located between the cathode and a light-emitting layer that is closest to the cathode.

(c) Anode-Hole injection layer-(Hole transport layer)-Light-emitting layer-(Electron transport layer)-Electron injection layer-Repeating unit A-Repeating unit A . . . -Cathode

The “repeating unit A” indicates a unit of a layer structure of Electrode-Hole injection layer-(Hole transport layer)-Light-emitting layer-(Electron transport layer)-Electron injection layer.

Preferred examples of the layer structure of the electroluminescent device according to the present invention may include the following structures. In the following layer structures, the layer containing the polymer compound according to the present invention can be used for one or more layers selected from the group consisting of the hole injection layer, the hole transport layer, the electron injection layer, and the electron transport layer.

(a) Anode-Hole injection layer-Light-emitting layer-Cathode (b) Anode-Light-emitting layer-Electron injection layer-Cathode (c) Anode-Hole injection layer-Light-emitting layer-Electron injection layer-Cathode (d) Anode-Hole injection layer-Hole transport layer-Light-emitting layer-Cathode (e) Anode-Hole injection layer-Hole transport layer-Light-emitting layer-Electron injection layer-Cathode (f) Anode-Light-emitting layer-Electron transport layer-Electron injection layer-Cathode (g) Anode-Hole injection layer-Light-emitting layer-Electron transport layer-Electron injection layer-Cathode (h) Anode-Hole injection layer-Hole transport layer-Light-emitting layer-Electron transport layer-Electron injection layer-Cathode

The layer containing the polymer compound according to the present invention is preferably the electron injection layer or the electron transport layer. When the layer containing the polymer compound is the electron injection layer or the electron transport layer, the first electrode is the cathode.

The electroluminescent device according to the present invention may be further provided with an insulating layer adjacent to an electrode in order to improve adhesion with the electrode and improve the injection of charges from the electrode. A thin buffer layer may be provided on the interface of the charge transport layer and the light-emitting layer. The order and number of the layers to be stacked and the thickness of the layers may be selected taking light-emitting efficiency and device life into consideration.

Next, the material and forming method of the layers constituting the electroluminescent device according to the present invention will be described in detail.

—Substrate—

As a substrate constituting the electroluminescent device according to the present invention, any one is usable so long as it does not chemically change when an electrode is formed thereon and an organic layer is formed thereon. For example, substrates made from glass, plastics, polymer films, metal films, silicon, or the like and substrates obtained by laminating these materials may be used. Such substrates are commercially available or can be produced by known methods.

When the electroluminescent device according to the present invention constitutes a pixel of a display device, the substrate may have thereon a circuit for driving the pixel or have a planarized film on this drive circuit. When the planarized film is provided, the center line average roughness (Ra) of the planarized film satisfies preferably Ra<10 nm.

Ra can be measured based on JIS-B0601-2001 of Japanese Industrial Standards (JIS) with reference to JIS-B0651 to JIS-B0656, JIS-B0671-1, or the like.

—Anode—

In view of hole supply property to an organic semiconductor material used for the hole injection layer, the hole transport layer, an interlayer, the light-emitting layer, or the like, the anode constituting the electroluminescent device according to the present invention has preferably a work function of 4.0 eV or more on the surface of the anode on the light-emitting layer side.

As the material of the anode, electroconductive compounds such as metals, alloys, metal oxides, and metal sulfides, and mixtures thereof can be used. Specific examples may include electroconductive metal oxides such as tin oxide, zinc oxide, indium oxide, indium tin oxide (ITO), indium zinc oxide (IZO), and molybdenum oxide; metals such as gold, silver, chromium, and nickel; and mixtures of these electroconductive metal oxides and metals.

The anode may have a single layer structure composed of one or two or more of these materials or a multilayered structure composed of a plurality of layers having the same composition or different compositions. When it has a multilayered structure, it is more preferred to dispose a material having a work function of 4.0 eV or more on the outermost layer on the light-emitting layer side.

As a method for forming the anode, known methods can be used. Examples of the method may include a vacuum deposition method, a sputtering method, an ion plating method, a plating method, and a method by film formation from a solution (that may use a mixed solution with a macromolecular binder).

The thickness of the anode is usually from 10 nm to 10 μm, preferably from 40 nm to 500 nm.

In view of preventing faulty electric connection such as short circuit, the center line average roughness (Ra) of the surface of the anode on the light-emitting layer side satisfies preferably Ra<10 nm and more preferably Ra<5 nm.

Furthermore, the anode may be subjected to a surface treatment with a solution containing an electron acceptor compound such as UV ozone, a silane coupling agent, or 2,3,5,6-tetrafluoro-7,7,8,8-tetracyanoquinodimethane after being formed by the above method. The surface treatment improves electric connection with a layer to be brought into contact with the anode.

When the anode is used as a light reflective electrode of the electroluminescent device according to the present invention, the anode preferably has a multilayered structure composed of a combination of a light reflective layer made of a highly light reflective metal and a high work function material layer containing a material having a work function of 4.0 eV or more.

Specific examples of the structure of the anode may include:

(i) Ag—MoO₃,

(ii) (Ag—Pd—Cu alloy)-(ITO and/or IZO), (iii) (Al—Nd alloy)-(ITO and/or IZO), (iv) (Mo—Cr alloy)-(ITO and/or IZO), and (v) (Ag—Pd—Cu alloy)-(ITO and/or IZO)-MoO₃.

In order to achieve a sufficient light reflectance, the thickness of the highly light reflective metal layer such as Al, Ag, an Al alloy, a Ag alloy, a Cr alloy, or the like is preferably 50 nm or more and more preferably 80 nm or more. The thickness of the high work function material layer such as ITO, IZO, and MoO₃ is usually within a range from 5 nm to 500 nm.

—Hole Injection Layer—

In the electroluminescent device according to the present invention, examples of the material for forming the hole injection layer other than the polymer compound according to the present invention may include: carbazole derivatives, triazole derivatives, oxazole derivatives, oxadiazole derivatives, imidazole derivatives, fluorene derivatives, polyarylalkane derivatives, pyrazoline derivatives, pyrazolone derivatives, phenylenediamine derivatives, arylamine derivatives, starburst type amines, phthalocyanine derivatives, amino-substituted chalcone derivatives, styrylanthracene derivatives, fluorenone derivatives, hydrazone derivatives, stilbene derivatives, silazane derivatives, aromatic tertiary amine compounds, styrylamine compounds, aromatic dimethylidyne-based compounds, porphyrin-based compounds, polysilane-based compounds, poly(N-vinylcarbazole) derivatives, organic silane derivatives, and polymers containing them; electroconductive metal oxides such as vanadium oxide, tantalum oxide, tungsten oxide, molybdenum oxide, ruthenium oxide, and aluminum oxide; electroconductive polymers and oligomers such as polyaniline, aniline-based copolymers, thiophene oligomers, and polythiophene; organic electroconductive materials such as poly(3,4-ethylenedioxythiophene)polystyrenesulfonic acid and polypyrrole and polymers containing them; amorphous carbon; acceptor organic compounds such as tetracyanoquinodimethane derivatives (for example, 2,3,5,6-tetrafluoro-7,7,8,8-tetracyanoquinodimethane), 1,4-naphthoquinone derivatives, diphenoquinone derivatives, and polynitro compounds; and silane coupling agents such as octadecyltrimethoxysilane.

The above materials may be used as a single component or a composition composed of a plurality of components. The hole injection layer may have a single layered structure composed only of the above material or a multilayered structure composed of a plurality of layers having the same or different compositions. In addition, materials exemplified as materials usable in the hole transport layer or the interlayer can also be used for the hole injection layer.

As a method for preparing the hole injection layer, known methods can be used. When the material used for the preparation of the hole injection layer is an inorganic material, the vacuum deposition method, the sputtering method, the ion plating, or the like can be employed. When the material is a low molecular organic material, the vacuum deposition method, a transfer method such as laser transfer or heat transfer, the method by film formation from a solution (that may use a mixed solution with a macromolecular binder), or the like can be employed. When a hole injection material is a macromolecular organic material, the method by film formation from a solution can be employed.

When the hole injection material is a low molecular organic material such as a pyrazoline derivative, an arylamine derivative, a stilbene derivative, and a triphenyldiamine derivative, the hole injection layer is preferably formed by the vacuum deposition method.

The hole injection layer may also be formed using a mixed solution containing a polymer compound binder and the low molecular organic material dispersed therein.

The polymer compound binder to be mixed is preferably a compound that does not extremely hinder charge transport, and a compound not exhibiting strong absorption to visible light is suited for use. Specific examples of the polymer compound binder may include poly(N-vinylcarbazole), polyaniline and derivatives thereof, polythiophene and derivatives thereof, poly(p-phenylenevinylene) and derivatives thereof, poly(2,5-thienylene vinylene) and derivatives thereof, polycarbonates, polyacrylates, polymethyl acrylate, polymethyl methacrylate, polystyrene, polyvinyl chloride, and polysiloxane.

The solvent for use in the film formation from a solution may be any solvent that can dissolve the hole injection material. Examples of the solvent may include: water; chlorine-containing solvents such as chloroform, methylene chloride, and dichloromethane; ether solvents such as tetrahydrofuran; aromatic hydrocarbon solvents such as toluene and xylene; ketone solvents such as acetone and methyl ethyl ketone; and ester solvents such as ethyl acetate, butyl acetate, and ethyl cellosolve acetate.

Examples of the film forming method from a solution may include application methods including: coating methods such as the spin coating method from a solution, the casting method, the bar coating method, the roll coating method, the wire bar coating method, the dip coating method, the slit coating method, a capillary coating method, the spray coating method, and a nozzle coating method; and printing methods such as the micro gravure printing method, the gravure printing method, the screen printing method, the flexographic printing method, the offset printing method, a reverse printing method, and the inkjet printing method. Because of the simplicity of pattern forming, preferred examples may include the printing methods such as the gravure printing method, the screen printing method, the flexographic printing method, the offset printing method, the reverse printing method, the inkjet printing method and the nozzle coating method.

When an organic compound layer such as the hole transport layer and the light-emitting layer is formed after the formation of the hole injection layer, and particularly when both layers are formed by an application method, a layered structure may not be formed, because the layer applied first dissolves in a solvent contained in a solution for a layer applied later. In such a case, a method for insolubilizing a lower layer may be employed. Examples of the insolubilizing method may include: a method of cross-linking a polymer compound through a cross-linking group added thereto, thereby insolubilizing the lower layer; a method of mixing with a low molecular compound having an aromatic-ring-containing cross-linking group, typified by aromatic bisazide, as a cross-linking agent and cross-linking it to insolubilize the lower layer; a method of mixing a low molecular compound having an aromatic-ring-free cross-linking group, typified by an acrylate group, as a cross-linking agent and cross-linking it to insolubilize the lower layer; a method of exposing the lower layer to ultraviolet light to cause cross-linking, thereby insolubilizing the lower layer in an organic solvent to be used in the formation of an upper layer; and a method of heating the lower layer to cause cross-linking, thereby insolubilizing it in an organic solvent to be used in the formation of the upper layer. The heating temperature when the lower layer is heated is usually from 100° C. to 300° C. The heating time is usually from 1 minute to 1 hour.

As another method for stacking the upper layer without dissolving the lower layer, there is a method using solutions different in polarity for the formation of the adjacent layers. For example, there is a method using a water soluble polymer compound for the lower layer and an oil soluble polymer compound for the upper layer to prevent the lower layer from dissolving even by the application of the upper layer.

The optimum thickness of the hole injection layer varies depending on the material used and may be selected so as to give adequate values of drive voltage and light-emitting efficiency. The thickness is usually 1 nm to 1 μm, preferably from 2 nm to 500 nm, and further preferably from 10 nm to 100 nm.

—Hole Transport Layer—

In the electroluminescent device according to the present invention, examples of a material constituting the hole transport layer other than the polymer compound according to the present invention may include: carbazole derivatives, triazole derivatives, oxazole derivatives, oxadiazole derivatives, imidazole derivatives, fluorene derivatives, polyarylalkane derivatives, pyrazoline derivatives, pyrazolone derivatives, phenylenediamine derivatives, arylamine derivatives, starburst type amines, phthalocyanine derivatives, amino-substituted chalcone derivatives, styrylanthracene derivatives, fluorenone derivatives, hydrazone derivatives, stilbene derivatives, silazane derivatives, aromatic tertiary amine compounds, styrylamine compounds, aromatic dimethylidyne-based compounds, porphyrin-based compounds, polysilane-based compounds, poly(N-vinylcarbazole) derivatives, organic silane derivatives, and polymers containing them; electroconductive polymers and oligomers such as polyaniline, aniline-based copolymers, thiophene oligomers, and polythiophene; and organic electroconductive materials such as polypyrrole.

The above materials may be used as a single component or a composition composed of a plurality of components. The hole transport layer may have a single layered structure composed only of the above material or a multilayered structure composed of a plurality of layers having the same or different compositions. In addition, materials exemplified as materials usable in the hole injection layer can also be used for the hole transport layer.

As a method for preparing the hole transport layer and the interlayer, for example, the same as the method for the film formation of the hole injection layer can be employed. Examples of the film forming method from a solution may include application methods and printing methods such as the spin coating method, the casting method, the bar coating method, the slit coating method, the spray coating method, the nozzle coating method, the gravure printing method, the screen printing method, the flexographic printing method, and the inkjet printing method. When a sublimation compound material is used, examples of the method may include the vacuum deposition method and the transfer method. Examples of the solvent for use in the film formation from a solution may include the solvents exemplified in the film forming method for the hole injection layer.

When an organic compound layer such as the light-emitting layer is formed by an application method after the formation of the hole transport layer, and when a lower layer dissolves in a solvent contained in a solution for a layer applied later, the lower layer can be insolubilized by the same method as exemplified in the film forming method for the hole injection layer.

The optimum thickness of the hole transport layer varies depending on the material used and may be selected so as to give adequate values of drive voltage and light-emitting efficiency. The thickness is usually 1 nm to 1 μm, preferably from 2 nm to 500 nm, and further preferably from 5 nm to 100 nm.

—Light-Emitting Layer—

In the electroluminescent device according to the present invention, when the light-emitting layer contains the polymer compound, conjugated polymer compounds such as polyfluorene derivatives, polyparaphenylene vinylene derivatives, polyphenylene derivatives, polyparaphenylene derivatives, polythiophene derivatives, polydialkylfluorenes, polyfluorenebenzothiadiazole, and polyalkylthiophenes are suited for use as the polymer compound.

The light-emitting layer containing the polymer compound may contain a macromolecular dye compound such as a perylene dye, a coumarin dye, and a rhodamine dye, and a low molecular dye compound such as rubrene, perylene, 9,10-diphenylanthracene, tetraphenylbutadiene, nile red, coumarin 6, and quinacridone. In addition, the light-emitting layer may contain a naphthalene derivative, anthracene or a derivative thereof, perylene or a derivative thereof, a dye based on polymethine, xanthene, coumarin, and cyanine, a metal complex of 8-hydroxyquinoline or a derivative thereof, an aromatic amine, tetraphenylcyclopentadiene or a derivative thereof, tetraphenylbutadiene or a derivative thereof, and a metal complex emitting phosphorescence such as tris(2-phenylpyridine)iridium.

The light-emitting layer of the electroluminescent device according to the present invention may include a composition composed of a non-conjugated polymer compound and a luminous organic compound such as the above organic dye or the above metal complex. Examples of the non-conjugated polymer compound may include polyethylene, polyvinyl chloride, polycarbonate, polystyrene, polymethyl methacrylate, polybutyl methacrylate, polyester, polysulfone, polyphenylene oxide, polybutadiene, poly(N-vinylcarbazole), hydrocarbon resins, ketone resins, phenoxy resins, polyamide, ethyl cellulose, vinyl acetate, ABS resins, polyurethane, melamine resins, unsaturated polyester resins, alkyd resins, epoxy resins, and silicone resins. The non-conjugated polymer compound may include, on the side chain thereof, a structure of one or more derivatives or compounds selected from the group consisting of carbazole derivatives, triazole derivatives, oxazole derivatives, oxadiazole derivatives, imidazole derivatives, fluorene derivatives, polyarylalkane derivatives, pyrazoline derivatives, pyrazolone derivatives, phenylenediamine derivatives, arylamine derivatives, amino-substituted chalcone derivatives, styrylanthracene derivatives, fluorenone derivatives, hydrazone derivatives, stilbene derivatives, silazane derivatives, aromatic tertiary amine compounds, styrylamine compounds, aromatic dimethylidyne compounds, porphyrin compounds, and organic silane derivatives.

When the light-emitting layer contains a low molecular compound, examples of the low molecular compound may include low molecular dye compounds such as rubrene, perylene, 9,10-diphenylanthracene, tetraphenylbutadiene, nile red, coumarin 6, carbazole, and quinacridone, naphthalene derivatives, anthracene and derivatives thereof, perylene and derivatives thereof, dyes based on polymethine, xanthene, coumarin, cyanine, and indigo, metal complexes of 8-hydroxyquinoline and derivatives thereof, metal complexes of phthalocyanine and derivatives thereof, aromatic amines, tetraphenylcyclopentadiene and derivatives thereof, and tetraphenylbutadiene and derivatives thereof.

When the light emitting layer contains a metal complex emitting phosphorescence, examples of the metal complex may include tris(2-phenylpyridine)iridium, thienylpyridine ligand-containing iridium complexes, phenylquinoline ligand-containing iridium complexes, and triazacyclononane skeleton-containing terbium complexes.

The above materials may be used as a single component or a composition composed of a plurality of components. The light-emitting layer may have a single layered structure composed one or two or more of the above materials or a multilayered structure composed of a plurality of layers having the same or different compositions.

As a film forming method for the light-emitting layer, the same as the method for the film formation of the hole injection layer may be employed. Examples of the film forming method from a solution may include application methods and printing methods such as the spin coating method, the casting method, the bar coating method, the slit coating method, the spray coating method, the nozzle coating method, the gravure printing method, the screen printing method, the flexographic printing method, and the inkjet printing method. When a sublimation compound material is used, examples of the method may include the vacuum deposition method and a transfer method.

Examples of the solvent for use in the film formation from a solution may include the solvents exemplified in the film forming method for the hole injection layer.

When an organic compound layer such as the electron transport layer is formed by an application method after the formation of the light-emitting layer, and when a lower layer dissolves in a solvent contained in a solution for a layer applied later, the lower layer can be insolubilized by the same method as exemplified in the film forming method for the hole injection layer.

The optimum thickness of the light-emitting layer varies depending on the material used and may be selected so as to give adequate values of drive voltage and light-emitting efficiency. The thickness is usually 5 nm to 1 μm, preferably from 10 nm to 500 nm, and more preferably from 30 nm to 200 nm.

—Electron Transport Layer—

In the electroluminescent device according to the present invention, known materials that constitute the electron transport layer other than the polymer compound according to the present invention can be used. Examples of the material may include triazole derivatives, oxazole derivatives, oxadiazole derivatives, imidazole derivatives, fluorene derivatives, benzoquinone and derivatives thereof, naphthoquinone and derivatives thereof, anthraquinone and derivatives thereof, tetracyanoanthraquinodimethane and derivatives thereof, fluorenone derivatives, diphenyldicyanoethylene and derivatives thereof, diphenoquinone derivatives, anthraquinodimethane derivatives, anthrone derivatives, thiopyran dioxide derivatives, carbodiimide derivatives, fluorenylidenemethane derivatives, distyrylpyrazine derivatives, aromacyclic tetracarboxylic anhydrides such as naphthalene and perylene, phthalocyanine derivatives, various metal complexes typified by metal complexes of a 8-quinolinol derivative, metal phthalocyanines, and metal complexes having benzoxazole or benzothiazole as a ligand, organic silane derivatives, metal complexes of 8-hydroxyquinoline or a derivative thereof, polyquinoline and derivatives thereof, polyquinoxaline and derivatives thereof, and polyfluorene and derivatives thereof. Of these materials, triazole derivatives, oxadiazole derivatives, benzoquinone and derivatives thereof, anthraquinone and derivatives thereof, metal complexes of 8-hydroxyquinoline or a derivative thereof, polyquinoline and derivatives thereof, polyquinoxaline and derivatives thereof, and polyfluorene and derivatives thereof are preferred.

The above materials may be used as a single component or a composition composed of a plurality of components. The electron transport layer may have a single layered structure composed one or two or more of the above materials or a multilayered structure composed of a plurality of layers having the same or different compositions. In addition, materials exemplified as materials usable in the electron injection layer can also be used for the electron transport layer.

As a film forming method for the electron transport layer, for example, the same as the method for the film formation of the hole injection layer may be employed. Examples of the film forming method from a solution may include application methods and printing methods such as the spin coating method, the casting method, the bar coating method, the slit coating method, the spray coating method, the nozzle coating method, the gravure printing method, the screen printing method, the flexographic printing method, and the inkjet printing method. When a sublimation compound material is used, examples of the method may include the vacuum deposition method and a transfer method.

Examples of the solvent for use in the film formation from a solution may include the solvents exemplified in the film forming method for the hole injection layer.

When an organic compound layer such as the electron injection layer is formed by an application method after the formation of the electron transport layer, and when a lower layer dissolves in a solvent contained in a solution for a layer applied later, the lower layer can be insolubilized by the same method as exemplified in the film forming method for the hole injection layer.

The optimum thickness of the electron transport layer varies depending on the material used and may be selected so as to give adequate values of drive voltage and light-emitting efficiency. The thickness is usually 1 nm to 1 μm, preferably from 2 nm to 500 nm, and more preferably from 5 nm to 100 nm.

—Electron Injection Layer—

In the electroluminescent device according to the present invention, known materials that constitute the electron injection layer other than the polymer compound according to the present invention can be used. Examples of the material may include triazole derivatives, oxazole derivatives, oxadiazole derivatives, imidazole derivatives, fluorene derivatives, benzoquinone and derivatives thereof, naphthoquinone and derivatives thereof, anthraquinone and derivatives thereof, tetracyanoanthraquinodimethane and derivatives thereof, fluorenone derivatives, diphenyldicyanoethylene and derivatives thereof, diphenoquinone derivatives, anthraquinodimethane derivatives, anthrone derivatives, thiopyran dioxide derivatives, carbodiimide derivatives, fluorenylidenemethane derivatives, distyrylpyrazine derivatives, aromacyclic tetracarboxylic anhydrides such as naphthalene and perylene, phthalocyanine derivatives, various metal complexes typified by metal complexes of a 8-quinolinol derivative, metal phthalocyanines, and metal complexes having benzoxazole or benzothiazole as a ligand, and organic silane derivatives.

The above materials may be used as a single component or a composition composed of a plurality of components. The electron injection layer may have a single layered structure composed only of the above material or a multilayered structure composed of a plurality of layers having the same or different compositions. In addition, materials exemplified as materials usable in the electron transport layer and a hole block layer can also be used for the electron injection layer.

As a film forming method for the electron injection layer, for example, the same as the method for the film formation of the hole injection layer may be employed. Examples of the film forming method from a solution may include application methods and printing methods such as the spin coating method, the casting method, the bar coating method, the slit coating method, the spray coating method, the nozzle coating method, the gravure printing method, the screen printing method, the flexographic printing method, and the inkjet printing method. When a sublimation compound material is used, examples of the method may include the vacuum deposition method and a transfer method.

Examples of the solvent for use in the film formation from a solution may include the solvents exemplified in the film forming method for the hole injection layer.

The optimum thickness of the electron injection layer varies depending on the material used and may be selected so as to give adequate values of drive voltage and light-emitting efficiency. The thickness is usually 1 nm to 1 μm, preferably from 2 nm to 500 nm, and more preferably from 5 nm to 100 nm.

—Cathode—

In the electroluminescent device according to the present invention, the cathode may have a single layered structure composed of a single material or a plurality of materials, or a multilayered structure composed of a plurality of layers. When the cathode has a single layer structure, examples of the material of the cathode may include low resistance metals such as gold, silver, copper, aluminum, chromium, tin, lead, nickel, and titanium, alloys containing these metals, electroconductive metal oxides such as tin oxide, zinc oxide, indium oxide, indium tin oxide (ITO), indium zinc oxide (IZO), and molybdenum oxide, and mixtures of the electroconductive metal oxide and the metal exemplified above, and among them, aluminum and alloys containing aluminum are preferred. When the cathode has a multilayered structure, it has preferably a two-layer structure including a first cathode layer and a cover cathode layer or a three-layer structure including a first cathode layer, a second cathode layer, and a cover cathode layer. The first cathode layer as used herein refers to a layer present on the side closest to the light-emitting layer among the cathodes. The cover cathode layer refers to a layer that covers the first cathode layer in a two-layer structure and covers the first cathode layer and the second cathode layer in a three-layer structure. In view of electron supplying capacity, the material of the first cathode layer has preferably a work function of 3.5 eV or less. Oxides, fluorides, carbonates, complex oxides, or the like of a metal having a work function of 3.5 eV or less are also suited for use as the first cathode layer material. As the material of the cover cathode layer, metals, metal oxides, or the like having a low resistivity and highly corrosion-resistant to water are suited for use.

Examples of the first cathode layer material may include one or more materials selected from the group consisting of alkali metals, alkaline earth metals, alloys containing one or more of these metals, oxides, halides, carbonates and complex oxides of the metals, and mixtures thereof. Examples of the alkali metals or oxides, halides, carbonates, or complex oxides thereof may include lithium, sodium, potassium, rubidium, cesium, lithium oxide, sodium oxide, potassium oxide, rubidium oxide, cesium oxide, lithium fluoride, sodium fluoride, potassium fluoride, rubidium fluoride, cesium fluoride, lithium carbonate, sodium carbonate, potassium carbonate, rubidium carbonate, cesium carbonate, potassium molybdate, potassium titanate, potassium tungstate, and cesium molybdate. Examples of the alkaline earth metals or oxides, halides, carbonates, or complex oxides thereof may include magnesium, calcium, strontium, barium, magnesium oxide, calcium oxide, strontium oxide, barium oxide, magnesium fluoride, calcium fluoride, strontium fluoride, barium fluoride, magnesium carbonate, calcium carbonate, strontium carbonate, barium carbonate, barium molybdate, and barium tungstate. Examples of the alloy containing one or more alkali metals or alkaline earth metals may include a Li—Al alloy, a Mg—Ag alloy, an Al—Ba alloy, a Mg—Ba alloy, a Ba—Ag alloy, and a Ca—Bi—Pb—Sn alloy. Compositions made of the material exemplified as the first cathode layer material and the material exemplified as the material constituting the electron injection layer can be used for the first cathode layer. Examples of the material of the second cathode layer may include the same materials as those of the first cathode layer.

Examples of the cover cathode layer material may include low resistance metals such as gold, silver, copper, aluminum, chromium, tin, lead, nickel, and titanium, alloys containing these metals, metal nanoparticles, metal nanowires, electroconductive metal oxides such as tin oxide, zinc oxide, indium oxide, indium tin oxide (ITO), indium zinc oxide (IZO), and molybdenum oxide, mixtures of these electroconductive metal oxides and metals, and nanoparticles of the electroconductive metal oxides, and electroconductive carbons such as graphene, fullerene, and carbon nanotubes.

Examples of the cathode having a multilayered structure may include: a two-layer structure including a first cathode layer and a cover cathode layer such as Mg/Al, Ca/Al, Ba/Al, NaF/Al, KF/Al, RbF/Al, CsF/Al, Na₂CO₃/Al, K₂CO₃/Al, and Cs₂CO₃/Al; and a three-layer structure including a first cathode layer, a second cathode layer, and a cover cathode layer such as LiF/Ca/Al, NaF/Ca/Al, KF/Ca/Al, RbF/Ca/Al, CsF/Ca/Al, Ba/Al/Ag, KF/Al/Ag, KF/Ca/Ag, and K₂CO₃/Ca/Ag. The symbol “/” means that the layers are adjacent to each other. The material of the second cathode layer preferably has a reduction action on the material of the first cathode layer. The presence or absence and degree of the reduction action between materials can be estimated, for example, from bond dissociation energy (ΔrH°) between compounds. More specifically, in the reduction reaction of the material constituting the first cathode electrode with the material constituting the second cathode layer, when they are a combination of materials to provide a positive bond dissociation energy, it can be said that the material of the second cathode layer has a reduction action on the material of the first cathode layer. With respect to the bond dissociation energy, it is possible to refer to, for example, “Handbook on Electrochemistry, 5th ed.” (Maruzen Co., Ltd., published in 2000) and “Thermodynamic Database MALT” (Kagaku Gijutsu-Sha, published in 1992).

As a method for preparing the cathode, known methods can be used. Examples of the method may include the vacuum deposition method, the sputtering method, the ion plating method, and the method by film formation from a solution (that may contain a macromolecular binder). For the formation of the cathode by using metals, metal oxides, fluorides, or carbonates, the vacuum deposition method is frequently used. For the formation of the cathode by using metal oxides having a high boiling point, metal complex oxides, or electroconductive metal oxides such as indium tin oxide (ITO), the sputtering method or the ion plating method are frequently used. For the formation of the cathode by using in combination two or more of metals, metal oxides, fluorides, carbonates, metal oxides having a high boiling point, metal complex oxides, and electroconductive metal oxides, a co-deposition method, the sputtering method, the ion plating method, or the like are used. For the formation of the cathode by using metal nanoparticles, metal nanowires, or electroconductive metal oxide nanoparticles, the method by film formation from a solution is frequently used. In particular, for the formation of the cathode by using compositions of low molecular organic compounds and metals, metal oxides, fluorides, or carbonates, the co-deposition method is suited.

The optimum thickness of the cathode varies depending on the material and the layer structure used and may be selected so as to give adequate values of drive voltage, light-emitting efficiency, and device life. The thickness of the first cathode layer is usually 0.5 nm to 20 nm, and the thickness of the cover cathode layer is usually 10 nm to 1 μm. For example, when Ba or Ca is used for the first cathode layer, and Al is used for the cover cathode layer, the thickness of Ba or Ca is preferably from 2 nm to 10 nm, and the thickness of Al is preferably from 10 nm to 500 nm. When NaF or KF is used for the first cathode layer, and Al is used for the cover cathode layer, the thickness of NaF or KF is preferably from 1 nm to 8 nm, and the thickness of Al is preferably from 10 nm to 500 nm.

In the electroluminescent device according to the present invention using the cathode as a light transmitting electrode, a visible light transmittance of the cover cathode layer is preferably 40% or more and more preferably 50% or more. This visible light transmittance can be achieved by using a transparent electroconductive metal oxide such as indium tin oxide (ITO), indium zinc oxide (IZO), or molybdenum oxide as the cover cathode layer material, or adjusting the thickness of the cover cathode layer to be 30 nm or less by using a low resistance metal such as gold, silver, copper, aluminum, chromium, tin, and lead, and an alloy containing such metals.

For the purpose of improving the light transmittance from the cathode side, an antireflection layer may be disposed on the cover cathode layer of the cathode. Materials used for the antireflection layer have preferably a refractive index of from 1.8 to 3.0. Examples of the materials capable of satisfying this refractive index may include ZnS, ZnSe, and WO₃. Although the thickness of the antireflection layer varies depending on the combination of the materials, it is usually from 10 nm to 150 nm.

—Insulating Layer—

An insulating layer with a thickness of 5 nm or less that the electroluminescent device according the present invention optionally has functions of improving adhesion with an electrode, improving injection of charges from the electrode, and preventing mixing with a layer adjacent to it. Examples of the material of the insulating layer may include metal fluorides, metal oxides, and organic insulating materials (polymethyl methacrylate or the like). Examples of the electroluminescent device provided with the insulating layer with a thickness of 5 nm or less may include a device provided with the insulating layer with a thickness 5 nm or less adjacent to the cathode and an device provided with the insulating layer with a thickness of 5 nm or less adjacent to the anode.

—Other Constituents—

The device may be further provided with a sealing member on the side opposite the substrate across the light emitting layer or the like. In addition, it may have optional constituents for constituting a display device including filters such as a color filter and a fluorescence conversion filter and circuits and wirings necessary for the driving of pixels.

—Method for Manufacturing Electroluminescent Device—

The electroluminescent device according to the present invention can be manufactured, for example, by successively stacking layers on a substrate. More specifically, the electroluminescent device can be manufactured by providing the anode on the substrate, stacking layers such as the hole injection layer and the hole transport layer one after another, stacking thereon the light-emitting layer, stacking thereon layers such as the electron transport layer and the electron injection layer, and further stacking the cathode thereon. Another manufacturing method includes providing the cathode on the substrate, stacking thereon layers such as the electron injection layer, the electron transport layer, the light-emitting layer, the hole transport layer, and the hole injection layer one after another, and further stacking the anode thereon to manufacture the electroluminescent device. A still another manufacturing method includes facing and joining the anode or an anode-side base material obtained by stacking layers on the anode and the cathode or a cathode side base material obtained by stacking layers on the cathode to manufacture the electroluminescent device.

—Application of Electroluminescent Device—

A display device can be manufactured using the electroluminescent device according to the present invention. The display device has the electroluminescent device as a pixel unit. As a form of the arrangement of pixel units, a usual arrangement in display devices such as television may be employed and a form of the arrangement in which a number of pixels may be arranged on a common substrate can be employed. In the device of the present invention, pixels arranged on the substrate can be formed in a pixel area defined by a bank. In addition, the electroluminescent device according to the present invention can be used for planar or curved illumination devices.

<Photovoltaic Cell>

A photovoltaic cell according to the present invention includes, for example, an anode, a cathode, a charge separation layer located between the anode and the cathode, and a layer that is located between the charge separation layer and the anode or cathode, and contains the polymer compound according to the present invention. The photovoltaic cell according to the present invention may have a substrate as an optional constituent and it may include, on the surface of the substrate, the anode, the cathode, the charge separation layer, and the layer containing the polymer compound according to the present invention, and optional constituents.

In one embodiment of the photovoltaic cell according to the present invention, the cathode is provided on the substrate, the charge separation layer is stacked thereon, the layer containing the polymer compound according to the present invention is stacked thereon, and the anode is further stacked thereon. In another embodiment, the cathode is provided on the substrate, the layer containing the polymer compound according to the present invention is stacked thereon, the charge separation layer is stacked thereon, and the anode is further stacked thereon. In still another embodiment, the cathode is provide on the substrate, the layer containing the polymer compound according to the present invention is stacked thereon, the charge separation layer is stacked thereon, the layer containing the polymer compound according to the present invention is stacked thereon, and the anode is further stacked thereon. In still another embodiment, the anode is provided on the substrate, the layer containing the polymer compound according to the present invention is stacked thereon, the charge separation layer is stacked thereon, and the anode is further stacked thereon. In still another embodiment, the anode is provided on the substrate, the charge separation layer is stacked thereon, the layer containing the polymer compound according to the present invention is stacked thereon, and the cathode is further stacked thereon. In further another embodiment, the anode is stacked on the substrate, the layer containing the polymer compound according to the present invention is stacked thereon, the charge separation layer is stacked thereon, the layer containing the polymer compound according to the present invention is stacked thereon, and the cathode is further stacked thereon. In these embodiments, layers other than the layer containing the polymer compound according to the present invention or the charge separation layer may be further provided. The constitution of the photovoltaic cell will be described in detail below.

The layer containing the polymer compound according to the present invention may contain a known electron donar compound and/or electron acceptor compound, metal nanoparticles, or metal oxide nanoparticles.

Examples of a method for forming the layer containing the polymer compound may include a method for film formation using a solution containing the polymer compound.

Examples of a solvent for use in film formation from a solution may include solvents having a solubility parameter of 9.3 or more out of water, alcohols, ethers, esters, carboxylic acids, alkyl halides, heterocyclic aromatic compounds, thiols, sulfides, thioketones, sulfoxides, nitro compounds, nitrile compounds, and mixed solvents of these solvents. The examples and solubility parameters of the solvents are described above.

Examples of the film forming method from a solution may include application methods such as the spin coating method, the casting method, the micro gravure printing method, the gravure printing method, the bar coating method, the roll coating method, the wire bar coating method, the dip coating method, the slit coating method, the cap coating method, the spray coating method, the screen printing method, the flexographic printing method, the offset printing method, the inkjet printing method, and the nozzle coating method.

Because the optimum thickness of the layer containing the polymer compound varies depending on the polymer compound used, the thickness may be selected so as to give an adequate value of photovoltaic efficiency. The thickness is preferably from 1 nm to 1 μm, more preferably from 2 nm to 500 nm, and further preferably from 2 nm to 200 nm.

The photovoltaic cell according to the present invention includes the anode, the cathode, and the charge separation layer located between the anode and the cathode and preferably includes the layer containing the polymer compound according to present invention either one of or both between the charge separation layer and the anode and between the charge separation layer and the anode. More preferably, the photovoltaic cell includes the layer containing the polymer compound between the cathode and the charge separation layer.

The charge separation layer of the photovoltaic cell according to the present invention preferably contains an electron donar compound and an electron acceptor compound.

The charge separation layer may contain one compound alone or two or more compounds in combination for each of the electron donar compound and the electron acceptor compound. The electron donar compound and the electron acceptor compound are relatively determined depending on the energy level thereof.

Examples of the electron donar compound may include pyrazoline derivatives, arylamine derivatives, stilbene derivatives, triphenyldiamine derivatives, and conjugated polymer compounds. Examples of the conjugated polymer compounds may include oligothiophene and derivatives thereof, polyfluorene and derivatives thereof, polyvinylcarbazole and derivatives thereof, polysilane and derivatives thereof, polysiloxane derivatives having, on the side chain or main chain thereof, an aromatic amine, polyaniline and derivatives thereof, polypyrrole and derivatives thereof, polyphenylenevinylene and derivatives thereof, and polythienylenevinylene and derivatives thereof.

Examples of the electron acceptor compound may include oxadiazole derivatives, anthraquinodimethane and derivatives thereof, benzoquinone and derivatives thereof, naphthoquinone and derivatives thereof, anthraquinone and derivatives thereof, tetracyanoanthraquinodimethane and derivatives thereof, fluorenone derivatives, diphenyldicyanoethylene and derivatives thereof, diphenoquinone derivatives, metal complexes of 8-hydroxyquinoline and derivatives thereof, polyquinoline and derivatives thereof, polyquinoxaline and derivatives thereof, polyfluorene and derivatives thereof, fullerenes such as C₆₀ and derivatives thereof, phenanthrene derivatives such as bathocuproine, metal oxides such as titanium oxide, and carbon nanotubes. As the electron acceptor compound, titanium oxide, carbon nanotubes, fullerene, and fullerene derivatives are preferred, and fullerene and fullerene derivatives are particularly preferred.

The thickness of the charge separation layer is usually from 1 nm to 100 μm, more preferably from 2 nm to 1000 nm, further preferably from 5 nm to 500 nm, and still more preferably from 20 nm to 200 nm.

<Method for Manufacturing Charge Separation Layer>

Any method can be employed for the method for manufacturing the charge separation layer and examples thereof may include film formation from a solution and film formation by the vacuum deposition method.

For the film formation from a solution, it is possible to use application methods such as the spin coating method, the casting method, the microgravure coating method, the gravure coating method, the bar coating method, the roll coating method, the wire bar coating method, the dip coating method, the spray coating method, the screen printing method, the gravure printing method, the flexographic printing method, the offset printing method, the inkjet printing method, a dispenser printing method, the nozzle coating method, and the capillary coating method. Among these, the spin coating method, the flexographic printing method, the gravure printing method, the inkjet printing method, and the dispenser printing method are preferred.

The photovoltaic cell according to the present invention is usually formed on a substrate. Any substrate is usable so long as it does not change upon formation of an electrode and formation of an organic material layer. Examples of the material of the substrate may include glass, plastics, polymer films, and silicon. When the substrate employed is opaque, the electrode on the opposite side (that is, an electrode distant from the substrate) is preferably transparent or translucent.

Examples of the transparent or translucent electrode material may include electroconductive metal oxide films and translucent thin metal films. Specific examples may include a film prepared using an electroconductive material composed of indium oxide, zinc oxide, tin oxide, and complexes thereof such as indium tin oxide (ITO), and indium zinc oxide, NESA, gold, platinum, silver, and copper. Among these, ITO, indium zinc oxide, and tin oxide are preferred. Examples of a method for forming the electrode may include the vacuum deposition method, the sputtering method, the ion plating method, and the plating method.

As an electrode material, organic transparent electroconductive films such as polyaniline and derivatives thereof and polythiophene and derivatives thereof may be used. Furthermore, as the electrode material, metals and electroconductive polymers can be used. One of a pair of electrodes is preferably made of a material having a small work function. Examples may include metals such as lithium, sodium, potassium, rubidium, cesium, magnesium, calcium, strontium, barium, aluminum, scandium, vanadium, zinc, yttrium, indium, cerium, samarium, europium, terbium, and ytterbium, alloys of two or more thereof, alloys of one or more of the above metals and one or more of gold, silver, platinum, copper, manganese, titanium, cobalt, nickel, tungsten, and tin, and graphite and graphite interlayer compounds. Examples of the alloys may include a magnesium-silver alloy, a magnesium-indium alloy, a magnesium-aluminum alloy, an indium-silver alloy, a lithium-aluminum alloy, a lithium-magnesium alloy, a lithium-indium alloy, and a calcium-aluminum alloy.

As means for improving the photovoltaic efficiency, an additional intermediate layer other than the charge separation layer may be used in addition to the layer containing the polymer compound according to the present invention. Examples of a material used as the intermediate layer may include halides and oxides of alkali metals or alkaline earth metals such as lithium fluoride. Additional examples may include fine particles of inorganic semiconductor such as titanium oxide and PEDOT (poly-3,4-ethylenedioxythiophene).

<Usage of Cell>

When the photovoltaic cell according to the present invention is exposed to light such as sunlight on the side of the transparent or translucent electrode, photovoltaic power is generated between the electrodes so that it can be operated as an organic thin-film solar cell. A plurality of organic thin-film solar cells integrated can be used as an organic thin film solar cell module.

By being exposed to light on the side of the transparent or translucent electrode while applying or not applying a voltage between the electrodes, a photocurrent flows so that it can be operated as an organic optical sensor. A plurality of organic light sensors integrated can be used as an organic image sensor.

<Solar Cell Module>

The organic thin-film solar cell can have basically a similar module structure to a conventional solar cell module. In the solar cell module, a cell is usually formed on a supporting substrate such as a metal, ceramic, or the like and it is covered with a filling resin, a protective glass, or the like to capture light from the side opposite the supporting substrate. Alternatively, the cell is formed on the supporting substrate made of a transparent material such as reinforced glass to capture light from the transparent supporting substrate side. Specifically, module structures called a super straight type, a substrate type, and a potting type, and a substrate-integrated module structure used in amorphous silicon solar cells, or the like are known. The organic thin-film solar cell according to the present invention can select these module structures as needed, depending on a purpose of use, a place of use, and an environment.

A typical module of the superstrate type or the substrate type has a structure in which cells are arranged at a given interval between the supporting substrates each of which is transparent and subjected to an antireflection treatment on one side or on both sides thereof; adjacent cells are connected to each other by metal leads or flexible wiring; and a current collecting electrode is placed at an outer peripheral portion to allow the electric power thus generated to be taken to the outside. In order to protect the cells or improve current collecting efficiency, various plastic materials such as ethylene vinyl acetate (EVA) may be provided in the form of a film or a filling resin between the substrate and cells according to the purposes.

When the module is used in a place where the covering of the surface with a hard material is not required, for example, a place with less external impact, it is possible to form a surface protective layer from a transparent plastic film or cure the filling resin to impart a protective function thereto, thereby eliminating one of the supporting substrates.

The supporting substrate is fixed, at the periphery thereof, with a metal frame in a sandwich form so as to ensure sealing of the inside and rigidity of the module. The space between the supporting substrate and the frame is hermetically sealed with a sealing material. A solar cell can also be formed on a curved surface if the cell itself, the supporting substrate, the filling material, or the sealing material is made of a flexible material.

In a solar cell using a flexible substrate such as a polymer film, the cell body can be manufactured by sequentially forming unit cells while delivering a roll-shaped substrate, cutting into a desired size, and then sealing a peripheral portion with a flexible, moisture-resistant material. It is also possible to manufacture a module structure called “SCAF” described in “Solar Energy Materials and Solar Cells”, 48, p 383-391. Furthermore, a solar cell using a flexible substrate can also be used after being bonded and fixed to curved glass or the like.

EXAMPLES

The present invention will be described more specifically below based on the examples and comparative example, however, the present invention is not limited to the following examples.

The weight-average molecular weight (Mw) and the number-average molecular weight (Mn) of a polymer compound were determined as polystyrene-equivalent weight-average molecular weight and polystyrene-equivalent number-average molecular weight, respectively, by using gel permeation chromatography (GPC) (“HLC-8220GPC” manufactured by Tosoh Corporation). A sample to be measured was dissolved in tetrahydrofuran to give a concentration of about 0.5% by weight and 50 μL of the resulting solution was injected into GPC. Tetrahydrofuran was used as a mobile phase of GPC and was fed at a flow rate of 0.5 mL/min. Structural analysis of the polymer compound was conducted by ¹H-NMR analysis using a 300 MHz NMR spectrometer manufactured by Varian, Inc. The measurement was conducted after dissolving the sample in a deuterated solvent (a solvent in which a hydrogen atom, in the molecules thereof, has been substituted with a deuterium atom) capable of dissolving the sample therein so as to give a concentration of 20 mg/mL.

Example 1 Synthesis of Compound A

After a reaction vessel was purged with a nitrogen gas, 5-bromo-2-hydroxybenzoic acid (92.85 g), ethanol (1140 mL), and concentrated sulfuric acid (45 mL) were refluxed for 48 hours and concentrated under reduced pressure. To the mixture was added ethyl acetate, and the organic layer was washed with water and a 10% by weight aqueous sodium carbonate solution. The organic layer was dried over anhydrous sodium sulfate and concentrated under reduced pressure. The resultant crude product was purified with silica gel column chromatography to obtain a compound A (95.38 g, with a yield of 91%).

Example 2 Synthesis of Compound B

After a reaction vessel was purged with a nitrogen gas, the compound A (95.0 g), bis(pinacolato)diboron (108.5 g), [1,1′-bis(diphenylphosphino)ferrocene]palladium(II) dichloride dichloromethane adduct (3.3 g), 1,1′-bis(diphenylphosphino)ferrocene (2.2 g), potassium acetate (117.2 g), and 1,4-dioxane (1.3 L) were stirred at 105° C. for 22 hours. The resultant reaction mixture was filtered and washed with dioxane and toluene. The filtrate was concentrated under reduced pressure, and to the filtrate was added ethyl acetate (2 L). The mixture was washed with a saturated saline solution, and the organic layer was dried over anhydrous sodium sulfate and concentrated under reduced pressure. The resultant crude product was purified with silica gel column chromatography to obtain a compound B (90.1 g, 308 mmol).

Example 3 Synthesis of Compound C

After a reaction vessel was purged with a nitrogen gas, 1,5-dihydroxynaphthalene (15.0 g), triethylamine (28.5 g), and chloroform (150 mL) were mixed and cooled to 0° C. To the mixture was added dropwise trifluoromethanesulfonic anhydride (68.7 g), and the mixture was stirred for 1 hour. To the resultant reaction mixture were added water and chloroform, the aqueous layer was removed, and the organic layer was washed with water. The organic layer was dried over anhydrous sodium sulfate and concentrated under reduced pressure. The resultant solid was purified by recrystallization to obtain a compound C (31.46 g). In the following structural formula of the compound C, Tf represents a trifluoromethyl group.

Example 4 Synthesis of Compound D

After a reaction vessel was purged with a nitrogen gas, the compound B (16.90 g), the compound C (23.30 g), tetrakis(triphenylphosphine)palladium(0) (4.60 g), potassium phosphate (42.30 g), and 1,2-dimethoxyethane (340 mL) were stirred at 80° C. for 14 hours. The resultant reaction mixture was filtered and washed with chloroform and methanol. The filtrate was concentrated under reduced pressure and purified with silica gel column chromatography to obtain a compound D (8.85 g).

Example 5 Synthesis of Compound E

After a reaction vessel was purged with a nitrogen gas, the compound D (8.80 g), 2-[2-(2-methoxyethoxy)ethoxy]ethyl p-toluene sulfonate (12.52 g), dimethylformamide (380 mL), potassium carbonate (13.32 g), and 1,4,7,10,13,16-hexaoxacyclooctadecane (also referred to as “1,4,7,10,13,16-hexaoxacyclooctadecane” (also referred to as “18-crown-6”)) (1.02 g) were stirred at 100° C. for 23 hours. The resultant reaction mixture was added to water and extracted with ethyl acetate. The organic layer was washed with an aqueous sodium chloride solution, dried over anhydrous sodium sulfate, and concentrated under reduced pressure. The resultant crude product was purified with silica gel column chromatography to obtain a compound E (7.38 g).

Example 6 Synthesis of Compound F

After a reaction vessel was purged with a nitrogen gas, the compound E (5.53 g), bis(pinacolato)diboron (11.25 g), (1,5-cyclooctadiene)(methoxy)iridium(I) dimer (0.15 g, manufactured by Sigma-Aldrich Co.), 4,4′-di-tert-butyl-2,2′-dipyridyl (0.12 g, manufactured by Sigma-Aldrich Co.), and 1,4-dioxane (300 mL) were stirred at 110° C. for 19 hours. The resultant reaction mixture was concentrated under reduced pressure. The crude product was purified with silica gel column chromatography and then purified by recrystallization to obtain a compound F (5.81 g).

¹H NMR (400 MHz, CDCl₃, rt) δ (ppm) 1.27-1.41 (30H), 3.39 (6H), 3.57 (4H), 3.66-3.75 (8H), 3.83 (4H), 3.99 (4H), 4.27-4.42 (8H), 7.13 (2H), 7.60 (2H), 7.76 (2H), 7.93 (2H), 8.30 (2H).

Example 7 Synthesis of Compound G

After forming a nitrogen gas flow within a reaction vessel, 2,7-dibromo-9-fluorenone (121.9 g), catechol (883.1 g), 3-mercaptopropionic acid (4.87 g), and concentrated sulfuric acid (18.4 g) were mixed and stirred at 125° C. for 2 hours. The resultant mixture was left to be cooled and added to iced water, and the resultant solid was collected by filtration. The resultant solid was dissolved in ethanol, and the ethanol solution was added to hexane, and the resultant solid was collected by filtration to obtain a compound G (168.1 g)

Example 8 Synthesis of Compound H

After forming a nitrogen gas flow within a reaction vessel, the compound G (138.4 g), 2-[2-(2-methoxyethoxy)ethoxy]ethyl-p-toluene sulfonate (408.6 g), potassium carbonate (358.5 g), and acetonitrile (2.5 L) were mixed and refluxed under heating for 3 hours. After being left to be cooled, the resultant reaction mixture was filtered, and the filtrate was concentrated under reduced pressure and purified with silica gel column chromatography to obtain a compound H (109.4 g).

Example 9 Synthesis of Compound I

After a reaction vessel was purged with a nitrogen gas, the compound H (101.2 g) bis(pinacolato)diboron (53.1 g), [1,1′-bis(diphenylphosphino)ferrocene]dichloropalladium(II) dichloromethane complex (3.7 g), 1,1′-bis(diphenylphosphino)ferrocene (5.4 g), potassium acetate (90.6 g), and dioxane (900 mL) were mixed, heated to 110° C., and refluxed under heating for 8 hours. After being left to be cooled, the resultant reaction mixture was filtered, and the filtrate was concentrated under reduced pressure and purified with silica gel column chromatography to obtain a compound I (51.4 g).

Example 10 Synthesis of Polymer Compound A

After a reaction vessel was purged with an argon gas, the compound H (0.53 g), the compound F (0.43 g), dichlorobis(triphenylphosphine)palladium (0.3 mg), methyltrioctylammonium chloride (trade name “Aliquat 336” (registered trademark) manufactured by Sigma-Aldrich Co.) (5 mg), toluene (12 mL), and a 2 mol/L aqueous sodium carbonate solution (1 mL) were stirred at 105° C. for 9 hours. Phenylboronic acid (23 mg) was then added to the mixture, and the mixture was stirred at 105° C. for 14 hours. To the resultant reaction mixture were added sodium diethyldithiocarbamate trihydrate (0.40 g) and water (8 mL), and the mixture was stirred at 80° C. for 2 hours. The resultant mixture was added dropwise to methanol, and the precipitate was collected by filtration and dried. The resultant solid was dissolved in chloroform and purified with alumina and silica gel chromatography. The eluate was added dropwise to methanol, and the precipitate was collected by filtration and dried to obtain a polymer compound A (0.56 g). Polystyrene-equivalent number-average molecular weight of the polymer compound A was 3.4×10⁴. The polymer compound A is composed of a structural unit represented by Formula (A).

Example 11 Synthesis of Cesium Salt of Polymer Compound A (Conjugated Polymer Compound 1)

After a reaction vessel was purged with an argon gas, the polymer compound A (0.25 g), tetrahydrofuran (13 mL), methanol (6 mL), cesium hydroxide monohydrate (69 mg), and water (1 mL) were stirred at 65° C. for 6 hours. The resultant reaction mixture was concentrated and added dropwise to isopropanol, and the solid was collected by filtration and dried. To the resultant solid was added methanol, and the mixture was filtered. The filtrate was added dropwise to isopropanol, and the solid was collected by filtration and dried to obtain a conjugated polymer compound 1 (0.19 g). The conjugated polymer compound 1 is composed of a structural unit represented by Formula (B).

Example 12 Synthesis of Compound J

After a nitrogen gas flow was set within a reaction vessel, the compound F (2.00 g), copper bromide (2.22 g), N,N-dimethylformamide (40 mL), and water (24 mL) were mixed and stirred at 100° C. for 5 hours. After being left to be cooled, the resultant reaction mixture was collected by filtration, and the solid was collected and dried. The solid was dissolved in chloroform and filtered, and the filtrate was concentrated. The resultant solid was washed with methanol and acetone to obtain a compound J (1.55 g).

Example 13 Synthesis of Polymer Compound B

After a reaction vessel was purged with an argon gas, the compound F (0.29 g), the compound J (0.31 g), dichlorobis(triphenylphosphine)palladium (0.2 mg), methyltrioctylammonium chloride (trade name “Aliquat 336” (registered trademark) manufactured by Sigma-Aldrich Co.) (3.4 mg, manufactured by Sigma-Aldrich Co.), toluene (8 mL), and a 2 mol/L aqueous sodium carbonate solution (1.4 mL) were stirred at 105° C. for 6 hours. Phenylboronic acid (16.7 mg) was then added to the mixture, and the mixture was stirred at 105° C. for 14 hours. To the resultant reaction mixture were added sodium diethyldithiocarbamate trihydrate (0.3 g) and water (6 mL), and the mixture was stirred at 80° C. for 2 hours. The resultant mixture was concentrated and dried. The resultant solid was dissolved in chloroform and purified with alumina and silica gel chromatography. The eluate was added dropwise to methanol, and the precipitate was collected by filtration and dried to obtain a polymer compound B (0.36 g). Polystyrene-equivalent number-average molecular weight of the polymer compound B was 2.0×10⁴. The polymer compound B is composed of a structural unit represented by Formula (C).

Example 14 Synthesis of Cesium Salt of Polymer Compound B (Conjugated Polymer Compound 2)

After a reaction vessel was purged with an argon gas, the polymer compound B (0.15 g), tetrahydrofuran (8.6 mL), methanol (4.3 mL), cesium hydroxide monohydrate (9.4 mg), and water (0.8 mL) were stirred at 65° C. for 6 hours. The resultant reaction mixture was concentrated and added dropwise to isopropanol, and the solid was collected by filtration and dried. To the resultant solid was added methanol, and the mixture was filtered. The filtrate was added dropwise to isopropanol, and the solid was collected by filtration and dried to obtain a conjugated polymer compound 2 (0.14 g). The conjugated polymer compound 2 is composed of a structural unit represented by Formula (D).

Example 15 Synthesis of Polymer Compound C

After a reaction vessel was purged with an argon gas, the compound H (0.32 g), the compound F (0.26 g), N,N′-bis(4-bromophenyl)-N,N′-bis(4-tert-butyl-2,6-dimethylphenyl) 1,4-phenylenediamine (0.013 g), dichlorobis(triphenylphosphine)palladium (0.2 mg), methyltrioctylammonium chloride (trade name “Aliquat 336” (registered trademark) manufactured by Sigma-Aldrich Co.) (3.0 mg, manufactured by Sigma-Aldrich Co.), toluene (7 mL), and a 2 mol/L aqueous sodium carbonate solution (1.3 mL) were stirred at 105° C. for 9 hours. Phenylboronic acid (14.4 mg) was then added to the mixture, and the mixture was stirred at 105° C. for 14 hours. To the resultant reaction mixture were added sodium diethyldithiocarbamate trihydrate (0.3 g) and water (5 mL), and the mixture was stirred at 80° C. for 2 hours. The resultant mixture was added dropwise to methanol, and the precipitate was collected by filtration and dried. The solid was dissolved in chloroform and purified with alumina and silica gel chromatography. The eluate was added dropwise to methanol, and the precipitate was collected by filtration and dried to obtain a polymer compound C (0.32 g). Polystyrene-equivalent number-average molecular weight of the polymer compound B was 3.4×10⁴. The polymer compound C is composed of a structural unit represented by Formula (E).

N,N′-bis(4-bromophenyl)-N,N′-bis(4-tert-butyl-2,6-dimethylphenyl) 1,4-phenylenediamine can be synthesized according to a method described in, for example, Japanese Patent Application Laid-open No. 2008-749017.

Synthesis of Cesium Salt of Polymer Compound C (Conjugated Polymer Compound 3)

After a reaction vessel was purged with an argon gas, the polymer compound C (0.15 g), tetrahydrofuran (7.6 mL), methanol (3.8 mL), cesium hydroxide monohydrate (42 mg), and water (0.7 mL) were stirred at 65° C. for 6 hours. The resultant reaction mixture was concentrated and added dropwise to isopropanol, and the solid was collected by filtration and dried. To the resultant solid was added methanol, and the mixture was filtered. The filtrate was added dropwise to isopropanol, and the solid was collected by filtration and dried to obtain a conjugated polymer compound 3 (0.12 g). The conjugated polymer compound 3 is composed of a structural unit represented by Formula (F).

Reference Example 1 Synthesis of Polyurethane Sodium Salt (Non-Conjugated Polymer Compound 1)

After a reaction vessel was purged with a nitrogen gas, 1,3-butanediol (1.0 g), dibutyltin dilaurate (7.5 mg), and dimethylolpropionic acid (0.5 g) were put in a 100 mL flask. DMF (50 mL) was added to the mixture, and the mixture was stirred at 90° C. for 30 minutes. To the mixture was then added isophorone diisocyanate (3.3 g), and the mixture was heated at 90° C. for 3 hours. A solution containing a polymer compound obtained in this stage was subjected to GPC measurement according to the above-described method to measure the molecular weight of the polymer compound. Polystyrene-equivalent number-average molecular weight of the polymer compound was 1.9×10³, and polystyrene-equivalent weight-average molecular weight of the polymer compound was 3.0×10³. The resultant reaction solution was cooled to 60° C. and neutralized through the addition of a 1M aqueous sodium hydroxide solution. The reaction solution was further stirred at 60° C. further for 1 hour, and the solvent was distilled off from the reaction solution to obtain a white solid (2.0 g). The resultant white solid is referred to as a non-conjugated polymer compound 1. The non-conjugated polymer compound 1 is composed of a structural unit represented by Formula (I).

Example 17 Preparation of Electroluminescent Device 1

Onto an ITO anode (thickness: 45 nm), which had been patterned for film formation on the surface of a glass substrate, a solution of a hole injection material was applied to form a hole injection layer with a film thickness of 60 nm by the spin coating method. The glass substrate on which the hole injection layer had been formed was heated at 200° C. for 10 minutes under a nitrogen atmosphere (in a nitrogen atmosphere) to insolubilize the hole injection layer. The resulting substrate was left to be cooled to room temperature to obtain a substrate having the hole injection layer thereon.

As the solution of the hole injection material, AQ-1200, which is a polythiophene/sulfonic acid-based hole injection material purchased from Plextronics, Inc., was used.

Next, a hole-transporting polymer material and xylene were mixed to obtain a composition for forming a hole transport layer containing a 0.7% by weight hole-transporting polymer material.

The hole-transporting polymer material was synthesized according to the following process.

After making the gas within a reaction vessel an inert gas atmosphere, 2,7-dibromo-9,9-di(octyl)-fluorene (1.4 g), 2,7-bis(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-9,9-di(octyl)fluorene (6.4 g), N,N′-bis(4-bromophenyl)-N,N′-bis(4-butylphenyl)-1,4-phenylenediamine (4.1 g), bis(4-bromophenyl)benzocyclobutene amine (0.6 g), tetraethylammonium hydroxide (1.7 g), palladium acetate (4.5 mg), tri(2-methoxyphenyl)phosphine (0.03 g), and toluene (100 mL) were mixed, and the resultant mixture was stirred at 100° C. for 2 hours. To the mixture was then added phenylboronic acid (0.06 g), and the resultant mixture was stirred for 10 hours. After being left to be cooled, the aqueous layer was removed. After adding an aqueous sodium diethyldithiocarbamate solution and stirring the mixture, the aqueous layer was removed, and the organic layer was washed with water and a 3% by volume aqueous acetic acid solution. After pouring the organic layer into methanol to precipitate a solid, the solid collected by filtration was dissolved in toluene again and passed through a silica gel column and an alumina column. The eluted toluene solution containing the solid was collected. The collected toluene solution was poured into methanol to precipitate the solid. The precipitated solid was collected by filtration and vacuum dried at 50° C. to obtain a hole-transporting polymer material. Polystyrene-equivalent weight-average molecular weight of the hole-transporting polymer material was 3.0×10⁵.

Onto the hole injection layer of the substrate on which the hole injection layer had been formed obtained as described above, the composition for forming a hole transport layer was applied by the spin coating method to form an applied film with a thickness of 20 nm. The substrate having the applied film was heated at 180° C. for 60 minutes under a nitrogen atmosphere (in a nitrogen atmosphere) to insolubilize the applied film. The substrate was then left to be cooled to room temperature to obtain a substrate having the hole transport layer thereon.

Next, a light-emitting polymer material and xylene were mixed to obtain a composition for forming a light-emitting layer containing a 1.4% by weight light-emitting polymer material.

The light-emitting polymer material was synthesized according to the following process.

After making the gas within a reaction vessel an inert gas atmosphere, 2,7-dibromo-9,9-di(octyl)-fluorene (9.0 g), N,N′-bis(4-bromophenyl)-N,N′-bis(4-tert-butyl-2,6-dimethylphenyl) 1,4-phenylenediamine (1.3 g), 2,7-bis(4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-yl)-9,9-di(4-hexyphenyl)fluorene (13.4 g), tetraethylammonium hydroxide (43.0 g), palladium acetate (8 mg), tri(2-methoxyphenyl)phosphine (0.05 g), and toluene (200 mL) were mixed, and the resultant mixture was stirred at 90° C. for 8 hours. To the mixture was then added phenylboronic acid (0.22 g), and the resultant mixture was stirred for 14 hours. After being left to be cooled, the aqueous layer was removed. After adding an aqueous sodium diethyldithiocarbamate solution and stirring the mixture, the aqueous layer was removed, and the organic layer was washed with water and a 3% by volume aqueous acetic acid solution. After pouring the organic layer into methanol to precipitate a solid, the solid collected by filtration was dissolved in toluene again and passed through a silica gel column and an alumina column. The eluted toluene solution containing the solid was collected. The collected toluene solution was poured into methanol to precipitate the solid. The precipitated solid was vacuum dried at 50° C. to obtain a light-emitting polymer material (12.5 g). According to gel permeation chromatography, polystyrene-equivalent weight-average molecular weight of the obtained light-emitting polymer material was 3.1×10⁵.

Onto the hole transport layer of the substrate on which the hole transport layer had been formed obtained as described above, the composition for forming a light-emitting layer was applied by the spin coating method to form an applied film with a thickness of 80 nm. The substrate having the applied film was heated at 130° C. for 10 minutes in a nitrogen atmosphere to evaporate the solvent and left to be cooled to room temperature to obtain a substrate having the light-emitting layer thereon.

Methanol and the conjugated polymer compound 1 were mixed to obtain a solution containing a 0.2% by weight conjugated polymer compound 1. Onto the light-emitting layer of the substrate on which the light-emitting layer had been formed as described above, the solution was applied by the spin coating method to obtain an applied film with a thickness of 10 nm. The substrate having the applied film was heated at 130° C. for 10 minutes in a nitrogen atmosphere to evaporate the solvent and left to be cooled to room temperature to obtain a substrate having the conjugated polymer compound 1.

The substrate having the layer containing the conjugated polymer compound 1 obtained as described above was inserted into a vacuum deposition apparatus, and an Al film with a thickness of 80 nm was formed on the layer by the vacuum deposition method to form a cathode. Thus, a layered structure 1 was prepared.

The layered structure 1 thus prepared was taken out of the vacuum deposition apparatus and sealed with a sealing glass and a two-part mixing type epoxy resin in a nitrogen atmosphere to obtain an electroluminescent device 1.

Example 18 Preparation of Electroluminescent Device 2

An electroluminescent device 2 was obtained in the same manner as Example 17 except that the conjugated polymer compound 2 was used in place of the conjugated polymer compound 1 in Example 17.

Example 19 Preparation of Electroluminescent Device 3

An electroluminescent device 3 was obtained in the same manner as Example 17 except that the conjugated polymer compound 3 was used in place of the conjugated polymer compound 1 in Example 17.

Example 20 Preparation of Electroluminescent Device 4

An electroluminescent device 4 was obtained in the same manner as Example 17 except that Ag was used in place of Al in Example 17.

Example 21 Preparation of Electroluminescent Device 5

An electroluminescent device 5 was obtained in the same manner as Example 17 except that Au was used in place of Al in Example 17.

Comparative Example 1 Preparation of Electroluminescent Device C1

An electroluminescent device C1 was obtained in the same manner as Example 17 except that the cathode was directly formed without forming the layer containing the conjugated polymer compound 1 in Example 17.

Comparative Example 2 Preparation of Electroluminescent Device C2

An electroluminescent device C2 was obtained in the same manner as Example 20 except that the cathode was directly formed without forming the layer containing the conjugated polymer compound 1 in Example 20.

Comparative Example 3 Preparation of Electroluminescent Device C3

An electroluminescent device C3 was obtained in the same manner as Example 21 except that the cathode was directly formed without forming the layer containing the conjugated polymer compound 1 in Example 21.

Comparative Example 4 Preparation of Electroluminescent Device C4

An electroluminescent device C4 was obtained in the same manner as Example 17 except that the non-conjugated polymer compound 1 was used in place of the conjugated polymer compound 1 in Example 17.

MEASUREMENT

A forward voltage of 10 V was applied to the electroluminescent devices 1 to 5 and C1 to C4 obtained as described above to measure light-emitting brightness and light-emitting efficiency. The results are indicated in Table 1.

TABLE 1 Light- Light- emitting emitting polymer brightness efficiency compound Cathode (cd/m²) (cd/A) Example 17 Conjugated Al 4222.1 3.98 (Electroluminescent polymer device 1) compound 1 Example 18 Conjugated Al 4709.0 5.82 (Electroluminescent polymer device 2) compound 2 Example 19 Conjugated Al 3560.5 5.36 (Electroluminescent polymer device 3) compound 3 Example 20 Conjugated Ag 170.7 1.27 (Electroluminescent polymer device 4) compound 1 Example 21 Conjugated Au 8.18 0.07 (Electroluminescent polymer device 5) compound 1 Comparative Example 1 Absent Al 1.5 0.01 (Electroluminescent device C1) Comparative Example 2 Absent Ag 12.8 0.5 (Electroluminescent device C2) Comparative Example 3 Absent Au Light was Light was (Electroluminescent not not device C3) emitted emitted Comparative Example 4 Non- Al 0.7 0.01 (Electroluminescent conjugated device C4) polymer compound 1 

1. An electronic device including a layer comprising a polymer compound comprising one or more structural units selected from the group consisting of a structural unit represented by formula (1) and a structural unit represented by formula (14) as a charge injection layer and/or a charge transport layer, wherein the structural unit represented by formula (1) is:

wherein Ar¹ represents a (2+m1+m2)-valent fused polycyclic aromatic group that optionally has a substituent; R¹ represents a group represented by formula (2) or formula (3); R² represents a group represented by formula (4); m1 represents an integer of 1 or more; m2 represents an integer of 1 or more; when R¹ and R² are each plurally present, they each may be the same or different; and a hydrogen atom in formula (1) may be replaced with a substituent other than R¹ or R²; wherein the group represented by formula (2) is: —R³-{(Q¹)_(n1)-Y¹(M¹)_(a1)(Z¹)_(b1)}_(m3)  (2) wherein R³ represents a single bond, or a (1+m3)-valent organic group that optionally has a substituent; Q¹ represents a divalent organic group; Y¹ represents —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, —PO₃ ²⁻ or —B(R^(α))₃ ⁻; M¹ represents a metallic cation, or represents an ammonium cation that optionally has a substituent; Z¹ represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(a))₄ ⁻, R^(a)SO₃ ⁻, R^(a)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; n1 represents an integer of 0 or more; a1 represents an integer of 1 or more, and b1 represents an integer of 0 or more, wherein a1 and b1 are selected such that a charge of the group represented by formula (2) is zero; R^(α) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; R^(a) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m3 represents an integer of 1 or more, and when R³ is a single bond, m3 represents 1; and when Q¹, Y¹, M¹, Z¹, n1, a1 and b1 are each plurally present, they each may be the same or different; wherein the group represented by formula (3) is: —R⁴-{(Q²)_(n2)-Y²(M²)_(a2)(Z²)_(b2)}_(m4)  (3) wherein R⁴ represents a single bond, or a (1+m4)-valent organic group that optionally has a substituent; Q² represents a divalent organic group; Y² represents a carbocation, an ammonium cation, a phosphonium cation, a sulfonium cation, or an iodonium cation; M² represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(b))₄ ⁻, R^(b)SO₃ ⁻, R^(b)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; Z² represents a metallic cation, or represents an ammonium cation that optionally has a substituent; n2 represents an integer of 0 or more; a2 represents an integer of 1 or more, and b2 represents an integer of 0 or more, wherein a2 and b2 are selected such that a charge of the group represented by formula (3) is zero; R^(b) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m4 represents an integer of 1 or more, and when R⁴ is a single bond, m4 represents 1; and when Q², Y², M², Z², n2, a2 and b2 are each plurally present, they each may be the same or different; wherein the group represented by formula (4) is: —R⁵-{(Q³)_(n3)-Y³}_(m5)  (4) wherein R⁵ represents a single bond, or a (1+m5)-valent organic group that optionally has a substituent; Q³ represents a divalent organic group; Y³ represents a cyano group, or a group represented by any one of formulae (5) to (13); n3 represents an integer of 0 or more; m5 represents an integer of 1 or more, and when R⁵ is a single bond, m5 is 1; and when Q³, Y³ and n3 are each plurally present, they each may be the same or different; wherein the group represented by any one of formulae (5) to (13) is: —O—(R′O)_(a3)—R″  (5)

—S—(R′S)_(a4)—R″  (7) —C(═O)—(R′—C(═O))_(a4)—R″  (8) —C(═S)—(R′—C(═S))_(a4)—R″  (9) —N{(R′)_(a4)R″}₂  (10) —C(═O)O—(R′—C(═O)O)_(a4)—R″  (11) —C(═O)O—(R′O)_(a4)—R″  (12) —NHC(═O)—(R′NHC(═O))_(a4)—R″  (13) wherein R′ represents a divalent hydrocarbon group that optionally has a substituent; R″ represents a hydrogen atom, a monovalent hydrocarbon group that optionally has a substituent, a carboxyl group, a sulfo group, a hydroxy group, a mercapto group, —NR^(C) ₂, a cyano group or —C(═O)NR^(c) ₂; R′″ represents a trivalent hydrocarbon group that optionally has a substituent; a3 represents an integer of 1 or more; a4 represents an integer of 0 or more; R^(c) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; and when R′, R″ and R′″ are each plurally present, they each may be the same or different; and wherein the structural unit represented by formula (14) is:

wherein Ar² represents a (2+m6+m7)-valent fused polycyclic aromatic group that optionally has a substituent; R⁶ represents a group represented by formula (15) or formula (16); R⁷ represents the group represented by formula (4); m6 represents an integer of 1 or more; m7 represents an integer of 0 or more; when R⁶ and R⁷ are each plurally present, they each may be the same or different; and a hydrogen atom in formula (14) may be replaced with a substituent other than R⁶ or R⁷; wherein the group represented by formula (15) is:

wherein R⁸ represents a (1+m8+m9)-valent organic group that optionally has a substituent; Q¹, Q³, Y¹, Y³, M¹, Z¹, n1, n3, a1 and b1 are the same as the corresponding definitions above; m8 and m9 each independently represent an integer of 1 or more; and when Q¹, Q³, Y¹, Y³, M¹, Z¹, n1, n3, a1 and b1 are each plurally present, they each may be the same or different; wherein the group represented by formula (16) is:

wherein R⁹ represents a (1+m10+m11)-valent organic group that optionally has a substituent; Q², Q³, Y², M², Z², n2, n3, a2 and b2 are the same as the corresponding definitions above; m10 and m11 each independently represent an integer of 1 or more; and when Q², Q³, Y², Y³, M², Z², n2, n3, a2 and b2 are each plurally present, they each may be the same or different.
 2. The electronic device according to claim 1, wherein the (2+m1+m2)-valent fused polycyclic aromatic group that optionally has a substituent which is represented by Ar¹ is a group remaining after removing (2+m1+m2) hydrogen atoms from a ring represented by any one of the following formulae:


3. The electronic device according to claim 1, wherein the (2+m6+m7)-valent fused polycyclic aromatic group that optionally has a substituent which is represented by Ar² is a group remaining after removing (2+m6+m7) hydrogen atoms from a ring represented by any one of the following formulae:


4. The electronic device according to claim 1, wherein the layer comprising the polymer compound is an electron injection layer and/or an electron transport layer.
 5. The electronic device according to claim 1, which is an electroluminescent device.
 6. A polymer compound comprising one or more structural units selected from the group consisting of a structural unit represented by formula (1) and a structural unit represented by formula (14), wherein the structural unit represented by formula (1) is:

wherein Ar¹ represents a (2+m1+m2)-valent fused polycyclic aromatic group that optionally has a substituent; R¹ represents a group represented by formula (2) or formula (3); R² represents a group represented by formula (4); m1 represents an integer of 1 or more; m2 represents an integer of 1 or more; when R¹ and R² are each plurally present, they each may be the same or different; and a hydrogen atom in formula (1) may be replaced with a substituent other than R¹ or R²; wherein the group represented by formula (2) is: —R³-{(Q¹)_(n1)-Y¹(M¹)_(a1)(Z1)_(b1)}_(m3)  (2) wherein R³ represents a single bond, or a (1+m3)-valent organic group that optionally has a substituent; Q¹ represents a divalent organic group; Y¹ represents —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, —PO₃ ²⁻ or —B(R^(α))₃ ⁻; M¹ represents a metallic cation, or represents an ammonium cation that optionally has a substituent; Z¹ represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(a))₄ ⁻, R^(a)SO₃ ⁻, R^(a)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; n1 represents an integer of 0 or more; a1 represents an integer of 1 or more, and b1 represents an integer of 0 or more, wherein a1 and b1 are selected such that a charge of the group represented by formula (2) is zero; R^(α) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; R^(a) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m3 represents an integer of 1 or more, and when R³ is a single bond, m3 represents 1; and when Q¹, Y¹, M¹, Z¹, n1, a1 and b1 are each plurally present, they each may be the same or different; wherein the group represented by formula (3) is: —R⁴-{(Q²)_(n2)-Y²(M²)_(a2)(Z²)_(b2)}_(m4)  (3) wherein R⁴ represents a single bond, or a (1+m4)-valent organic group that optionally has a substituent; Q² represents a divalent organic group; Y² represents a carbocation, an ammonium cation, a phosphonium cation, a sulfonium cation, or an iodonium cation; M² represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(b))₄ ⁻, R^(b)SO₃ ⁻, R^(b)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; Z² represents a metallic cation, or represents an ammonium cation that optionally has a substituent; n2 represents an integer of 0 or more; a2 represents an integer of 1 or more, and b2 represents an integer of 0 or more, wherein a2 and b2 are selected such that a charge of the group represented by formula (3) is zero; R^(b) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m4 represents an integer of 1 or more, and when R⁴ is a single bond, m4 represents 1; and when Q², Y², M², Z², n2, a2 and b2 are each plurally present, they each may be the same or different; wherein the group represented by formula (4) is: —R⁵-{(Q³)_(n3)-Y³}_(m5)  (4) wherein R⁵ represents a single bond, or a (1+m5)-valent organic group that optionally has a substituent; Q³ represents a divalent organic group; Y³ represents a cyano group, or a group represented by any one of formulae (5) to (13); n3 represents an integer of 0 or more; m5 represents an integer of 1 or more, and when R⁵ is a single bond, m5 is 1; and when Q³, Y³ and n3 are each plurally present, they each may be the same or different; wherein the group represented by any one of formulae (5) to (13) is: —O—(R′O)_(a3)—R″  (5)

—S—(R′S)_(a4)—R″  (7) —C(═O)—(R′—C(═O))_(a4)—R″  (8) —C(═S)—(R′—C(═S))_(a4)—R″  (9) —N{(R′)_(a4)R″}₂  (10) —C(═O)O—(R′—C(═O)O)_(a4)—R″  (11) —C(═O)O—(R′O)_(a4)—R″  (12) —NHC(═O)—(R′NHC(═O))_(a4)—R″  (13) wherein R′ represents a divalent hydrocarbon group that optionally has a substituent; R″ represents a hydrogen atom, a monovalent hydrocarbon group that optionally has a substituent, a carboxyl group, a sulfo group, a hydroxy group, a mercapto group, —NR^(C) ₂, a cyano group or —C(═O)NR^(c) ₂; R′″ represents a trivalent hydrocarbon group that optionally has a substituent; a3 represents an integer of 1 or more; a4 represents an integer of 0 or more; R^(c) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; and when R′, R″ and R′″ are each plurally present, they each may be the same or different; and wherein the structural unit represented by formula (14) is:

wherein Ar² represents a (2+m6+m7)-valent fused polycyclic aromatic group that optionally has a substituent; R⁶ represents a group represented by formula (15) or formula (16); R⁷ represents the group represented by formula (4); m6 represents an integer of 1 or more; m7 represents an integer of 0 or more; when R⁶ and R⁷ are each plurally present, they each may be the same or different; and a hydrogen atom in formula (14) may be replaced with a substituent other than R⁶ or R⁷; wherein the group represented by formula (15) is:

wherein R⁸ represents a (1+m8+m9)-valent organic group that optionally has a substituent; Q¹, Q³, Y¹, Y³, M¹, Z¹, n1, n3, a1 and b1 are the same as the corresponding definitions above; m8 and m9 each independently represent an integer of 1 or more; and when Q¹, Q³, Y¹, Y³, M¹, Z¹, n1, n3, a1 and b1 are each plurally present, they each may be the same or different; wherein the group represented by formula (16) is:

wherein R⁹ represents a (1+m10+m11)-valent organic group that optionally has a substituent; Q², Q³, Y², Y³, M², Z², n2, n3, a2 and b2 are the same as the corresponding definitions above; m10 and m11 each independently represent an integer of 1 or more; and when Q², Q³, Y², Y³, M², Z², n2, n3, a2 and b2 are each plurally present, they each may be the same or different.
 7. The polymer compound according to claim 6, wherein the (2+m1+m2)-valent fused polycyclic aromatic group that optionally has a substituent which is represented by Ar¹ is a group remaining after removing (2+m1+m2) hydrogen atoms from a ring represented by any one of the following formulae:


8. The polymer compound according to claim 6, wherein the (2+m6+m7)-valent fused polycyclic aromatic group that optionally has a substituent which is represented by Ar² is a group remaining after removing (2+m6+m7) hydrogen atoms from a ring represented by any one of the following formulae:


9. An organic compound represented by formula (17):

wherein Ar³ represents a (2+m12+m13)-valent fused polycyclic aromatic group that optionally has a substituent; R¹⁰ represents a group represented by formula (2) or formula (3), or a group represented by formula (18) or formula (19); R¹¹ represents a group represented by formula (4); m12 and m13 each independently represent an integer of 1 or more; X¹ and X² each independently represent a group involved in a condensation polymerization; when R¹⁰ and R¹¹ are each plurally present, they each may be the same or different; and a hydrogen atom in formula (17) may be replaced with a substituent other than R¹⁰ or R¹¹; wherein the group represented by formula (2) is: —R³-{(Q¹)_(n1)-Y¹(M¹)_(a1)(Z¹)_(b1)}m3  (2) wherein R³ represents a single bond, or a (1+m3)-valent organic group that optionally has a substituent; Q¹ represents a divalent organic group; Y¹ represents —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, —PO₃ ²⁻ or —B(R^(α))₃ ⁻; M¹ represents a metallic cation, or represents an ammonium cation that optionally has a substituent; Z¹ represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(a))₄ ⁻, R^(a)SO₃ ⁻, R^(a)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; n1 represents an integer of 0 or more; a1 represents an integer of 1 or more, and b1 represents an integer of 0 or more, wherein a1 and b1 are selected such that a charge of the group represented by formula (2) is zero; R^(α) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; R^(a) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m3 represents an integer of 1 or more, and when R³ is a single bond, m3 represents 1; and when Q¹, Y¹, M¹, Z¹, n1, a1 and b1 are each plurally present, they each may be the same or different; wherein the group represented by formula (3) is: —R⁴-{(Q²)_(n2)-Y²(M²)_(a2)(Z²)_(b2)}_(m4)  (3) wherein R⁴ represents a single bond, or a (1+m4)-valent organic group that optionally has a substituent; Q² represents a divalent organic group; Y² represents a carbocation, an ammonium cation, a phosphonium cation, a sulfonium cation, or an iodonium cation; M² represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(b))₄ ⁻, R^(b)SO₃ ⁻, R^(b)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; Z² represents a metallic cation, or represents an ammonium cation that optionally has a substituent; n2 represents an integer of 0 or more; a2 represents an integer of 1 or more, and b2 represents an integer of 0 or more, wherein a2 and b2 are selected such that a charge of the group represented by formula (3) is zero; R^(b) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m4 represents an integer of 1 or more, and when R⁴ is a single bond, m4 represents 1; and when Q², Y², M², Z², n2, a2 and b2 are each plurally present, they each may be the same or different; wherein the group represented by formula (18) is: —R¹²-{(Q⁴)_(n4)-Y⁴}_(m14)  (18) wherein R¹² represents a single bond, or a (1+m14)-valent organic group that optionally has a substituent; Q⁴ represents a divalent organic group; Y⁴ represents —CO₂R^(χ), —SO₃R^(χ), —SO₂R^(χ), —PO₃(R^(χ))₂ or —B(R^(χ))₂; n4 represents an integer of 0 or more; R^(χ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m14 represents an integer of 1 or more, and when R¹² is a single bond, m14 represents 1; and when Q⁴, Y⁴, n4 and R^(χ) are each plurally present, they each may be the same or different; wherein the group represented by formula (19) is: —R¹³-{(Q⁵)_(n5)-Y⁵}_(m15)  (19) wherein R¹³ represents a single bond, or a (1+m15)-valent organic group that optionally has a substituent; Q⁵ represents a divalent organic group; Y⁵ represents a halogenated alkyl group, a halogen atom, —N(R^(δ))₂, —P(R^(δ))₂ or —SR^(δ); n5 represents an integer of 0 or more; R^(δ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m15 represents an integer of 1 or more, and when R¹³ is a single bond, m15 represents 1; and when Q⁵, Y⁵, n5 and R^(δ) are each plurally present, they each may be the same or different; wherein the group represented by formula (4) is: —R⁵-{(Q³)_(n3)-Y³}_(m5)  (4) wherein R⁵ represents a single bond, or a (1+m5)-valent organic group that optionally has a substituent; Q³ represents a divalent organic group; Y³ represents a cyano group, or a group represented by any one of formulae (5) to (13); n3 represents an integer of 0 or more; m5 represents an integer of 1 or more, and when R⁵ is a single bond, m5 is 1; and when Q³, Y³ and n3 are each plurally present, they each may be the same or different; wherein the group represented by any one of formulae (5) to (13) is: —O—(R′O)_(a3)—R″  (5)

—S—(R′S)_(a4)—R″  (7) —C(═O)—(R′—C(═O))_(a4)—R″  (8) —C(═S)—(R′—C(═S))_(a4)—R″  (9) —N{(R′)_(a4)R″}₂  (10) —C(═O)O—(R′—C(═O)O)_(a4)—R″  (11) —C(═O)O—(R′O)_(a4)—R″  (12) —NHC(═O)—(R′NHC(═O))_(a4)—R″  (13) wherein R′ represents a divalent hydrocarbon group that optionally has a substituent; R″ represents a hydrogen atom, a monovalent hydrocarbon group that optionally has a substituent, a carboxyl group, a sulfo group, a hydroxy group, a mercapto group, —NR^(C) ₂, a cyano group or —C(═O)NR^(c) ₂; R′″ represents a trivalent hydrocarbon group that optionally has a substituent; a3 represents an integer of 1 or more; a4 represents an integer of 0 or more; R^(c) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; and when R′, R″ and R′″ are each plurally present, they each may be the same or different.
 10. A method of producing a polymer compound comprising a structural unit represented by formula (1), which includes polymerizing an organic compound represented by formula (17A) to obtain the polymer compound comprising the structural unit represented by formula (1), wherein the organic compound represented by formula (17A) is:

wherein R^(10′) represents a group represented by formula (2) or formula (3); Ar³ represents a (2+m12+m13)-valent fused polycyclic aromatic group that optionally has a substituent; R¹¹ represents a group represented by formula (4); m12 and m13 each independently represent an integer of 1 or more; X¹ and X² each independently represent a group involved in a condensation polymerization; when R^(10′) and R¹¹ are each plurally present, they each may be the same or different; and a hydrogen atom in formula (17A) may be replaced with a substituent other than R^(10′) or R¹¹; wherein the group represented by formula (2) is: —R³-{(Q¹)_(n1)-Y¹(M¹)_(a1)(Z¹)_(b1)}_(m3)  (2) wherein R³ represents a single bond, or a (1+m3)-valent organic group that optionally has a substituent; Q¹ represents a divalent organic group; Y¹ represents —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, —PO₃ ²⁻ or —B(R^(α))₃ ⁻; M¹ represents a metallic cation, or represents an ammonium cation that optionally has a substituent; Z¹ represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(a))₄ ⁻, R^(a)SO₃ ⁻, R^(a)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; n1 represents an integer of 0 or more; a1 represents an integer of 1 or more, and b1 represents an integer of 0 or more, wherein a1 and b1 are selected such that a charge of the group represented by formula (2) is zero; R^(α) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; R^(a) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m3 represents an integer of 1 or more, and when R³ is a single bond, m3 represents 1; and when Q¹, Y¹, M¹, Z¹, n1, a1 and b1 are each plurally present, they each may be the same or different; wherein the group represented by formula (3) is: —R⁴-{(Q²)_(n2)-Y²(M²)_(a2)(Z²)_(b2)}_(m4)  (3) wherein R⁴ represents a single bond, or a (1+m4)-valent organic group that optionally has a substituent; Q² represents a divalent organic group; Y² represents a carbocation, an ammonium cation, a phosphonium cation, a sulfonium cation, or an iodonium cation; M² represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(b))₄ ⁻, R^(b)SO₃ ⁻, R^(b)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; Z² represents a metallic cation, or represents an ammonium cation that optionally has a substituent; n2 represents an integer of 0 or more; a2 represents an integer of 1 or more, and b2 represents an integer of 0 or more, wherein a2 and b2 are selected such that a charge of the group represented by formula (3) is zero; R^(b) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m4 represents an integer of 1 or more, and when R⁴ is a single bond, m4 represents 1; and when Q², Y², M², Z², n2, a2 and b2 are each plurally present, they each may be the same or different; wherein the group represented by formula (4) is: —R⁵-{(Q³)_(n3)-Y³}_(m5)  (4) wherein R⁵ represents a single bond, or a (1+m5)-valent organic group that optionally has a substituent; Q³ represents a divalent organic group; Y³ represents a cyano group, or a group represented by any one of formulae (5) to (13); n3 represents an integer of 0 or more; m5 represents an integer of 1 or more, and when R⁵ is a single bond, m5 is 1; and when Q³, Y³ and n3 are each plurally present, they each may be the same or different; wherein the group represented by any one of formulae (5) to (13) is: —O—(R′O)_(a3)—R″  (5)

—S—(R′S)_(a4)—R″  (7) —C(═O)—(R′—C(═O))_(a4)—R″  (8) —C(═S)—(R′—C(═S))_(a4)—R″  (9) —N{(R′)_(a4)R″}₂  (10) —C(═O)O—(R′—C(═O)O)_(a4)—R″  (11) —C(═O)O—(R′O)_(a4)—R″  (12) —NHC(═O)—(R′NHC(═O))_(a4)—R″  (13) wherein R′ represents a divalent hydrocarbon group that optionally has a substituent; R″ represents a hydrogen atom, a monovalent hydrocarbon group that optionally has a substituent, a carboxyl group, a sulfo group, a hydroxy group, a mercapto group, —NR^(C) ₂, a cyano group or —C(═O)NR^(c) ₂; R′″ represents a trivalent hydrocarbon group that optionally has a substituent; a3 represents an integer of 1 or more; a4 represents an integer of 0 or more; R^(c) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; and when R′, R″ and R′″ are each plurally present, they each may be the same or different; and wherein the structural unit represented by formula (1) is:

wherein Ar¹ represents a (2+m1+m2)-valent fused polycyclic aromatic group that optionally has a substituent; R¹ represents the group represented by formula (2) or formula (3); R² represents the group represented by formula (4); m1 represents an integer of 1 or more; m2 represents an integer of 1 or more; when R¹ and R² are each plurally present, they each may be the same or different; and a hydrogen atom in formula (1) may be replaced with a substituent other than R¹ or R².
 11. A method of producing a polymer compound comprising a structural unit represented by formula (1), which includes: (i) polymerizing an organic compound represented by formula (17B) to obtain a polymer compound comprising a structural unit represented by formula (17B′); (ii) ionizing the polymer compound comprising the structural unit represented by formula (17B′) to obtain the polymer compound comprising the structural unit represented by formula (1), wherein the organic compound represented by formula (17B) is:

wherein R^(10″) represents a group represented by formula (18) or formula (19); Ar³ represents a (2+m12+m13)-valent fused polycyclic aromatic group that optionally has a substituent; R¹¹ represents a group represented by formula (4); m12 and m13 each independently represent an integer of 1 or more; X¹ and X² each independently represent a group involved in a condensation polymerization; when R^(10″) and R¹¹ are each plurally present, they each may be the same or different; and a hydrogen atom in formula (17B) may be replaced with a substituent other than R^(10″) or R¹¹; wherein the group represented by formula (18) is: —R¹²-{(Q⁴)_(n4)-Y⁴}_(m14)  (18) wherein R¹² represents a single bond, or a (1+m14)-valent organic group that optionally has a substituent; Q⁴ represents a divalent organic group; Y⁴ represents —CO₂R^(χ), —SO₃R^(χ), —SO₂R^(χ), —PO₃(R^(χ))₂ or —B(R^(χ))₂; n4 represents an integer of 0 or more; R^(χ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m14 represents an integer of 1 or more, and when R¹² is a single bond, m14 represents 1; and when Q⁴, Y⁴, n4 and R^(χ) are each plurally present, they each may be the same or different; wherein the group represented by formula (19) is: —R¹³-{(Q⁵)_(n5)-Y⁵}_(m15)  (19) wherein R¹³ represents a single bond, or a (1+m15)-valent organic group that optionally has a substituent; Q⁵ represents a divalent organic group; Y⁵ represents a halogenated alkyl group, a halogen atom, —N(R^(δ))₂, —P(R^(δ))₂ or —SR^(δ); n5 represents an integer of 0 or more; R^(δ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m15 represents an integer of 1 or more, and when R¹³ is a single bond, m15 represents 1; and when Q⁵, Y⁵, n5 and R^(δ) are each plurally present, they each may be the same or different; wherein the group represented by formula (4) is: —R⁵-{(Q³)_(n3)-Y³}_(m5)  (4) wherein R⁵ represents a single bond, or a (1+m5)-valent organic group that optionally has a substituent; Q³ represents a divalent organic group; Y³ represents a cyano group, or a group represented by any one of formulae (5) to (13); n3 represents an integer of 0 or more; m5 represents an integer of 1 or more, and when R⁵ is a single bond, m5 is 1; and when Q³, Y³ and n3 are each plurally present, they each may be the same or different; wherein the group represented by any one of formulae (5) to (13) is: —O—(R′O)_(a3)—R″  (5)

—S—(R′S)_(a4)—R″  (7) —C(═O)—(R′—C(═O))_(a4)—R″  (8) —C(═S)—(R′—C(═S))_(a4)—R″  (9) —N{(R′)_(a4)R″}₂  (10) —C(═O)O—(R′—C(═O)O)_(a4)—R″  (11) —C(═O)O—(R′O)_(a4)—R″  (12) —NHC(═O)—(R′NHC(═O))_(a4)—R″  (13) wherein R′ represents a divalent hydrocarbon group that optionally has a substituent; R″ represents a hydrogen atom, a monovalent hydrocarbon group that optionally has a substituent, a carboxyl group, a sulfo group, a hydroxy group, a mercapto group, —NR^(C) ₂, a cyano group or —C(═O)NR^(c) ₂; R′″ represents a trivalent hydrocarbon group that optionally has a substituent; a3 represents an integer of 1 or more; a4 represents an integer of 0 or more; R^(c) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; and when R′, R″ and R′″ are each plurally present, they each may be the same or different; wherein the organic compound represented by formula (17B′) is:

wherein R^(10″) represents the group represented by formula (18) or formula (19); Ar³, R¹¹, m12 and m13 are the same as the corresponding definitions above; and a hydrogen atom in formula (17B′) may be replaced with a substituent other than R^(10″) or R¹¹; and wherein the structural unit represented by formula (1) is:

wherein Ar¹ represents a (2+m1+m2)-valent fused polycyclic aromatic group that optionally has a substituent; R¹ represents a group represented by formula (2) or formula (3); R² represents the group represented by formula (4); m1 represents an integer of 1 or more; m2 represents an integer of 1 or more; when R¹ and R² are each plurally present, they each may be the same or different; and a hydrogen atom in formula (1) may be replaced with a substituent other than R¹ or R²; wherein the group represented by formula (2) is: —R³-{(Q¹)_(n1)-Y¹(M¹)_(a1)(Z¹)_(b1)}_(m3)  (2) wherein R³ represents a single bond, or a (1+m3)-valent organic group that optionally has a substituent; Q¹ represents a divalent organic group; Y¹ represents —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, —PO₃ ²⁻ or —B(R^(α))₃ ⁻; M¹ represents a metallic cation, or represents an ammonium cation that optionally has a substituent; Z¹ represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(a))₄ ⁻, R^(a)SO₃ ⁻, R^(a)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; n1 represents an integer of 0 or more; a1 represents an integer of 1 or more, and b1 represents an integer of 0 or more, wherein a1 and b1 are selected such that a charge of the group represented by formula (2) is zero; R^(α) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; R^(a) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m3 represents an integer of 1 or more, and when R³ is a single bond, m3 represents 1; and when Q¹, Y¹, M¹, Z¹, n1, a1 and b1 are each plurally present, they each may be the same or different; wherein the group represented by formula (3) is: —R⁴-{(Q²)_(n2)-Y²(M²)_(a2)(Z²)_(b2)}_(m4)  (3) wherein R⁴ represents a single bond, or a (1+m4)-valent organic group that optionally has a substituent; Q² represents a divalent organic group; Y² represents a carbocation, an ammonium cation, a phosphonium cation, a sulfonium cation, or an iodonium cation; M² represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(b))₄ ⁻, R^(b)SO₃ ⁻, R^(b)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; Z² represents a metallic cation, or represents an ammonium cation that optionally has a substituent; n2 represents an integer of 0 or more; a2 represents an integer of 1 or more, and b2 represents an integer of 0 or more, wherein a2 and b2 are selected such that a charge of the group represented by formula (3) is zero; R^(b) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m4 represents an integer of 1 or more, and when R⁴ is a single bond, m4 represents 1; and when Q², Y², M², Z², n2, a2 and b2 are each plurally present, they each may be the same or different.
 12. A polymer compound comprising a structural unit represented by formula (17B′):

wherein R^(10″) represents a group represented by formula (18) or formula (19); Ar^(a) represents a (2+m12+m13)-valent fused polycyclic aromatic group that optionally has a substituent; R¹¹ represents a group represented by formula (4); m12 and m13 each independently represent an integer of 1 or more; and a hydrogen atom in formula (17B′) may be replaced with a substituent other than R^(10″) or R¹¹; wherein the group represented by formula (18) is: —R¹²-{(Q⁴)_(n4)-Y⁴}_(m14)  (18) wherein R¹² represents a single bond, or a (1+m14)-valent organic group that optionally has a substituent; Q⁴ represents a divalent organic group; Y⁴ represents —CO₂R^(χ), —SO₃R^(χ), —SO₂R^(χ), —PO₃(R^(χ))₂ or —B(R^(χ))₂; n4 represents an integer of 0 or more; R^(χ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m14 represents an integer of 1 or more, and when R¹² is a single bond, m14 represents 1; and when Q⁴, Y⁴, n4 and R^(χ) are each plurally present, they each may be the same or different; wherein the group represented by formula (19) is: —R¹³-{(Q⁵)_(n5)-Y⁵}_(m15)  (19) wherein R¹³ represents a single bond, or a (1+m15)-valent organic group that optionally has a substituent; Q⁵ represents a divalent organic group; Y⁵ represents a halogenated alkyl group, a halogen atom, —N(R^(δ))₂, —P(R^(δ))₂ or —SR^(δ); n5 represents an integer of 0 or more; R^(δ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m15 represents an integer of 1 or more, and when R¹³ is a single bond, m15 represents 1; and when Q⁵, Y⁵, n5 and R^(δ) are each plurally present, they each may be the same or different; wherein the group represented by formula (4) is: —R⁵-{(Q³)_(n3)-Y³}_(m5)  (4) wherein R⁵ represents a single bond, or a (1+m5)-valent organic group that optionally has a substituent; Q³ represents a divalent organic group; Y³ represents a cyano group, or a group represented by any one of formulae (5) to (13); n3 represents an integer of 0 or more; m5 represents an integer of 1 or more, and when R⁵ is a single bond, m5 is 1; and when Q³, Y³ and n3 are each plurally present, they each may be the same or different; wherein the group represented by any one of formulae (5) to (13) is: —O—(R′O)_(a3)—R″  (5)

—S—(R′S)_(a4)—R″  (7) —C(═O)—(R′—C(═O))_(a4)—R″  (8) —C(═S)—(R′—C(═S))_(a4)—R″  (9) —N{(R′)_(a4)R″}₂  (10) —C(═O)O—(R′—C(═O)O)_(a4)—R″  (11) —C(═O)O—(R′O)_(a4)—R″  (12) —NHC(═O)—(R′NHC(═O))_(a4)—R″  (13) wherein R′ represents a divalent hydrocarbon group that optionally has a substituent; R″ represents a hydrogen atom, a monovalent hydrocarbon group that optionally has a substituent, a carboxyl group, a sulfo group, a hydroxy group, a mercapto group, —NR^(C) ₂, a cyano group or —C(═O)NR^(c) ₂; R′″ represents a trivalent hydrocarbon group that optionally has a substituent; a3 represents an integer of 1 or more; a4 represents an integer of 0 or more; R^(c) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; and when R′, R″ and R′″ are each plurally present, they each may be the same or different.
 13. An organic compound represented by formula (20):

wherein Ar⁴ represents a (2+m16+m17)-valent fused polycyclic aromatic group that optionally has a substituent; R¹⁴ represents a group represented by formula (15) or formula (16), or a group represented by formula (21) or formula (22); R¹⁵ represents a group represented by formula (4); m16 represents an integer of 1 or more; m17 represents an integer of 0 or more; X³ and X⁴ each independently represent a group involved in a condensation polymerization; when R¹⁴ and R¹⁵ are each plurally present, they each may be the same or different; and a hydrogen atom in formula (20) may be replaced with a substituent other than R¹⁴ or R¹⁵; wherein the group represented by formula (15) is:

wherein R⁸ represents a (1+m8+m9)-valent organic group that optionally has a substituent; Q¹ represents a divalent organic group; Q³ represents a divalent organic group; Y¹ represents —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, —PO₃ ²⁻ or —B(R^(α))₃ ⁻; Y³ represents a cyano group, or a group represented by any one of formulae (5) to (13); M¹ represents a metallic cation, or represents an ammonium cation that optionally has a substituent; Z¹ represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(a))₄ ⁻, R^(a)SO₃ ⁻, R^(a)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; n1 represents an integer of 0 or more; n3 represents an integer of 0 or more; a1 represents an integer of 1 or more, and b1 represents an integer of 0 or more, wherein a1 and b1 are selected such that a charge of the group represented by formula (2) is zero; R^(α) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; R^(a) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m8 and m9 each independently represent an integer of 1 or more; and when Q¹, Q³, Y¹, Y³, M¹, Z¹, n1, n3, a1 and b1 are each plurally present, they each may be the same or different; wherein the group represented by any one of formulae (5) to (13) is: —O—(R′O)_(a3)—R″  (5)

—S—(R′S)_(a4)—R″  (7) —C(═O)—(R′—C(═O))_(a4)—R″  (8) —C(═S)—(R′—C(═S))_(a4)—R″  (9) —N{(R′)_(a4)R″}₂  (10) —C(═O)O—(R′—C(═O)O)_(a4)—R″  (11) —C(═O)O—(R′O)_(a4)—R″  (12) —NHC(═O)—(R′NHC(═O))_(a4)—R″  (13) wherein R′ represents a divalent hydrocarbon group that optionally has a substituent; R″ represents a hydrogen atom, a monovalent hydrocarbon group that optionally has a substituent, a carboxyl group, a sulfo group, a hydroxy group, a mercapto group, —NR^(C) ₂, a cyano group or —C(═O)NR^(c) ₂; R′″ represents a trivalent hydrocarbon group that optionally has a substituent; a3 represents an integer of 1 or more; a4 represents an integer of 0 or more; R^(c) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; and when R′, R″ and R′″ are each plurally present, they each may be the same or different; wherein the group represented by formula (16) is:

wherein R⁹ represents a (1+m10+m11)-valent organic group that optionally has a substituent; Q³, Y³ and n3 are the same as the corresponding definitions above; Q² represents a divalent organic group; Y² represents a carbocation, an ammonium cation, a phosphonium cation, a sulfonium cation, or an iodonium cation; M² represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(b))₄ ⁻, R^(b)SO₃ ⁻, R^(b)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; Z² represents a metallic cation, or represents an ammonium cation that optionally has a substituent; n2 represents an integer of 0 or more; a2 represents an integer of 1 or more, and b2 represents an integer of 0 or more, wherein a2 and b2 are selected such that a charge of the group represented by formula (3) is zero; R^(b) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m10 and m11 each independently represent an integer of 1 or more; and when Q², Q³, Y², Y³, M², Z², n2, n3, a2 and b2 are each plurally present, they each may be the same or different; wherein the group represented by formula (21) is:

wherein R^(15′) represents a (1+m18+m19)-valent organic group that optionally has a substituent; Q³, Y³ and n3 are the same as the corresponding definitions above; Q⁴ represents a divalent organic group; Y⁴ represents —CO₂R^(χ), —SO₃R^(χ), —SO₂R^(χ), —PO₃(R^(χ))₂ or —B(R^(χ))₂; n4 represents an integer of 0 or more; R^(χ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m18 and m19 each independently represent an integer of 1 or more; and when Q³, Q⁴, Y³, Y⁴, n3 and n4 are each plurally present, they each may be the same or different; wherein the group represented by formula (22) is:

wherein R¹⁶ represents a (1+m20+m21)-valent organic group that optionally has a substituent; Q³, Y³ and n3 are the same as the corresponding definitions above; Q⁵ represents a divalent organic group; Y⁵ represents a halogenated alkyl group, a halogen atom, —N(R^(δ))₂, —P(R^(δ))₂ or —SR^(δ); n5 represents an integer of 0 or more; R^(δ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m20 and m21 each independently represent an integer of 1 or more; and when Q³, Q⁵, Y³, Y⁵, n3 and n5 are each plurally present, they each may be the same or different. wherein the group represented by formula (4) is: —R⁵-{(Q³)_(n3)-Y³}_(m5)  (4) wherein R⁵ represents a single bond, or a (1+m5)-valent organic group that optionally has a substituent; Q³, Y³ and n3 are the same as the corresponding definitions above; m5 represents an integer of 1 or more, and when R⁵ is a single bond, m5 is 1; and when Q³, Y³ and n3 are each plurally present, they each may be the same or different.
 14. A method of producing a polymer compound comprising a structural unit represented by formula (14), which includes polymerizing an organic compound represented by formula (20A) to obtain the polymer compound comprising the structural unit represented by formula (14), wherein the organic compound represented by formula (20A):

wherein R^(14′) represents a group represented by formula (15) or formula (16); Ar⁴ represents a (2+m16+m17)-valent fused polycyclic aromatic group that optionally has a substituent; R¹⁵ represents a group represented by formula (4); m16 represents an integer of 1 or more; m17 represents an integer of 0 or more; X³ and X⁴ each independently represent a group involved in a condensation polymerization; when R^(14′) and R¹⁵ are each plurally present, they each may be the same or different; and a hydrogen atom in formula (20A) may be replaced with a substituent other than R^(14′) or R¹⁵; wherein the group represented by formula (15) is:

wherein R⁸ represents a (1+m8+m9)-valent organic group that optionally has a substituent; Q¹ represents a divalent organic group; Q³ represents a divalent organic group; Y¹ represents —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, —PO₃ ²⁻ or —B(R^(α))₃ ⁻; Y³ represents a cyano group, or a group represented by any one of formulae (5) to (13); M¹ represents a metallic cation, or represents an ammonium cation that optionally has a substituent; Z¹ represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(a))₄ ⁻, R^(a)SO₃ ⁻, R^(a)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; n1 represents an integer of 0 or more; n3 represents an integer of 0 or more; a1 represents an integer of 1 or more, and b1 represents an integer of 0 or more, wherein a1 and b1 are selected such that a charge of the group represented by formula (2) is zero; R^(α) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; R^(a) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m8 and m9 each independently represent an integer of 1 or more; and when Q¹, Q³, Y¹, Y³, M¹, Z¹, n1, n3, a1 and b1 are each plurally present, they each may be the same or different; wherein the group represented by any one of formulae (5) to (13) is: —O—(R′O)_(a3)—R″  (5)

—S—(R′S)_(a4)—R″  (7) —C(═O)—(R′—C(═O))_(a4)—R″  (8) —C(═S)—(R′—C(═S))_(a4)—R″  (9) —N{(R′)_(a4)R″}₂  (10) —C(═O)O—(R′—C(═O)O)_(a4)—R″  (11) —C(═O)O—(R′O)_(a4)—R″  (12) —NHC(═O)—(R′NHC(═O))_(a4)—R″  (13) wherein R′ represents a divalent hydrocarbon group that optionally has a substituent; R″ represents a hydrogen atom, a monovalent hydrocarbon group that optionally has a substituent, a carboxyl group, a sulfo group, a hydroxy group, a mercapto group, —NR^(C) ₂, a cyano group or —C(═O)NR^(c) ₂; R′″ represents a trivalent hydrocarbon group that optionally has a substituent; a3 represents an integer of 1 or more; a4 represents an integer of 0 or more; R^(c) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; and when R′, R″ and R′″ are each plurally present, they each may be the same or different; wherein the group represented by formula (16) is:

wherein R⁹ represents a (1+m10+m11)-valent organic group that optionally has a substituent; Q³, Y³ and n3 are the same as the corresponding definitions above; Q² represents a divalent organic group; Y² represents a carbocation, an ammonium cation, a phosphonium cation, a sulfonium cation, or an iodonium cation; M² represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(b))₄ ⁻, R^(b)SO₃ ⁻, R^(b)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; Z² represents a metallic cation, or represents an ammonium cation that optionally has a substituent; n2 represents an integer of 0 or more; a2 represents an integer of 1 or more, and b2 represents an integer of 0 or more, wherein a2 and b2 are selected such that a charge of the group represented by formula (3) is zero; R^(b) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m10 and m11 each independently represent an integer of 1 or more; and when Q², Q³, Y², Y³, M², Z², n2, n3, a2 and b2 are each plurally present, they each may be the same or different; wherein the group represented by formula (4) is: —R⁵-{(Q³)_(n3)-Y³}_(m5)  (4) wherein R⁵ represents a single bond, or a (1+m5)-valent organic group that optionally has a substituent; Q³, Y³ and n3 are the same as the corresponding definitions above; m5 represents an integer of 1 or more, and when R⁵ is a single bond, m5 is 1; and when Q³, Y³ and n3 are each plurally present, they each may be the same or different; and wherein the structural unit represented by formula (14) is:

wherein Ar² represents a (2+m6+m7)-valent fused polycyclic aromatic group that optionally has a substituent; R⁶ represents the group represented by formula (15) or formula (16); R⁷ represents the group represented by formula (4); m6 represents an integer of 1 or more; m7 represents an integer of 0 or more; when R⁶ and R⁷ are each plurally present, they each may be the same or different; and a hydrogen atom in formula (14) may be replaced with a substituent other than R⁶ or R⁷.
 15. A method of producing a polymer compound comprising a structural unit represented by formula (14), which includes: (i′) polymerizing an organic compound represented by formula (20B) to obtain a polymer compound comprising a structural unit represented by formula (20B′); (ii′) ionizing the polymer compound comprising the structural unit represented by formula (20B′) to obtain the polymer compound comprising the structural unit represented by formula (14), wherein the organic compound represented by formula (20B) is:

wherein R^(14″) represents a group represented by formula (21) or formula (22); Ar⁴ represents a (2+m16+m17)-valent fused polycyclic aromatic group that optionally has a substituent; R¹⁵ represents a group represented by formula (4); m16 represents an integer of 1 or more; m17 represents an integer of 0 or more; X³ and X⁴ each independently represent a group involved in a condensation polymerization; when R^(14″) and R¹⁵ are each plurally present, they each may be the same or different; and a hydrogen atom in formula (20B) may be replaced with a substituent other than R^(14″) or R¹⁵; wherein the group represented by formula (21) is:

wherein R^(15′) represents a (1+m18+m19)-valent organic group that optionally has a substituent; Q³ represents a divalent organic group; Q⁴ represents a divalent organic group; Y³ represents a cyano group, or a group represented by any one of formulae (5) to (13); Y⁴ represents —CO₂R^(χ), —SO₃R^(χ), —SO₂R^(χ), —PO₃(R^(χ))₂ or —B(R^(χ))₂; n3 represents an integer of 0 or more; n4 represents an integer of 0 or more; R^(χ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m18 and m19 each independently represent an integer of 1 or more; and when Q³, Q⁴, Y³, Y⁴, n3 and n4 are each plurally present, they each may be the same or different; wherein the group represented by any one of formulae (5) to (13) is: —O—(R′O)_(a3)—R″  (5)

—S—(R′S)_(a4)—R″  (7) —C(═O)—(R′—C(═O))_(a4)—R″  (8) —C(═S)—(R′—C(═S))_(a4)—R″  (9) —N{(R′)_(a4)R″}₂  (10) —C(═O)O—(R′—C(═O)O)_(a4)—R″  (11) —C(═O)O—(R′O)_(a4)—R″  (12) —NHC(═O)—(R′NHC(═O))_(a4)—R″  (13) wherein R′ represents a divalent hydrocarbon group that optionally has a substituent; R″ represents a hydrogen atom, a monovalent hydrocarbon group that optionally has a substituent, a carboxyl group, a sulfo group, a hydroxy group, a mercapto group, —NR^(C) ₂, a cyano group or —C(═O)NR^(c) ₂; R′″ represents a trivalent hydrocarbon group that optionally has a substituent; a3 represents an integer of 1 or more; a4 represents an integer of 0 or more; R^(c) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; and when R′, R″ and R′″ are each plurally present, they each may be the same or different; wherein the group represented by formula (22) is:

wherein R¹⁶ represents a (1+m20+m21)-valent organic group that optionally has a substituent; Q³, Y³ and n3 are the same as the corresponding definitions above; Q⁵ represents a divalent organic group; Y⁵ represents a halogenated alkyl group, a halogen atom, —N(R^(δ))₂, —P(R^(δ))₂ or —SR^(δ); n5 represents an integer of 0 or more; R^(δ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m20 and m21 each independently represent an integer of 1 or more; and when Q³, Q⁵, Y³, Y⁵, n3 and n5 are each plurally present, they each may be the same or different. wherein the group represented by formula (4) is: —R⁵-{(Q³)_(n3)-Y³}_(m5)  (4) wherein R⁵ represents a single bond, or a (1+m5)-valent organic group that optionally has a substituent; Q³, Y³ and n3 are the same as the corresponding definitions above; m5 represents an integer of 1 or more, and when R⁵ is a single bond, m5 is 1; and when Q³, Y³ and n3 are each plurally present, they each may be the same or different; wherein the group represented by formula (20B′) is:

wherein R^(14″) represents the group represented by formula (21) or formula (22); Ar⁴, R¹⁵, m16 and m17 are the same as the corresponding definitions above; and a hydrogen atom in formula (20B′) may be replaced with a substituent other than R^(14″) or R¹⁵; and wherein the structural unit represented by formula (14) is:

wherein Ar² represents a (2+m6+m7)-valent fused polycyclic aromatic group that optionally has a substituent; R⁶ represents a group represented by formula (15) or formula (16); R⁷ represents the group represented by formula (4); m6 represents an integer of 1 or more; m7 represents an integer of 0 or more; when R⁶ and R⁷ are each plurally present, they each may be the same or different; and a hydrogen atom in formula (14) may be replaced with a substituent other than R⁶ or R⁷. wherein the group represented by formula (15) is:

wherein R⁸ represents a (1+m8+m9)-valent organic group that optionally has a substituent; Q³, Y³ and n3 are the same as the corresponding definitions above; Q¹ represents a divalent organic group; Y¹ represents —CO₂ ⁻, —SO₃ ⁻, —SO₂ ⁻, —PO₃ ²⁻ or —B(R^(α))₃ ⁻; M¹ represents a metallic cation, or represents an ammonium cation that optionally has a substituent; Z¹ represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(a))₄ ⁻, R^(a)SO₃—, R^(a)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; n1 represents an integer of 0 or more; a1 represents an integer of 1 or more, and b1 represents an integer of 0 or more, wherein a1 and b1 are selected such that a charge of the group represented by formula (2) is zero; R^(α) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; R^(a) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m8 and m9 each independently represent an integer of 1 or more; and when Q¹, Q³, Y¹, Y³, M¹, Z¹, n1, n3, a1 and b1 are each plurally present, they each may be the same or different; wherein the group represented by formula (16) is:

wherein R⁹ represents a (1+m10+m11)-valent organic group that optionally has a substituent; Q³, Y³ and n3 are the same as the corresponding definitions above; Q² represents a divalent organic group; Y² represents a carbocation, an ammonium cation, a phosphonium cation, a sulfonium cation, or an iodonium cation; M² represents F⁻, Cl⁻, Br⁻, I⁻, OH⁻, B(R^(b))₄ ⁻, R^(b)SO₃ ⁻, R^(b)COO⁻, ClO⁻, ClO₂ ⁻, ClO₃ ⁻, ClO₄ ⁻, SCN⁻, CN⁻, NO₃ ⁻, SO₄ ²⁻, HSO₄ ⁻, PO₄ ³⁻, HPO₄ ²⁻, H₂PO₄ ⁻, BF₄ ⁻ or PF₆ ⁻; Z² represents a metallic cation, or represents an ammonium cation that optionally has a substituent; n2 represents an integer of 0 or more; a2 represents an integer of 1 or more, and b2 represents an integer of 0 or more, wherein a2 and b2 are selected such that a charge of the group represented by formula (3) is zero; R^(b) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m10 and m11 each independently represent an integer of 1 or more; and when Q², Q³, Y², Y³, M², Z², n2, n3, a2 and b2 are each plurally present, they each may be the same or different.
 16. A polymer compound comprising a structural unit represented by formula (20B′):

wherein R^(14″) represents a group represented by formula (21) or formula (22); Ar⁴ represents a (2+m16+m17)-valent fused polycyclic aromatic group that optionally has a substituent; R¹⁵ represents a group represented by formula (4); m16 represents an integer of 1 or more; m17 represents an integer of 0 or more; and when R^(14″) and R¹⁵ are each plurally present, they each may be the same or different. a hydrogen atom in formula (20B′) may be replaced with a substituent other than R^(14″) or R¹⁵; wherein the group represented by formula (21) is:

wherein R^(15′) represents a (1+m18+m19)-valent organic group that optionally has a substituent; Q³ represents a divalent organic group; Q⁴ represents a divalent organic group; Y³ represents a cyano group, or a group represented by any one of formulae (5) to (13); Y⁴ represents —CO₂R^(χ), —SO₃R^(χ), —SO₂R^(χ), —PO₃(R^(χ))₂ or —B(R^(χ))₂; n3 represents an integer of 0 or more; n4 represents an integer of 0 or more; R^(χ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m18 and m19 each independently represent an integer of 1 or more; and when Q³, Q⁴, Y³, Y⁴, n3 and n4 are each plurally present, they each may be the same or different; wherein the group represented by any one of formulae (5) to (13) is: —O—(R′O)_(a3)—R″  (5)

—S—(R′S)_(a4)—R″  (7) —C(═O)—(R′—C(═O))_(a4)—R″  (8) —C(═S)—(R′—C(═S))_(a4)—R″  (9) —N{(R′)_(a4)R″}₂  (10) —C(═O)O—(R′—C(═O)O)_(a4)—R″  (11) —C(═O)O—(R′O)_(a4)—R″  (12) —NHC(═O)—(R′NHC(═O))_(a4)—R″  (13) wherein R′ represents a divalent hydrocarbon group that optionally has a substituent; R″ represents a hydrogen atom, a monovalent hydrocarbon group that optionally has a substituent, a carboxyl group, a sulfo group, a hydroxy group, a mercapto group, —NR^(C) ₂, a cyano group or —C(═O)NR^(c) ₂; R′″ represents a trivalent hydrocarbon group that optionally has a substituent; a3 represents an integer of 1 or more; a4 represents an integer of 0 or more; R^(c) represents an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; and when R′, R″ and R′″ are each plurally present, they each may be the same or different; wherein the group represented by formula (22) is:

wherein R¹⁶ represents a (1+m20+m21)-valent organic group that optionally has a substituent; Q³, Y³ and n3 are the same as the corresponding definitions above; Q⁵ represents a divalent organic group; Y⁵ represents a halogenated alkyl group, a halogen atom, —N(R^(δ))₂, —P(R^(δ))₂ or —SR^(δ); n5 represents an integer of 0 or more; R^(δ) represents a hydrogen atom, an alkyl group having 1 to 30 carbon atoms that optionally has a substituent, or an aryl group having 6 to 50 carbon atoms that optionally has a substituent; m20 and m21 each independently represent an integer of 1 or more; and when Q³, Q⁵, Y³, Y⁵, n3 and n5 are each plurally present, they each may be the same or different; wherein the group represented by formula (4) is: —R⁵-{(Q³)_(n3)-Y³}_(m5)  (4) wherein R⁵ represents a single bond, or a (1+m5)-valent organic group that optionally has a substituent; Q³, Y³ and n3 are the same as the corresponding definitions above; m5 represents an integer of 1 or more, and when R⁵ is a single bond, m5 is 1; and when Q³, Y³ and n3 are each plurally present, they each may be the same or different. 